Exfoliated graphite with graphene flakes as potential candidates for TL dosimeters at high gamma doses.

Graphite powder (GP) subjected to microwave radiation (MWG) results in exfoliation of graphite particles into few-layered graphene flakes (GF) intermixed with partially exfoliated graphite particles (PEG). Characterization of MWG by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM) and Raman spectroscopy reveal few-layer GF with sizes ranging from 0.2 to 5 µm. Raman D, G, and 2D (G') bands characteristic of graphitic structures include evidence of the presence of bilayered graphene. The thermoluminescent (TL) dosimetric properties of MWG are evaluated and can be characterized as a gamma-ray sensitive and dose-resistant material with kinetic parameters (activation energy for the main peak located at 400 and 408 K is 0.69 and 0.72 eV) and threshold dose (~1 kGy and 5 kGy respectively). MWG is a low-Z material (Zeff = 6) with a wide linear range of TL dose-response (0.170-2.5 kGy) tested at doses in the 1-20 kGy range with promising results for applications in gamma-ray dosimetry. Results obtained in gamma irradiated MWG are compared with those obtained in graphite powder samples (GP) without microwave treatment.

Fibrous growth of tricalcium phosphate ceramics.

Structural transformation and sintering processes of tricalcium phosphate (TCP) ceramics prepared from defective hydroxyapatite (Ca9HPO4(PO4)5OH) were studied by X-ray diffraction (XRD) and atomic force microscopy (AFM). Starting powders with Ca/P ratio approximately 1.5 were obtained by adding 0.5 l of 0.3 M H3PO4 solution to an equal volume of 0.45 M Ca(OH)2. In the prepared ceramics, the onset temperature for transformation of defective hydroxyapatite into TCP (witlokite) agrees with the onset temperature for sintering (800 degrees C). Sintering occurs through the formation of a fibrous structure, which resembles biological hard tissue. In the 1000-1200 degrees C range, these fibres coalesce into grains of up to 0.6 microm in size with a fibrous-laminar morphology. At the end of this sintering stage witlokite transforms into alphaTCP. At about 1450 degrees C, partial decomposition of alphaTCP into Ca2P2O7+Ca4P2O9 is observed. AFM observations suggest that Ca2P2O7 is segregated in the liquid state and increases the velocity of grain growth (up to 12 microm).