Specific Erosion Resistance Behaviour of Cold Forged and Angular Extruded Aluminium.

Aluminium finds wide application in mechanical engineering due to its low density and corrosion resistance. In this research, aluminium was subjected to two different metal forming technologies-cold forging (upsetting) and equal channel angular pressing (ECAP)-to obtain improvement in its exploitation properties. Parallel to changing mechanical properties by using these two processes, there was a change in the microstructure of the material. The resulting microstructures were examined using an optical microscope. A different treated aluminium was subjected to erosion wear in various time intervals. Wear testing was conducted for two different impingement angles causing abrasive wear and impact wear. The erosion mechanisms were examined by scanning electron microscopy. These results showed that there is no statistically significant difference in erosion wear for different states at the same impingement angle. However, the difference is noticeable at different wear angles. The significance of the difference in wear of the samples treated with the forging and ECAP techniques was validated by statistical analysis with tests of different sensitivities. The results of the t-test showed that ECAPed samples present a statistically significant difference in the loss of mass due to variations in erosion angle during the 30, 45, and 60 min wearing. A substantial difference in the change in sample mass is also visible for the forged state worn for 60 min.

Risk Evaluation for Coating Thickness Conformity Assessment.

This paper presents the conformity assessment process of the epoxy coating thickness applied on water pipes made of gray cast iron with the specifications given for this kind of coating appliance. An epoxy coating was applied to prevent a special form of corrosion called the graphitization of cast iron. In order for the pipe to withstand its designed service life, it is necessary to ensure the required thickness of the applied coating. In accordance with the EN 877 norm, the thickness of the epoxy coating on the pipes for the projected corrosiveness of the environment C4 and the durability of 20 years is at least 70 µm and this indicates the required accuracy of the product. To achieve the desired product quality, statistical control of the coating application process was carried out and the impact of uncertainty associated with the measurement result was analyzed. Considering the quality of the coating application process and the quality of the measuring system, and to ensure the quality of products and to reduce consumer risk, the optimal thickness of the coating was determined.