Interval cranioplasty: comparison of current standards.

BACKGROUND: Although different cranioplasty storage methods are currently in use, no study has prospectively compared these methods. The authors compare freezing and subcutaneous storage methods in a rat model. METHODS: Trephine defects (10 mm) were created in 45 Sprague-Dawley rats. The cranial bone grafts were stored in an autologous subcutaneous pocket (n = 15), frozen at -80°C (n = 15), immediately analyzed (n = 12), or immediately replanted into the defect (n = 3). After 10 days of storage, the subcutaneous or frozen grafts were either replanted (subcutaneous, n = 3; frozen, n = 3) or analyzed (subcutaneous, n = 12; frozen, n = 12). Grafts underwent histologic analysis, 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay, alkaline phosphatase assay, mechanical testing, and micro-computed tomographic imaging. RESULTS: After 10 days of storage, physiologic assays demonstrated a significant decrease in cellular functionality (e.g., alkaline phosphatase assay concentration: fresh, 18.8 ± 0.77 mM/mg; subcutaneous, 12.2 ± 0.63 mM/mg; frozen, 8.07 ± 1.1 mM/mg; p < 0.012 for all comparisons). Mechanical integrity (maximal load) of fresh grafts was greatest (fresh, 9.26 ± 0.29 N; subcutaneous, 6.27 ± 0.64 N; frozen, 4.65 ± 0.29 N; fresh compared with frozen, p < 0.001; fresh compared with subcutaneous, p = 0.006). Replantation of subcutaneously stored and frozen grafts resulted in limited bony union and considerable resorption after 12 weeks; in contrast, replanted fresh grafts demonstrated bony union and little resorption. CONCLUSIONS: Current preservation methods for interval cranioplasty do not maintain bone graft viability. Subcutaneous storage appears to provide a small advantage compared with freezing.

A Comparative Study of MTA Solubility in Various Media.

INTRODUCTION: Solubility of root filling materials is heavily influenced by the environment they are in contact with. This study compared the solubility of ProRoot MTA in deionized water and synthetic tissue fluid. MATERIALS AND METHODS: Forty specimens of prepared MTA were immersed in deionized water and synthetic tissue fluid (20 samples each). The solubility was assessed after 7 and 28 days. Scanning electron microscope observation was also performed. The mean weight loss was evaluated using a digital scale. Data were analyzed using one-way ANOVA. Tukey test was performed for multiple comparisons. RESULTS: MTA solubility in synthetic tissue fluid was significantly lower than deionized water after 7 and 28 days (P<0.05). Secondary electron detectors revealed the presence of lumps and platelets on the surfaces of both specimens. Also, more voids were observed in specimen stored in deionized water. CONCLUSION: MTA dissolved faster in deionized water than synthetic tissue fluid. Despite this, the solubility of this material in both media was acceptable.

Analysis of changes in implant screws subject to occlusal loading: a preliminary analysis.

Loosening of the abutment screw can present a problem for the stability of the implant-supported crown or prosthesis. The purpose of this study was to understand the parameters of screw loosening, using an in vitro model, including loss of torque, screw head rotation, changes in screw dimension, and distortion of the implant-abutment joint. Implants (4 x 10 mm) were potted in autopolymerizing blocks. Abutments were placed with screws tightened with a 35-Ncm torque and standardized crowns fabricated. There were 3 implant systems used: Nobel Biocare USA, Inc. (Yorba Linda, CA), 3i Implant Innovations, Inc. (Palm Beach Gardens, FL), and Bio-Lok International, Inc. (Deerfield Beach, FL). Seven samples were tested for each system. Samples were loaded with 300-N loads for 50,000 cycles at 1 Hz. Torque turn audits were performed at 10,000, 25,000, and 50,000 cycles. At the conclusion of the loading, counterclockwise rotation of the abutment screw was measured. The screws were retrieved and measurements made compared with the controls. Finally, 1 sample from each group was embedded in resin, sectioned longitudinally, and examined under the standard error of the mean. The Nobel Biocare system showed a 9.4-Ncm loss of torque from the loading protocol. This result was accompanied by a counterclockwise rotation of 7 degrees and a 200-ìm elongation of the screw. Finally, there was compression and distortion of the longitudinally sectioned joint architecture observed with the standard error of the mean. From the 3i and Bio-Lok International groups, no loss of torque, counterclockwise rotation, or lengthening of the screws was observed. Intimate adaptation of the joint without distortion was seen in the longitudinal sections. Screw loosening appears to follow specific parameters that include counterclockwise rotation, lengthening of the screw, and distortion of the screw joint. This process is likely associated with both the physical properties of the screw as well as its configuration.