RESUMO
High surface area activated carbons were prepared with Spartina alterniflora and cotton stalk as raw materials and KOH as activating agent. Effects of materials type, impregnation ratio, activation temperature and heat preservation time on the yield, elemental composition and adsorptive capacity of activated carbon were studied. The properties and pore structure of the carbons were characterized with nitrogen adsorption, powder X-ray diffractometry (XRD), infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Main pore characteristics of activated carbons were analyzed by BET equation, Horvath-Kawazoe BET method and DFT method. The considerable preparation conditions are obtained as follows: impregnation ratio of 3: 1, an activation temperature of 800 degrees C and an activation time of 1.5 h. The BET surface area of activated carbon prepared from Spartina alterniflora reached 2 825 m2 x g(-1) when its total pore volume, yield, iodine number and methylene blue adsorption were 1.374 cm3 x g(-1), 16.36%, 1797 mg x g(-1) and 495 mg x g(-1) respectively under above conditions. The activated carbon from cotton stalk was prepared with BET surface area of 2 135 m2 x g(-1), total pore volume of 1.038 cm3 x g(-1), yield of 11.22%, methylene blue adsorption of 1 251 mg x g(-1), and iodine number of 478 mg x g(-1), respectively. The methylene blue adsorption and iodine number are much higher than the national first level for activated carbon. The Langmuir maximum adsorption capacities of 2,4-dinitrophenol on the two carbons were 932 mg x g(-1) and 747 mg x g(-1), respectively, which are superior to ordinary activated carbon and activated carbon fiber.