Cerium Dioxide Particles to Tune Radiopacity of Dental Adhesives: Microstructural and Physico-Chemical Evaluation.

The insufficient radiopacity of dental adhesives applied under composite restorations makes the radiographic diagnosis of recurrent caries challenging. Consequently, the misdiagnosis may lead to unnecessary replacement of restorations. The aims of this study were to formulate experimental dental adhesives containing cerium dioxide (CeO2) and investigate the effects of different loadings of CeO2 on their radiopacity and degree of conversion for the first time. CeO2 was characterized by X-ray diffraction analysis, Fourier transforms infrared spectroscopy, and laser diffraction for particle size analysis. Experimental dental adhesives were formulated with CeO2 as the inorganic filler with loadings ranging from 0.36 to 5.76 vol.%. The unfilled adhesive was used as a control. The studied adhesives were evaluated for dispersion of CeO2 in the polymerized samples, degree of conversion, and radiopacity. CeO2 presented a monoclinic crystalline phase, peaks related to Ce-O bonding, and an average particle size of around 16 µm. CeO2 was dispersed in the adhesive, and the addition of these particles increased the adhesives' radiopacity (p < 0.05). There was a significant decrease in the degree of conversion with CeO2 loadings higher than 1.44 vol.%. However, all materials showed a similar degree of conversion in comparison to commercially available adhesives. CeO2 particles were investigated for the first time as a promising compound to improve the radiopacity of the dental adhesives.

Niobium containing bioactive glasses as remineralizing filler for adhesive resins.

OBJECTIVE: The aim of this study was to incorporate sol-gel-derived bioactive glass as filler into experimental adhesive resins and evaluate the influence of glass composition on the physicochemical and biological properties of the developed adhesives. MATERIALS AND METHODS: Sol-gel particles were produced with or without the addition of niobium (BAGNb or BAG, respectively). The produced particles were incorporated (2wt%) into experimental adhesive resins formulated with 66wt% bisphenol A-glycidyl methacrylate and 33wt% hydroxyethyl methacrylate. Ethyl dimethyl-4-aminobenzoate and camphorquinone were used as photoinitiator system. Two experimental groups were produced: ABAGNb and ABAG. The adhesive without particles was used as control (ACG). The materials were tested for their degree of conversion, softening in solvent, and cytotoxicity. The mineral deposition was analyzed by Raman spectroscopy. Flexural strength and immediate and 1-year microtensile bond strength were evaluated. RESULTS: No statistical difference was found in degree of conversion. ABAGNb showed reduced softening and higher mineral deposition than ACG and ABAG after 28 days. ABAG and ABAGNb resulted in higher cell viability and lower flexural strength when compared to ACG. After 1-year, ABAGNb and ABAG presented statistically significant lower µTBS values. SIGNIFICANCE: Sol-gel-derived bioactive glasses promoted increased mineral deposition and cell viability for experimental adhesives with increased phosphate content and longitudinal µTBS values for the ABAGNb group. These results suggest the potential of the studied particles to be applied as bioactive fillers for dental adhesives. Reductions in longitudinal µTBS and flexural strength, however, were observed for both glasses compositions and must be considered.

Nanoneedle-like zinc oxide as a filler particle for an experimental adhesive resin.

AIM: The aim of this study was to develop an experimental adhesive resin with nanoneedle-like zinc oxide (N-ZnO), an inorganic filler, that could avoid particle agglomeration and lead to a homogeneous stress distribution within the material and characterize it. MATERIALS AND METHODS: N-ZnO particles obtained by a thermal evaporation technique were characterized regarding size and surface area and added at 0 (control), 1, 2, 5, and 10 wt%, to an experimental adhesive resin. The following experimental adhesive resins' properties were assessed: radiopacity, contact angle to conditioned enamel and dentin, color, degree of conversion, flexural strength, resistance to degradation, and cytotoxicity. Statistical analysis was performed using one-way ANOVA and Tukey's post hoc test and paired Student's t-test. RESULTS: Particles presented a mean particle size of 40 nm and a specific surface area of 16 m2/g. N-ZnO10%showed an increased radiopacity when compared to N-ZnO0%. Contact angles were significantly higher for N-ZnO10%at enamel and N-ZnO2%, N-ZnO5%, and N-ZnO10%at dentin. All groups showed color change when compared to N-ZnO0%. Higher the N-ZnO concentration, lower the degree of conversion. There were no significant differences between the groups for flexural strength and resistance to degradation. The addition of N-ZnO showed no difference in cytotoxicity when compared to positive control, N-ZnO0%, and all groups showed higher values than negative control. CONCLUSIONS: N-ZnO possibly exceeded potential limitations due to particles' agglomeration and improved the transference and distribution of stress within the material. It could be effectively used as a filler for adhesive resins.

