RESUMO
Reactions between a gas phase and a solid material are of high importance in the study of alternative ways for energy conversion utilizing otherwise useless carbon dioxide (CO2). The photocatalytic CO2 reduction to hydrocarbon fuels like e.g., methane (CH4) is such a potential candidate process converting solar light into molecular bonds. In this work, the design, construction, and operation of a high-purity gas-solid photoreactor is described. The design aims at eliminating any unwanted carbon-containing impurities and leak points, ensuring the collection of reliable and reproducible data in photocatalytic CO2 reduction measurements. Apart from the hardware design, a detailed experimental procedure including gas analysis is presented, allowing newcomers in the field of gas-solid CO2 reduction to learn the essential basics and valuable tricks. By performing extensive blank measurements (with/without sample and/or light) the true performance of photocatalytic materials can be monitored, leading to the identification of trends and the proposal of possible mechanisms in CO2 photoreduction. The reproducibility of measurements between different versions of the here presented reactor on the ppm level is evidenced.
RESUMO
In this study we assess the general applicability of the widely used P25-TiO2 in gas-phase photocatalytic CO2 reduction based on experimentally determined reactivity descriptors from classical heterogeneous catalysis (productivity) and photochemistry (apparent quantum yield/AQY). A comparison of the results with reports on the use of P25 for thermodynamically more feasible reactions and our own previous studies on P25-TiO2 as photocatalyst imply that the catalytic functionality of this material, rather than its properties as photoabsorber, limits its applicability in the heterogeneous photocatalytic CO2 reduction in the gas phase. The AQY of IrOx/TiO2 in overall water splitting in a similar high-purity gas-solid process was four times as high, but still far from commercial viability.
RESUMO
Although the photocatalytic reduction of CO2 to CH4 by using H2O as the oxidant presupposes the formation of O2, it is often not included in the product analysis of most of the studies dealing with photocatalytic CO2 reduction or it is reported to be not formed at all. The present study aims to clarify the absence of O2 in the photocatalytic gas phase CO2 reduction on TiO2. By modifying P25-TiO2 with IrOx co-catalysts it was possible to observe photocatalytic water splitting, i.e. the formation of gaseous O2 and H2 in almost stoichiometric amounts, without the use of sacrificial agents, while bare P25-TiO2 showed no activity in H2 and O2 formation under similar reaction conditions. Investigating the effect of improved H2O oxidation properties on the photocatalytic CO2 reduction revealed that the CH4 formation on P25 from CO2 was completely inhibited as long as the H2O splitting reaction proceeded. Furthermore, we found that a certain amount of O2 is consumed under conditions of photocatalytic water oxidation. A quantification showed it to be in the same order of magnitude as the oxygen which is missing as a byproduct from photocatalytic CO2 conversion. A detailed interpretation of the results in the context of the general understanding of the photocatalytic CO2 reduction with H2O on TiO2 allows the hypothesis that P25-TiO2 undergoes a stoichiometric reaction, meaning that the CH4 formation is not based on a true catalytic cycle and runs only as long as TiO2 can consume oxygen.
RESUMO
A self-made, low-cost tubular reactor for the gas-phase photocatalytic CO2 reduction was developed. The resulting flow conditions cause an intensive interaction between the reactants in the gas-phase and the fixed bed photocatalyst. This approach is used to test the scalability of tubular reactors for the photocatalytic CO2 reduction.
RESUMO
Alloyed silver-gold nanoparticles were prepared in nine different metal compositions with silver/gold molar ratios of ranging from 90:10 to 10:90. The one-pot synthesis in aqueous medium can easily be modified to gain control over the final particle diameter and the stabilizing agents. The purification of the particles to remove synthesis by-products (which is an important factor for subsequent in vitro experiments) was carried out by multiple ultracentrifugation steps. Characterization by transmission electron microscopy (TEM), differential centrifugal sedimentation (DCS), dynamic light scattering (DLS), UV-vis spectroscopy and atomic absorption spectroscopy (AAS) showed spherical, monodisperse, colloidally stable silver-gold nanoparticles of ≈7 nm diameter with measured molar metal compositions very close to the theoretical values. The examination of the nanoparticle cytotoxicity towards HeLa cells and human mesenchymal stem cells (hMSCs) showed that the toxicity is not proportional to the silver content. Nanoparticles with a silver/gold molar composition of 80:20 showed the highest toxicity.
RESUMO
A one-pot synthesis of fluorescent bimetallic silver-gold nanoparticles in aqueous medium is presented. Carboxylic acid-functionalized nanoparticles were prepared with different metal compositions from 90 : 10 to 10 : 90 (n : n) for silver : gold with a diameter of 1.8 ± 0.4 nm. Pure silver and gold nanoparticles were prepared for comparison. Spectroscopic analyses showed that the ligand, i.e. 11-mercaptoundecanoic acid, binds to the particle surface by the thiol group, leaving the carboxylic acid accessible for further functionalization, e.g. by suitable coupling reactions. Nanoparticles with a silver content up to 60 : 40 showed autofluorescence with a large Stokes shift of about 250-300 nm (maximum wavelength of the emission between 608 nm and 645 nm). The intracellular localization of bimetallic silver-gold nanoparticles was studied in HeLa cells by confocal laser scanning microscopy (CLSM). The alloyed silver-gold nanoparticles showed no significant cytotoxicity at a metal concentration of 5 µg mL-1 for 24 h, but were cytotoxic to some degree at 50 µg mL-1 at higher silver content.