Influence of Strontium on the Biological Behavior of Bioactive Glasses for Bone Regeneration.

Bioactive glasses (BGs) can potentially be applied in biomedicine, mainly for bone repair and replacement, given their unique ability to connect to natural bone tissue and stimulate bone regeneration. Since their discovery, several glass compositions have been developed to improve the properties and clinical abilities of traditional bioactive glass. Different inorganic ions, such as strontium (Sr2+), have been incorporated in BG due to their ability to perform therapeutic functions. Sr2+ has been gaining prominence due to its ability to stimulate osteogenesis, providing an appropriate environment to improve bone regeneration, in addition to its antibacterial potential. However, as there are still points in the literature that are not well consolidated, such as the influence of ionic concentrations and the BG production technique, this review aims to collect information on the state of the art of the biological behavior of BGs containing Sr2+. It also aims to gather data on different types of BGs doped with different concentrations of Sr2+, and to highlight the manufacturing techniques used in order to analyze the influence of the incorporation of this ion for bone regeneration purposes.

Solution Blow Spun Silica Nanofibers: Influence of Polymeric Additives on the Physical Properties and Dye Adsorption Capacity.

The physical properties of porous silica nanofibers are an important factor that impacts their performance in various applications. In this study, porous silica nanofibers were produced via solution blow spinning (SBS) from a silica precursor/polymer solution. Two polyvinylpyrrolidone (PVP, Mw = 360,000 and 1,300,000) were chosen as spinning aids in order to create different pore properties. The effect of their physical properties on the adsorption of methylene blue (MB) in an aqueous solution was explored. After forming, the nanofibers were calcined to remove the organic phase and create pores. The calcined nanofibers had a large amount of micro and mesopores without the use of additional surfactants. The molecular weight of the PVP impacted the growth of silica particles and consequently the pore size. High Mw PVP inhibited the growth of silica particles, resulting in a large volume of micropores. On the other hand, silica nanofibers with a high fraction of mesopores were obtained using the lower Mw PVP. These results demonstrate a simple method of producing blow spun silica nanofibers with defined variations of pore sizes by varying only the molecular weight of the PVP. In the adsorption process, the accessible mesopores improved the adsorption performance of large MB molecules.

Development of Scheelite Tailings-Based Ceramic Formulations with the Potential to Manufacture Porcelain Tiles, Semi-Stoneware and Stoneware.

New ceramic formulations based on scheelite tailing were developed, and their potential in the ceramic industry was evaluated. Green bodies with different contents of scheelite tailing (0-8 wt%) were sintered (1150 °C, 1200 °C, and 1250 °C) and characterized in terms of the main mineralogical phases, microstructure, and physico-mechanical properties. The mullite was the main phase identified in all sintered temperatures. This result was also ratified with the aid of scanning electron microscope (SEM) images, in which small needles of the mullite were detected. The presence of mullite is required because it contributes to increasing the mechanical resistance of the material. The physico-mechanical properties measured (water absorption, linear shrinkage, apparent porosity, and flexural strength) were compared to the ISO 13006, and the samples sintered at 1150 °C presented potential to be used as semi-stoneware, while those sintered at 1200 °C and 1250 °C can be employed stoneware and porcelain tiles, respectively.