Mineral deposition promoted by resin-based sealants with different calcium phosphate additions.

The aim of this study was to evaluate the influence of different calcium phosphates (CaPs) on the physical, biological, and remineralizing properties of experimental resin-based sealants (RBSs). Triethylene-glycol dimethacrylate (90wt%) and bisphenol A-glycidyl methacrylate (10wt%) were used to produce resin-based sealants. Hydroxyapatite (SHAp), α-tricalcium phosphate (Sα-TCP) and octacalcium phosphate (SOCP) were added to the sealants in a 10wt% concentration. One group without CaPs was used as the control group (SCG). The degree of conversion (DC) was assessed with Fourier-transformed infrared spectroscopy, whereas cytotoxicity was tested with the HaCaT keratinocyte cell line. The ultimate tensile strength (UTS) was used to assess the mechanical strength of the experimental RBSs. Sealed enamel was used for colorimetric assay. Mineral deposition was assessed with Raman spectroscopy after 7, 14, and 28 days of sample immersion in artificial saliva. Scanning electron microscopy was used to analyze the surface morphology after 28 days of immersion. The addition of 10wt% of fillers significantly reduced the DC of sealants. SOCP groups showed reduced cell viability. Higher UTS was found for Sα-TCP and SHAp. The color analysis showed that SGC and demineralized teeth presented higher mismatches with the sound tissue. Mineral deposition was observed for SHAp and Sα-TCP after 7 days, with increased phosphate content and mineral deposits for SHAp after 28 days. RBS with the addition of 10% HAp promoted increased mineralization in vitro after 28 days, and did not affect cell viability, DC, mechanical properties, or RBS color in the enamel.

Boron Nitride Nanotubes as Filler for Resin-Based Dental Sealants.

The aim of this study was to evaluate the influence of boron-nitride nanotubes (BNNTs) on the properties of resin-based light-curing dental sealants (RBSs) when incorporated at different concentration. RBSs were formulated using methacrylate monomers (90 wt.% TEGDMA, 10 wt.% Bis-GMA). BNNTs were added to the resin blend at 0.1 wt.% and 0.2 wt.%. A Control group without filler was also designed. Degree of conversion, ultimate tensile strength, contact angle, surface free energy, surface roughness and color of the RBSs were evaluated for the tested materials. Their cytotoxicity and mineral deposition ability (Bioactivity) were also assessed. A suitable degree of conversion, no effect in mechanical properties and no cytotoxic effect was observed for the experimental materials. Moreover, the surface free energy and the surface roughness decreased with the addition of BNNTs. While the color analysis showed no difference between specimens containing BNNTs and the control group. Mineral deposition occurred in all specimens containing BNNTs after 7d. In conclusion, the incorporation of BNNTs may provide bioactivity to resin-based dental sealants and reduce their surface free energy.

Calcium phosphates as fillers for methacrylate-based sealer.

