Magnetic carboxymethyl cellulose-silk fibroin hydrogel: A ternary nanobiocomposite exhibiting excellent biological activity and in vitro hyperthermia of cancer therapy.

In this work, a magnetic nanobiocomposite scaffold based on carboxymethylcellulose (CMC) hydrogel, silk fibroin (SF), and magnetite nanoparticles was fabricated. The structural properties of this new magnetic nanobiocomposite were characterized by various analyses such as FT-IR, XRD, EDX, FE-SEM, TGA and VSM. According to the particle size histogram, most of the particles were between 55 and 77 nm and the value of saturation magnetization of this nanobiocomposite was reported 41.65 emu.g- 1. Hemolysis and MTT tests showed that the designed magnetic nanobiocomposite was compatible with the blood. In addition, the viability percentage of HEK293T normal cells did not change significantly, and the proliferation rate of BT549 cancer cells decreased in its vicinity. EC50 values for HEK293T normal cells after 48 h and 72 h were 3958 and 2566, respectively. Also, these values for BT549 cancer cells after 48 h and 72 h were 0.4545 and 0.9967, respectively. The efficiency of fabricated magnetic nanobiocomposite was appraised in a magnetic fluid hyperthermia manner. The specific absorption rate (SAR) of 69 W/g (for the 1 mg/mL sample at 200 kHz) was measured under the alternating magnetic field (AMF).

Fabrication of a magnetic alginate-silk fibroin hydrogel, containing halloysite nanotubes as a novel nanocomposite for biological and hyperthermia applications.

In this study, the main focus was on designing and synthesizing a novel magnetic nanobiocomposite and its application in hyperthermia cancer treatment. Regarding this aim, sodium alginate (SA) hydrogel with CaCl2 cross-linker formed and modified by silk fibroin (SF) natural polymer and halloysite nanotubes (HNTs), followed by in situ Fe3O4 magnetic nanoparticles preparation. No important differences were detected in red blood cells (RBCs) hemolysis, confirming the high blood compatibility of the treated erythrocytes with this nanobiocomposite. Moreover, the synthesized SA hydrogel/SF/HNTs/Fe3O4 nanobiocomposite does not demonstrate toxicity toward HEK293T normal cell line after 48 and 72 h. The anticancer property of SA hydrogel/SF/HNTs/Fe3O4 nanobiocomposites against breast cancer cell lines was corroborated. The magnetic saturation of the mentioned magnetic nanobiocomposite was 15.96 emu g-1. The specific absorption rate (SAR) was measured to be 22.3 W g-1 by applying an alternating magnetic field (AMF). This novel nanobiocomposite could perform efficiently in the magnetic fluid hyperthermia process, according to the obtained results.

Decoration of graphene oxide nanosheets with carboxymethylcellulose hydrogel, silk fibroin and magnetic nanoparticles for biomedical and hyperthermia applications.

In this study, an efficient nanobiocomposite based on graphene oxide (GO), carboxymethylcellulose (CMC) hydrogel, silk fibroin (SF), and Fe3O4 nanoparticles was synthesized. For this purpose and in order to provide a suitable scaffold for the nanobiocomposite, GO was functionalized with a CMC hydrogel via covalent bonding. In the next step, SF was added to the synthesized structure to increase biocompatibility and biodegradability. Fe3O4 was added into the structure by an in situ process and the GO-CMC hydrogel/SF/Fe3O4 nanobiocomposite was synthesized. The synthesized structure was evaluated in terms of toxicity and hemocompatibility and finally, it was used in the hyperthermia technique. This nanocomposite did not destroy healthy HEK293T cells after 48 h and 72 h, while it did annihilate BT549 cancer cells. The GO-CMC hydrogel/SF/Fe3O4 nanobiocomposite has EC50 values of 0.01466 and 0.1415 against HEK293T normal cells and BT549 cancer cells, respectively (after 72 h). The nanocomposite has good potential in hyperthermia applications and at a concentration and a frequency of 1 mg mL-1 and 400 kHz it has a SAR of 67.7 W g-1.