Ageing Evaluation of Foamed Polymer Modified Bitumen with Bio-Flux Additive.

This paper presents the results of an analysis of the changes in the stiffness of asphalt binders modified with a bio-flux additive and subjected to the processes of foaming and short-term ageing. The purpose of the analyses was to determine changes in the rheological properties of asphalt binder as a result of technological processes characteristic of hot and warm mix asphalt technology. Three asphalt binders with similar penetration but varying degrees of polymer modification were tested: 50/70, 45/80-55 polymer-modified bitumen, and 45/80-80 highly modified bitumen. Tests were carried out on four groups of binders: original binders, foamed binders after 14 days of storage, non-foamed binders after Rolling Thin Film Oven Test (RTFOT) ageing, and foamed binders after 14 days of storage subjected to RTFOT ageing. The master curves of the complex shear modulus G* were analysed, and three indexes of binder stiffening were determined, characterising the investigated effects. The tests showed that some of the stiffening indices significantly depended on the degree of polymer modification and the content of the bio-flux additive. Moreover, it was found that the foaming process in the case of paving-grade bitumen and polymer-modified bitumen did not contribute to the additional stiffening of the binders.

Effects of Laboratory Ageing on the FTIR Measurements of Water-Foamed Bio-Fluxed Asphalt Binders.

The study investigated the effects of laboratory ageing on the fluxed and water-foamed asphalt binders in scope of Fourier transform infrared spectroscopic measurements of ageing indicators and changes in their chemical composition. The investigated binders included two paving grades, two polymer modified asphalt binders, and a highly modified asphalt binder. The bio-flux additive was produced from rapeseed methyl esters in an oxidation reaction in the presence of a metal catalyst and organic peroxide. The use of the bio-origin additive, in particular oil derivatives, was aimed at softening and better foaming of asphalt binders. This modification is possible due to the good mixability of vegetable oils with an asphalt binder, which gives a homogeneous product with reduced stiffness. The study involved the rolling thin film oven, short-term, and the pressure ageing vessel, long term, and ageing to induce oxidation on the evaluated asphalt binders. The addition of the bio-flux additive has significantly decreased the measured content of ketone compounds related to oxidation in both non-aged and aged asphalt binders, although this effect after ageing were far smaller in magnitude. Additionally, both ageing processes decreased significantly the absorbances in the ester spectral bands specific to the bio-flux additive. All mentioned effects were similar in magnitude in all tested asphalt binders.

Warm Mix Asphalt Binder Utilizing Water Foaming and Fluxing Using Bio-Derived Agent.

The present paper investigates the effects of simultaneous mechanical foaming using water and fluxing with a bio-derived agent on the properties of three distinct asphalt binders: 50/70 paving-grade bitumen, 45/80-55 polymer-modified bitumen, and 45/80-80 highly modified asphalt binder. The testing involved classical tests for assessing binder consistency (penetration at 25 °C, ring and ball softening point, Fraass breaking point, and dynamic viscosity) as well as performance tests (high and low Superpave critical temperatures and multiple stress creep recovery). The tests included assessment directly after asphalt binder foaming and were repeated after a 14-day period. It was shown that bitumen foaming had only short-term effects on the asphalt binders, which did not persist in the repeated tests after 14 days. The fluxing agent that was utilized caused significant changes in the consistency of all asphalt binders. The changes in the performance characteristics of the 50/70 and 45/80-55 binders were severe and amounted to a significant decrease in high-temperature performance of these binders. On the other hand, an improvement in all performance characteristics in the case of the 45/80-80 asphalt binder was observed as a result of the applied processes, particularly when measured 14 days after foaming. This study shows that the simultaneous use of foaming and the fluxing additive decreased the dynamic viscosity of the 45/80-80 binder, while improving its properties relating the pavement performance.

Study of High-Temperature Properties of Asphalt Mixtures Used for Bridge Pavement with Concrete Deck.

The paper presents the issue of resistance to permanent deformations of bridge pavements placed upon concrete bridge decks. In Europe, bridge asphalt pavement usually consists of a wearing course and a protective layer, which are placed over the insulation (waterproofing). Protective layers of bridge pavement are commonly constructed using low air void content asphalt mixes as this provides the suitable tightness of such layers. Due to increased binder content, asphalt mixes for bridge pavement may have reduced resistance to permanent deformations. The article presents test results of resistance to permanent deformations of asphalt mixes for the protective layers. In order to determine the composition of mixtures with low air void content and resistance to permanent deformation, an experimental design was applied using a new concept of asphalt mix composition. Twenty-seven different asphalt mixture compositions were analyzed. The mixtures varied in terms of binder content, sand content and grit ratio. Resistance to permanent deformation was tested using the laboratory uniaxial cyclic compression method (dynamic load creep). On the basis of experimental results and statistical analysis, the functions of asphalt mixture permanent deformation resistance were established. This enabled a determination of suitable mixture compositions for protective layers for concrete bridge decks.

Influence of Overheating Phenomenon on Bitumen and Asphalt Mixture Properties.

In the course of manufacturing, transport and installation, road bitumens and asphalt mixtures can be exposed to the impact of elevated process temperatures exceeding 240 °C. This mainly applies to the mixtures used for road pavements and bridge deck insulation during adverse weather conditions. The heating process should not change the basic and rheological properties of binders and the asphalt mixtures that to a degree cause the degradation of asphalt pavement durability. The work involved analyzing the properties of non-modified bitumens and SBS polymer modified bitumens, heated at temperatures of 200 °C, 250 °C and 300 °C for 1 h. Next, the asphalt mixtures were heated in the same temperatures. Based on the developed Overheating Degradation Index (ODI) it was demonstrated that polymer-modified bitumens were characterized by higher overheating sensitivity A(ODI) than non-modified bitumens, which was confirmed by mixture test results. Overheating limit temperatures T(ODI) were determined, which in the case of polymer-modified bitumens are up to 20 °C lower than for non-modified bitumens. When the temperature increases above T(ODI), loss of viscoelastic properties occurs in the material which causes, among other effects, a loss of resistance to fatigue cracking.