Wetting Behaviour of Water, Ethanol, Rhamnolipid, and Triton X-165 Mixture in the Polymer-Solution Drop-Air System.

Despite the fact that the wetting properties of multicomponent mixtures including the surface active compounds play a very important role in many practical applications, they are not sufficiently known. Thus, the wettability of polytetrafluoroethylene (PTFE) and poly (methyl methacrylate) (PMMA) by the water + ethanol (ET) solution of rhamnolipid (RL) with Triton X-165 (TX165) mixture was studied. The investigations involved measuring the advancing contact angles of this solution on PTFE and PMMA by varying the concentration of TX165 while maintaining a constant concentration of ET and RL. Additionally, a thermodynamic analysis was conducted to obtain the compositions and concentrations of the ET, RL, and TX165 mixtures at the different interfaces. The composition and concentration of the interface mixed layer were considered using two different approaches to the wetting process. From these considerations, it follows that, depending on the ET concentration, it is possible to form the TX165 + RL layer at the solid-water + ET mixed solvent, as well as the water + ET-air interfaces, but not at the solid-water and water-air ones. This conclusion is in accordance with the Gibbs standard free energy of adsorption of particular components of the studied mixture at the solution-air and solid-solution interfaces.

Thermodynamic Characterization of Rhamnolipid, Triton X-165 and Ethanol as well as Their Mixture Behaviour at the Water-Air Interface.

In many industrial fields, in medicine or pharmacy, there are used multi-component mixtures of surfactants as well as more and more often mixtures containing biosurfactants. Thus, in our study the mixtures of rhamnolipid (RL), ethanol (ET) and Triton X-165 (TX165) were applied. For these mixtures the surface tension of aqueous solutions with constant concentration and composition of ET and RL as well as the variable concentration of TX165 was measured. Based on the obtained results and the literature data, thermodynamic analyses of the adsorption process of ET, RL, TX165, binary mixtures of ET + RL, ET + TX165 and RL + TX165 as well as the ternary mixtures of RL + ET + TX165 at the water-air interface were made. This analysis allows to propose a new equation for calculation of the total ethanol concentration at the water-air interface using the Guggenheim-Adam adsorption isotherm. The constants in the Langmuir and Szyszkowski equations for each component of the studied mixtures as well as the composition of the mixed monolayer at the water-air interface were also successfully analysed based on the contribution of particular surface active compounds to the water surface tension reduction as well as based on the Frumkin isotherm of adsorption.

Wetting Properties of Rhamnolipid and Surfactin Mixtures with Triton X-165.

The wetting properties of the rhamnolipid and surfactin mixtures with Triton X-165 were considered based on the contact angle measurements of their aqueous solution on the polytetrafluoroethylene (PTFE), polymethyl methacrylate (PMMA) and quartz (Q) surfaces. The obtained contact angle isotherms were described by the exponential function of the second order as well as by Szyszkowski equation in some cases. Using the contact angle isotherms of individual biosurfactants and TX165 as well as the earlier obtained isotherms of their surface tension the contact angle isotherms of the biosurfactants mixtures with TX165 were deduced. As follows the presence of the maxima on the contact angle isotherms of the biosurfactants mixtures with TX165 is justified. They do not prove negative adsorption of the biosurfactant and TX165 at the interfaces. However, the mutual exchange of the biosurfactant and TX165 molecules is observed in the layers at the interfaces. The concentration of the studied mixtures at the PTFE-solution interface was established to be close to that at the solution-air one but that at the PTFE-air is equal to zero. However, the concentration of the studied mixtures at the PMMA-solution and quartz-solution is greater than zero. The concentration at the PMMA(quartz)-air and PMMA(quartz)-solution interfaces is smaller than that at the solution-air one.

Thermodynamic Analysis of the Adsorption and Micellization Activity of the Mixtures of Rhamnolipid and Surfactin with Triton X-165.

The surface tension of aqueous solutions of Triton X-165 with rhamnolipid or surfactin mixtures was measured. The obtained results were applied for the determination of the concentration and composition of the Triton X-165 and biosurfactants mixture at the water-air interface as well as the contribution of the particular component of the mixtures to water surface tension reduction and the mutual influence of these components on the critical micelle concentration. The determination of these quantities was based on both the commonly used concepts and a new one proposed by us, which assumes that the composition of the mixed monolayer at the water-air interface depends directly on the pressure of the monolayer of the single mixture component and allows us to determine the surface concentration of each mixture component independently of surface tension isotherms shape. Taking into account the composition of the mixed monolayer at the water-air interface, the standard Gibbs adsorption free energy was considered. The obtained results allow us to state that the concentration of both mixture components corresponding to their saturated monolayer and the surface tension of their aqueous solution can be predicted using the surfactants' single monolayer pressure and their mole fraction in the mixed monolayer determined in the proposed way.