Nanostructured Metal Phosphide Based Catalysts for Electrochemical Water Splitting: A Review.

Amongst various futuristic renewable energy sources, hydrogen fuel is deemed to be clean and sustainable. Electrochemical water splitting (EWS) is an advanced technology to produce pure hydrogen in a cost-efficient manner. The electrocatalytic hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) are the vital steps of EWS and have been at the forefront of research over the past decades. The low-cost nanostructured metal phosphide (MP)-based electrocatalysts exhibit unconventional physicochemical properties and offer very high turnover frequency (TOF), low over potential, high mass activity with improved efficiency, and long-term stability. Therefore, they are deemed to be potential electrocatalysts to meet practical challenges for supporting the future hydrogen economy. This review discusses the recent research progress in nanostructured MP-based catalysts with an emphasis given on in-depth understanding of catalytic activity and innovative synthetic strategies for MP-based catalysts through combined experimental (in situ/operando techniques) and theoretical investigations. Finally, the challenges, critical issues, and future outlook in the field of MP-based catalysts for water electrolysis are addressed.

Recovery of high surface area mesoporous silica from waste hexafluorosilicic acid (H2SiF6) of fertilizer industry.

In this article we report recovery of mesoporous silica from the waste material (hexafluorosilicic acid) of phosphate fertilizer industry. The process involves the reaction of hexafluorosilicic acid (50 ml, 24 wt% H(2)SiF(6)) and 100ml, 0.297 M Na(2)CO(3) to generate the alkaline aqueous slurry. Silica was separated from the slurry by filtration and the sodium fluoride was extracted from the aqueous solution by evaporation method. The obtained mesoporous silica was characterized by N(2) absorption/desorption (BET), thermogravimetric analysis (TGA), X-ray diffraction (XRD), scanning electron microscope (SEM), and EDS. The results confirm that the separation of silica and NaF was successful and the final products have high purity. The silica product was found to have an average pore diameter of 4.14 nm and a high surface area (up to 800 m(2)/g). The process reported in this study may significantly reduce the release of hazardous materials into the environment and it might confer economic benefits to the responsible industries.