OBJECTIVES: The aim of this study was to evaluate the mineral deposition, push-out bond strength, radiopacity, the degree of conversion, film thickness, flow, calcium ion release, and pH of experimental endodontic sealers containing hydroxyapatite (HAp), aflfa-ticalcium phosphate (α-TCP), or octacalcium phosphate (OCP) particles. MATERIALS AND METHODS: Fifty single straight root human premolars were instrumented and divided into five groups (n = 10). Experimental endodontic sealers were formulated by 70 wt% urethane dimethacrylate (UDMA), 15 wt% of glycerol-1,3-dimethacrylate (GDMA), 15 wt% of ethoxylated bisphenol A glycol dimethacrylate (BISEMA), camphorquinone (CQ), N,N-dihydroxyethyl-para-toluidine (DHEPT), and benzoyl-peroxide. 10 wt% of each HAp, α-TCP, or OCP were added to the resin and its properties were assessed. RESULTS: After 7 days, the degree of conversion ranged from 44.69% (GOCP) to 50.74% (Gcontrol) and no statistical difference were observed (p < 0.05). GAHplus showed the highest push-out bond strength 4.91 (± 2.38) MPa at 28 days of analysis (p < 0.05). Film thickness and pH were not statistically different (p > 0.05). Statically lower values of flow were found for GHAp, GOCP, and Gα-TCP (p < 0.05). Calcium deposition values were higher for GHAp at 28 days. CONCLUSIONS: Bond strength, degree of conversion, and film thickness of endodontic sealers with phosphates showed similar results compared with AHplus, but displayed higher amounts of Ca2+ release. CLINICAL RELEVANCE: Phosphate fillers improve the performance of endodontic sealers after 28 days of simulated body fluid.

Evaluation of an antibacterial orthodontic adhesive incorporated with niobium-based bioglass: an in situ study.

This in situ study aimed to evaluate the antibacterial and anti-demineralization effects of an experimental orthodontic adhesive containing triazine and niobium phosphate bioglass (TAT) around brackets bonded to enamel surfaces. Sixteen volunteers were selected to use intra-oral devices with six metallic brackets bonded to enamel blocks. The experimental orthodontic adhesives were composed by 75% BisGMA and 25% TEGDMA containing 0% TAT and 20% TAT. Transbond XT adhesive (TXT) was used as a control group. Ten volunteers, mean age of 29 years, were included in the study. The six blocks of each volunteer were detached from the appliance after 7 and 14 days to evaluate mineral loss and bacterial growth including total bacteria, total Streptococci, Streptococci mutans, and Lactobacilli. Statistical analysis was performed using GLM model - univariate analysis of variance for microhardness and 2-way ANOVA for bacterial growth (p<0.05). The 20% TAT adhesive caused no difference between distances from bracket and the sound zone at 10-µm deep after 7 and 14 days. After 14 days, higher mineral loss was shown around brackets at 10- to 30-µm deep for TXT and 0% TAT adhesives compared to 20% TAT. S. mutans growth was inhibited by 20% TAT adhesive at 14 days. Adhesive with 20% TAT showed lower S. mutans and total Streptococci growth than 0% TAT and TXT adhesives. The findings of this study show that the adhesive incorporated by triazine and niobium phosphate bioglass had an anti-demineralization effect while inhibiting S. mutans and total Streptococci growth. The use of this product may inhibit mineral loss of enamel, preventing the formation of white spot lesions.

Physical and mechanical properties of dual functional cements-an in vitro study.

OBJECTIVES: The aim of this study was to evaluate the physical and mechanical properties of different dual functional cements. MATERIALS AND METHODS: Three dual functional cements (Allcem Core (FGM), Rebilda DC (VOCO), and LuxaCore Z (DMG)), a luting resin cement (Rely X ARC (3 M ESPE)), and a Core Buildup composite resin GrandioSo (VOCO) were used. Flexural strength (n = 10) and film thickness (n = 6) were evaluated according to ISO 4049:2009. Flow (n = 6) was evaluated according to ISO 6876:2001. Degree of conversion (DC) was assessed immediately and 24 h after polymerization (n = 5). For resistance to dislodgment (RD) analysis, bovine teeth were prepared to receive fiber glass posts, and a push-out test (n = 12) was used. RESULTS: Luxacore Z presented lower flexural strength when compared to GrandioSo (p < 0.001). No statistical difference was found between cements for film thickness (p = 0.66). Reduced flow values were found for Allcem Core (p = 0.006). No statistical difference was found for immediate DC for different cements (p > 0.05). After 24 h, DC increased for all groups, except for Luxacore Z (p = 0.054). The RD did not differ from the control Rely X ARC, regardless of the root third (p > 0.05). Luxacore Z showed lower mean values in the apical third compared to the coronal third (p = 0.046). CONCLUSIONS: The dual functional cements (Allcem Core and Rebilda DC) possessed similar physical and mechanical properties of luting resin cement (RelyX ARC) and Core Buildup composite resin (GrandioSo). Hence, they could be used for one-stage post and core buildup restorations. CLINICAL RELEVANCE: The dual functional cements could be used for one-stage post and core buildup restorations since they possess similar physical and mechanical properties of luting resin cements and Core Buildup composite resin.

