RESUMO
OBJECTIVE: The aim of this study was to evaluate the effect of five intracanal irrigants on bond strength of fiber posts cemented with newer self-adhesive resin cement. METHODS: A total of 60 extracted, single-rooted human premolars, sectioned at 14 mm, were prepared with the ProTaper Universal system with a size F3 instrument and filled with an F3 master cone and AH Plus. The root canal filling was partially removed, leaving 4 mm of apical gutta-percha. Specimens were randomly assigned to five groups (n=12), according to the solution used for dentin surface treatment before fiber post cementation, as follows: EDTA 17% (EDTA); QMix (QM); SmearClear (SC); 2.5% sodium hypochlorite (NaOCl), and 0.9% saline solution (SS). Ultrasonic activation was performed (three times, 20 seconds each), and root canals were dried with paper points. Fiber posts were cemented with RelyX U200. In one specimen per group, rhodamine B dye was mixed with RelyX U200 to provide adequate fluorescence for confocal laser scanning microscopy (CLSM) assessment. Specimens were transversally sectioned and three slices were obtained, one for each root third. Next, a push-out test was performed. A stereomicroscope and CLSM were used to analyze the failure modes and to illustrate the pattern of infiltration of RelyX U200 into dentinal tubules, respectively. Bond strength means were calculated, and analysis of variance and Bonferroni tests were used for statistical analysis. RESULTS: SS showed the highest mean bond strength values (11.5±5.3), superior to QM (5.1±3.1) and SC (5.1±3.3). NaOCl presented intermediary bond strength values (9.7±5.0), similar to EDTA (7.7±2.9) and SS. QM and SC showed the lowest mean bond strength (p<0.05). Adhesive failures between cement/dentin were predominant (53.9%). CONCLUSION: SS and NaOCl associated with ultrasonic activation seem to be adequate solutions for root canal cleaning before fiber post cementation with self-adhesive resin cement, whereas chelating solutions, such as EDTA, QM, and SC, cause a decrease in bond strength.