1.
Restor Dent Endod ; 43(2): e22, 2018 May.
Artigo em Inglês | MEDLINE | ID: mdl-29765902

RESUMO

OBJECTIVES: To evaluate and compare light-transmittance in dental tissues and dental composite restorations using the incremental double-layer technique with varying layer thickness. MATERIALS AND METHODS: B1-colored natural teeth slabs were compared to dental restoration build-ups with A2D and B1E-colored nanofilled, supra-nanofilled, microfilled, and microhybrid composites. The enamel layer varied from 0.3, 0.5, or 1.2 mm thick, and the dentin layer was varied to provide a standardized 3.7 mm overall sample thickness (n = 10). All increments were light-cured to 16 J/cm2 with a multi-wave LED (Valo, Ultradent). Using a spectrophotometer, the samples were irradiated by an RGB laser beam. A voltmeter recorded the light output signal to calculate the light-transmittance through the specimens. The data were analyzed using 1-way analysis of variance followed by the post hoc Tukey's test (p = 0.05). RESULTS: Mean light-transmittance observed at thicker final layers of enamel were significantly lower than those observed at thinner final layers. Within 1.2 mm final enamel resin layer (FERL) thickness, all composites were similar to the dental tissues, with exception of the nanofilled composite. However, within 0.5 mm FERL thickness, only the supra-nanofilled composite showed no difference from the dental tissues. Within 0.3 mm FERL thickness, none of the composites were similar to the dental tissues. CONCLUSIONS: The supra-nanofilled composite had the most similar light-transmittance pattern when compared to the natural teeth. However, for other composites, thicker FERL have a greater chance to match the light-transmittance of natural dental tissues.

2.
Braz. dent. sci ; 19(3): 59-64, 2016. ilus, tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-830986

RESUMO

Objective: To evaluate the effect of shade and curing mode on cure efficiency of two dual-cure resin cements. Material and Methods: Two shades (A2 and TRANS) of two different dual-cure resin cements (G-CEM, GC Dental and SET PP, SDI) were submitted to different curing modes: light curing through a 2 mm thick ceramic disc (IPS Empress Esthetic, A2, Ivoclar Vivadent) for 20 s (16 J/cm2), 40 s (32 J/ cm2) or 80 s (64 J/cm2) performed immediately or with 1 or 5 min of delay. Fourier transform infrared spectroscopy (FT-IR) was used to evaluate the degree of conversion (DC) after 48 h. For the statistical analysis, data were submitted to threeway analysis of variance, followed by Tukey’s test for multiple comparisons (p<0.05). Results: Shade influenced DC (%) for the dual-cure resin cements tested (p=0.00001). TRANS shade showed lower DC (%) for both cements when there was no delay before light-curing (p=0.00001). Curing mode also influenced DC (%) for the dual-cure resin cements tested: radiant exposure greater than 32 J/cm2 and delaying light-curing for 1 to 5 min increased the DC (%) for both dual-cure resin cements evaluated. Conclusions: One minute delay prior to light-curing improved the cure efficiency and may be a more clinically acceptable approach to increase the degree of conversion of dual-cure resin cements.


Objetivo: Avaliar a influência da cor e do modo de polimerização no grau de conversão de dois cimentos resinosos duais. Material e Métodos: Duas cores (A2 e TRANS) de dois cimentos resinosos duais (G-CEM, GC Dental e SET PP, SDI) foram submetidos a diferentes modos de cura: fotoativação através de um disco de cerâmica de 2 mm de espessura (IPS Empress Esthetic, A2, Ivoclar Vivadent) por 20 s (16 J/cm2), 40 s (32 J/cm2) ou 80 s (64 J/cm2) realizada imediatamente ou após 1 ou 5 min de espera. Espectrometria com transformada de Fourier (FT-IR) foi utilizada para avaliação do grau de conversão (GC) após 48 h. Para a análise estatística, os dados foram submetidos à análise de variância com três fatores, seguida de teste de Tukey para comparações múltiplas (p=0.05). Resultados: A cor influenciou o GC (%) dos cimentos resinosos duais avaliados (p=0.00001). A cor TRANS resultou menor GC (%) para ambos os cimentos quando não houve espera antes da fotoativação (p=0.00001). O modo de cura também teve influência n o GC (%) dos cimentos resinosos duais avaliados: doses de energia superiores a 32 J/cm2 e espera de 1 ou 5 min antes da fotoativação aumentou o GC (%) dos dois cimentos resinosos duais avaliados. Conclusão: Um min de espera antes da fotoativação melhorou a eficiência de cura e pode ser uma abordagem clinicamente aceitável para aumentar o grau de conversão de cimentos resinosos duais.


Assuntos
Cor , Cimentos Dentários , Polimerização