Effect of immersion in various disinfectant solutions on the properties of a heat-cured acrylic resin / Efeito da imersão em diferentes soluções desinfetantes nas propriedades de uma resina acrílica de termoativação

ABSTRACT Objective: The aim of the present study was to evaluate the influence, of immersion in different disinfectant solutions, on microhardness and surface roughness of a heat-cured acrylic resin. Methods: Specimens were immersed in distilled water, commercial vinegar for domestic use, sodium hypochlorite and hydrogen peroxide, for 150 hours or 300 hours (n=10). After periods of immersion, Knoop microhardness and surface roughness were evaluated using a microhardness tester and a roughness tester, respectively. The data were analyzed using two-way ANOVA and Holm-Sidak, at a level of significance of 5%. Results: The microhardness values ranged from 16.90 ± 0.33 to 17.80 ± 0.51 and roughness values from 0.05 ± 0.01 to 0.08 ± 0.02. There is no difference in microhardness and roughness between groups and times (p>0.05). Conclusion: Within the limitations of this study, it is possible to conclude that vinegar and hydrogen peroxide, as alternative disinfectant solutions for acrylic resin devices, did not promote deleterious effects on microhardness and polishing of a heat-cured acrylic resin used for the fabrication of prostheses, neither in the medium term nor the long term.

RESUMO Objetivo: Avaliar a influência da imersão em diferentes soluções desinfetantes na microdureza e rugosidade de uma resina acrílica de termoativação. Métodos: Corpos de prova de resina acrílica termopolimerizável foram imersos em água destilada, vinagre comercial de uso doméstico, hipoclorito de sódio e peróxido de hidrogênio, por períodos de 150 h ou 300 h (n=10). A microdureza Knoop e a rugosidade superficial dos corpos de prova foram avaliadas com o uso de microduro?metro e rugosímetro, respectivamente. Os dadosforam analisados com o teste análise de variância a dois critérios e Holm-Sidak, com nível de significância de 5%. Resultados: Osvalores de microdureza variaram de 16,90 ± 0,33 a 17,80 ± 0,51 e a rugosidade, de 0,05 ± 0,01a 0,08 ± 0,02. Não houve diferença nos resultados de microdureza e rugosidade entre os grupos e tempos (p>0.05). Conclusão: Dentro das limitações do estudo, é possível concluir que a utilização de vinagre ou de peróxido de hidrogênio, como alternativas para a desinfecção de resina acrílica, não provocam efeitos deletérios na dureza e no polimento da resina acrílica termoativada utilizada para confecção de próteses, nem a médio nem a longo prazo.

Evaluation of an antibacterial orthodontic adhesive incorporated with niobium-based bioglass: an in situ study

