Hydrogels Based on Natural Polymers Loaded with Bentonite and/or Halloysite: Composition Impact on Spectroscopic, Thermal, and Swelling Properties.

Hydrogels are characterized by their property of absorbing and releasing a high content of water and water-based liquids; thus, they can be applied in agriculture as controlled-release water and fertilizer products. The focus of this research was efficient and low-cost natural polymer-based hydrogels obtained by crosslinking gellan gum (GGLA) and starch (ST) with acetic acid (CA) and loading them with either bentonite (BET) and/or halloysite (HAL). The hydrogels were obtained by mixing 100, 75, 50, 25, and 0 wt.% of GGLA with 0, 25, 50, 75, and 100 wt.% ST water solutions. To obtain the networks, they were crosslinked with 10, 5, and 2 wt.% of CA and loaded with 2, 5, and 10 wt.% of BET and/or HAL. The samples were analyzed by infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), their swelling in water, and the state of bound water properties. The results of these analyses point to the formation of a polymeric network with a decomposition temperature of >250 °C, and tailorable swelling properties that vary between 3 and 77, depending on the hydrogel composition. In summary, GGLA-ST-BET/HAL hydrogels are a good option for eco-friendly agriculture materials.

Improved Conductivity in Gellan Gum and Montmorillonite Nanocomposites Electrolytes.

Nanocomposite polymer electrolytes (NPEs) were obtained using gellan gum (GG) and 1 to 40 wt.% of montmorillonite (Na+SYN-1) clay. The NPEs were crosslinked with formaldehyde, plasticized with glycerol, and contained LiClO4. The samples were characterized by impedance spectroscopy, thermal analyses (TGA and DSC), UV-vis transmittance and reflectance, X-ray diffraction (XRD), and continuous-wave electron paramagnetic resonance (CW-EPR). The NPEs of GG and 40 wt.% LiClO4 showed the highest conductivity of 2.14 × 10-6 and 3.10 × 10-4 S/cm at 30 and 80 °C, respectively. The samples with 10 wt.% Na+SYN-1 had a conductivity of 1.86 × 10-5 and 3.74 × 10-4 S/cm at 30 and 80 °C, respectively. TGA analyses revealed that the samples are thermally stable up to 190 °C and this did not change with clay addition. The transparency of the samples decreased with the increase in the clay content and at the same time their reflectance increased. Finally, CW-EPR was performed to identify the coordination environment of Cu2+ ions in the GG NPEs. The samples doped with the lowest copper concentration exhibit the typical EPR spectra due to isolated Cu2+ ions in axially distorted sites. At high concentrations, the spectra become isotropic because of dipolar and exchange magnetic effects. In summary, GG/clay NPEs presented good ionic conductivity results, which qualifies them for electrochemical device applications.