RESUMO
Discovering ways to increase the LED light extraction efficiency (LEE) should help create the largest performance improvement in the power of UV AlGaN LEDs. Employing surface roughening to increase the LEE of typical AlGaN UV LEDs is challenging and not well understood, yet it can be achieved easily in AlGaN LEDs grown on SiC. We fabricate thin-film UV LEDs (~294-310 nm) grown on SiC-with reflective contacts and roughened emission surface-to study and optimize KOH roughening of N-face AlN on the LEE as a function of roughened AlN pyramid size and KOH solution temperature. The LEE increased the most (2X) when the average AlN pyramid base diagonals (d) were comparable to the electroluminescence (EL) wavelength in the AlN layer (d ~λEL; 42-52 pyramids/µm2), but the LEE enhancement diminished when d was much larger than λEL (d ~5.5λEL; 2-3 pyramids/µm2). The UV LEDs had a 10 nm p-GaN contact layer, and the forward voltage was ~6 V at ~8 A/cm2, with a voltage efficiency (VE) of ~70%. The VE of the LEDs did not change after KOH roughening. This work suggests important implications to increase the LEE of AlGaN LEDs.
RESUMO
We demonstrate very high luminous efficacy green light-emitting diodes employing Al0.30Ga0.70N cap layer grown on patterned sapphire substrates by metal organic chemical vapor deposition. The peak external quantum efficiency and luminous efficacies were 44.3% and 239 lm/w, respectively. At 20 mA (20 A/cm2) the light output power was 14.3 mW, the forward voltage was 3.5 V, the emission wavelength was 526.6 nm, and the external quantum efficiency was 30.2%. These results are among the highest reported luminous efficacy values for InGaN based green light-emitting diodes.