Abstract This in situ study aimed to evaluate the antibacterial and anti-demineralization effects of an experimental orthodontic adhesive containing triazine and niobium phosphate bioglass (TAT) around brackets bonded to enamel surfaces. Sixteen volunteers were selected to use intra-oral devices with six metallic brackets bonded to enamel blocks. The experimental orthodontic adhesives were composed by 75% BisGMA and 25% TEGDMA containing 0% TAT and 20% TAT. Transbond XT adhesive (TXT) was used as a control group. Ten volunteers, mean age of 29 years, were included in the study. The six blocks of each volunteer were detached from the appliance after 7 and 14 days to evaluate mineral loss and bacterial growth including total bacteria, total Streptococci, Streptococci mutans, and Lactobacilli. Statistical analysis was performed using GLM model - univariate analysis of variance for microhardness and 2-way ANOVA for bacterial growth (p<0.05). The 20% TAT adhesive caused no difference between distances from bracket and the sound zone at 10-µm deep after 7 and 14 days. After 14 days, higher mineral loss was shown around brackets at 10- to 30-µm deep for TXT and 0% TAT adhesives compared to 20% TAT. S. mutans growth was inhibited by 20% TAT adhesive at 14 days. Adhesive with 20% TAT showed lower S. mutans and total Streptococci growth than 0% TAT and TXT adhesives. The findings of this study show that the adhesive incorporated by triazine and niobium phosphate bioglass had an anti-demineralization effect while inhibiting S. mutans and total Streptococci growth. The use of this product may inhibit mineral loss of enamel, preventing the formation of white spot lesions.

Performance of progressive and constant tapered instruments rotary systems at canal preparation / Desempenho de sistemas endodônticos rotatórios constante e progressivo no preparo do canal radicular

ABSTRACT Objective: The aim of this study was to compare the performance of two nickel-titanium rotary systems regarding the preparation time, final shape of canal, incidence of aberration, transportation, and fracture of instrument. Methods: A total of 40 simulated canals in resin blocks with 30o curves and a length of 17 mm were divided randomly into two groups: preparation with ProTaper and BioRaCe systems up to F5 and BR5 respectively. Pre- and post-operative canal images were taken and superimposed in order to identify aberrations, transportation, and to take measurements of the canal width. In addition, the preparation time and instrument fractures were recorded. The data were analyzed using Student's t test. Results: There is no difference (p>.05) comparing the systems regarding preparation time, canal aberration, and instrument fracture rates. The progressive tapered instruments of ProTaper prepared significantly larger canal widths in the apical third (p<.05). Conclusion: Overall, both systems provided safe canal preparation, associated with few canal aberrations and instrument fractures.

RESUMO Objetivo: Comparar o desempenho de dois sistemas rotatórios em relação ao tempo de preparo, formato final e alterações do canal, desvio e fratura de instrumento. Métodos: Um total de 40 canais simulados em blocos de resina com curvatura de 30o e comprimento de 17 mm foram divididos randomicamente nos sistemas ProTaper e BioRaCe preparados até F5 e BR5 respectivamente. Imagens pré e após o preparo dos canais foram obtidas e superpostas para identificação de alterações de forma, desvios e largura. O tempo de preparo e fratura de instrumentos também foram avaliados. Os dados foram analisados por teste t de Student. Resultados: O tempo de preparo, alterações de forma e taxa de fratura de instrumentos não teve diferença entre os dois sistemas avaliados (p>0,05). Os instrumentos progressivos do ProTaper resultou em canais significativamente mais largos no terço apical (p<0,05). Conclusão: Os dois sistemas rotatórios avaliados resultaram em preparo endodôntico seguro, com poucas alterações e fratura de instrumento.

Effect on adhesion of a nanocapsules-loaded adhesive system.

This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey's post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal µTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.

Effect of nanostructured zirconium dioxide incorporation in an experimental adhesive resin.

OBJECTIVES: The aim of this study was to evaluate the influence of nanostructured zirconium dioxide incorporation in an experimental adhesive resin. METHODS: ZrO2 particles were characterized by X-ray diffraction (XRD), micro-Raman spectroscopy and Brunauer-Emmett-Teller (B.E.T). Experimental adhesive resins were formulated with 0, 0.5, 1, 4.8, and 9.1% ZrO2 in weight. The adhesives were evaluated based on degree of conversion (DC), radiopacity, softening in solvent and microtensile bond strength (µTBS) 24 h and after 1 year of aging. Mineral deposition at the hybrid layer was assessed with micro-Raman spectroscopy at the baseline and after 14 days. RESULTS: XRD showed monoclinic and tetragonal phases of ZrO2.particles. B.E.T data revealed a surface area of 37.41 m2/g, and typical chemical groups were shown on the Raman spectra. The addition of ZrO2 did not influence the radiopacity. The addition of 4.8% and 9.1 wt.% ZrO2 showed higher initial hardness with increased softening in solvent (P < 0.05) and promoted mineral deposition at the dentin interface. DC was significantly increased in the group with 1% ZrO2 (P < 0.05). The µTBS test showed difference on the group with 9.1 wt.% of ZrO2, with a significant reduction after aging. CONCLUSION: The incorporation of ZrO2 promoted mineral deposition on the adhesive interface and the addition of 1 wt.% caused a significant increase on the DC without compromising the other physicochemical characteristics, which may prove promising for the development of new dental adhesive systems. CLINICAL RELEVANCE: The mineral deposition on the hybrid layer can result in a longer stability of the adhesive, thus delaying the hydrolytic degradation.

Influence of the addition of microsphere load amoxicillin in the physical, chemical and biological properties of an experimental endodontic sealer.

AIM: To develop an endodontic sealer with amoxicillin-loaded microsphere and to evaluate its properties. METHODS: Experimental sealer was obtained by mixing 70wt% UDMA, 15wt% GDMA and 15wt% BISEMA. In addition, CQ, DHEPT and PB were incorporated at 1 mol% and 0.01wt% BHT and 10wt% YbF3. Microspheres were produced by drying in spray dryer. Two experimental groups (10 and 15wt% of microspheres) and one control group (without microspheres) were formulated. The sealers were evaluated for the degree of conversion (n=3), degradation in solvent (n=3), drug release profile (n=3), antimicrobial activity (n=3), flow (n=3), film thickness (n=3) and cytotoxicity (n=3). Data were analyzed by ANOVA and Tukey with significance level of 5%. RESULTS: Microespheres presented a mean size of 2.664µm. Immediate degree of conversion ranged from 51.73% to 55.13% and the 24h degree of conversion ranged from 60.79% to 73.80%. Upon solvent degradation 54.44% and 56.21% reduction in hardness were observed for 10% and 15% concentrations respectivelly. The drug release profile showed an average release of 73.76% of the drug in 96h. Significant reduction in antimicrobial activity was observed for 10% concentration after 24h, 48h and 96h compared to control. The flow and film thickness showed values in accordance to the ISO 6876. Cytotoxicity showed high cellular viability. CONCLUSION: The addition of up to 10% of microspheres containing amoxicillin presented antimicrobial activity and did not alter the properties of the experimental endodontic cement. CLINICAL SIGNIFICANCE: Amoxicillin microspheres with its antimicrobial activity in root canal sealers could reduce reintervations in endodontics when persistent bacteria or reinfection takes place in root canal system.

Methacrylate-based root canal sealer containing chlorexidine and α-tricalcium phosphate.

The aim of this study was to develop and to characterize a methacrylate-based root canal sealer containing chlorhexidine (CHX) and α-tricalcium phosphate (α-TCP). Experimental dual cure methacrylate-based sealer was produced containing 0, 2.5, or 5 wt% of CHX and 0, 25, or 50 wt% of α-TCP. Experimental sealers were evaluated based on flow, film thickness, radiopacity, degree of conversion (DC), degradation in water, pH and antibacterial activity. Flow ranged from 15.09 ± 0.11 to 17.47 ± 0.42 mm. All groups presented mean film thickness lower than 50 µm and had radiopacity equivalent to 3 mmAl. DC was higher than 60% for all compositions. The weight loss (WL) ranged 0.12-3.47%. The groups containing 5% of CHX presented the highest WL and the lower pH values after 28 days of water immersion. All chlorexidine-compositions exhibited antibacterial efficacy against Enterococcus faecalis on direct contact and agar diffusion tests. CHX and α-TCP addition at an experimental methacrylate-based root canal sealer influenced the physicochemical properties and provided antibacterial properties. The incorporation of CHX and α-TCP could be an alternative to antibacterial sealers with potential to improve periapical healing in endodontic treatments. © 2017 Wiley Periodicals, Inc. J Biomater Res Part B: 106B: 1439-1443, 2018.

Effect on adhesion of a nanocapsules-loaded adhesive system

Abstract This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey's post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal μTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.

Effect of beverages on surface properties of resin-based sealants

Aim: The aim of this study was to determine degree of conversion of resin-based sealants and the effect of beverages on surface roughness and color change of materials. Methods: Two commercial resin-based sealants were evaluated (Defense Chroma® and BioSeal®). Degree of conversion (DC) was initially measured using Fourier-transformed infrared (FTIR). Specimens of each sealant were maintained in distilled water and immersed one hour daily in grape juice and cola drink for 30 days. One group was maintained only in distilled water, as a control. Surface roughness and color change were measured before immersion, after seven days of immersion and after 30 days of immersion. Results were analyzed using t-test, paired t-test, one-way repeated measures ANOVA, one-way ANOVA and post-hoc tests (0.05 level of significance). Results: There was no significant difference regarding degree of conversion and initial surface roughness comparing both commercial sealants. Surface roughness increased for BioSeal® immersed in cola drink for 30 days. After 30 days, all groups presented significant color change. Conclusions: The effect of beverages on color stability and surface roughness of resin-based sealants depended on exposure time and kind of beverage (AU)

Anti-inflammatory effect of an adhesive resin containing indomethacin-loaded nanocapsules.

OBJECTIVE: To analyze the anti-inflammatory and analgesic effects of an adhesive resin containing indomethacin-loaded nanocapsules in rat model. DESIGN: Adhesive resin disks with or without indomethacin-loaded nanocapsules were subcutaneously implanted into right hind paw of rats. A week after surgical procedure, 2% formalin solution was intradermally injected into plantar surface of paw. Nociceptive and inflammatory responses were evaluated by formalin test. Paw edema by pletismometer and mechanical hyperalgesia by von Frey test were performed on day 2, day 4, day 6, day 8, day 10 and day 12 after surgery. IL-6, IL-10, and lactate dehydrogenase (LDH) serum levels were determined by ELISA-sandwich test. RESULTS: Group containing indomethacin-loaded nanocapsules (NC) presented lower edema in the right hind paw at 24h after formalin injection than those of the control group (CT) (P<0.01). NC group showed decrease in the nociceptive response in phase I (neurogenic pain) compared to CT group (NC - 66.86±22.83s X CT - 130.17±35.83s, P<0.001). NC group presented supporting higher intensity of stimulus on days 8 and 12 (24h and 72h after formalin injection) (P<0.01 and P<0.02 respectively). The IL-6 serum level was also significantly higher in the NC group than CT group (p<0.001). CONCLUSIONS: These results indicate that an adhesive resin containing indomethacin-loaded nanocapsules has anti-inflammatory and nociceptive activities in a chemical model of acute inflammation. The present investigation confirms an adhesive resin with drug-loaded nanocapsules may be useful for improving therapeutic effect for adhesives to be used in deep cavities.

Influence of addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride to an experimental adhesive.

The aim of this study was to develop an experimental adhesive with addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride (METAC) and to evaluate its mechanical and biological properties and its in vitro antibacterial activity. An experimental adhesive resin was formulated with Bis-GMA, TEGDMA, and HEMA. The antibacterial monomer was added at concentrations of 1%, 2.5%, and 5% (METAC groups). A group without METAC addition was used as control. The experimental adhesives were evaluated as to their antibacterial potential against Streptococcus mutans, degree of conversion, and softening in ethanol for 2 hours. The data were analyzed by one-way ANOVA, Tukey's post-hoc test, and the paired Student's t-test (significance level of 0.05). METAC showed antibacterial activity against S. mutans at all concentrations (p < 0.05). There was no statistical difference across METAC groups (p > 0.05). The 1%, 2.5%, and 5% groups yielded the highest mean values for degree of conversion (p < 0.05). The 1% group did not differ from the control group (p > 0.05). There was no statistical difference in baseline microhardness values (p > 0.05) and microhardness values after immersion in ethanol were lower than at baseline for all groups (p < 0.05). There was no statistical difference in the reduction of Knoop hardness number (KHN) after immersion in ethanol for any of the groups (p > 0.05). The results of the present study indicate that METAC is a promising antibacterial agent when added to an adhesive system.