Experimental Study on Mechanical Properties of Different Resins Used in Oral Environments.

Background and Objectives: Acrylic resins remain the materials of choice for removable prosthesis due to their indisputable qualities. The continuous evolution in the field of dental materials offers practitioners today a multitude of therapeutic options. With the development of digital technologies, including both subtractive and additive methods, workflow has been considerably reduced and the precision of prosthetic devices has increased. The superiority of prostheses made by digital methods compared to conventional prostheses is much debated in the literature. Our study's objective was to compare the mechanical and surface properties of three types of resins used in conventional, subtractive, and additive technologies and to determine the optimal material and the most appropriate technology to obtain removable dentures with the highest mechanical longevity over time. Materials and Methods: For the mechanical tests, 90 samples were fabricated using the conventional method (heat curing), CAD/CAM milling, and 3D printing technology. The samples were analyzed for hardness, roughness, and tensile tests, and the data were statistically compared using Stata 16.1 software (StataCorp, College Station, TX, USA). A finite element method was used to show the behavior of the experimental samples in terms of the crack shape and its direction of propagation. For this assessment the materials had to be designed inside simulation software that has similar mechanical properties to those used for obtaining specimens for tensile tests. Results: The results of this study suggested that CAD/CAM milled samples showed superior surface characteristics and mechanical properties, comparable with conventional heat-cured resin samples. The propagation direction predicted by the finite element analysis (FEA) software was similar to that observed in a real-life specimen subjected to a tensile test. Conclusions: Removable dentures made from heat-cured resins remain a clinically acceptable option due to their surface quality, mechanical properties, and affordability. Three-dimensional printing technology can be successfully used as a provisional or emergency therapeutic solution. CAD/CAM milled resins exhibit the best mechanical properties with great surface finishes compared to the other two processing methods.

An Interdisciplinary Study Regarding the Characteristics of Dental Resins Used for Temporary Bridges.

Background and Objectives: The surface condition of the materials that are used for temporary prostheses influences their microbial colonization, with a direct impact on the oral tissues. This study aims at a comparative analysis of three types of resins for temporary bridges using conventional and digital technologies. The attention was focused on the analysis of the surface characteristics and mechanical strength of these materials. Materials and Methods: The surface condition was assessed for three distinct materials both before and after polishing- heat-curing resin Superpont C + B (SpofaDental, Jicin, Czech Republic) used unconventional technology, Zotion dental milling polymethyl methacrylate (PMMA) block (Zotion, Chongqing, China) for provisional crowns/bridges used in digital subtractive technologies and Freeprint Temp (Detax GmbH & Co. KG, Ettlingen, Germany) resin for temporary crowns and bridges that are used in 3D printing technologies. The two-way ANOVA analysis indicated that polishing leads to a statistically significant increase in roughness coefficients for all the three resins that were tested (p < 0.001). While the highest roughness coefficients were displayed in the 3D cured sample, the largest decrease was reported by the milled sample Results: The results revealed that surface roughness was significantly influenced by both the type of resin that was used (p < 0.001) and the treatment that was induced by finishing and polishing (p < 0.001). Similar p-values were obtained for each of the three resins. Conclusions: The results demonstrated a significant optimization of the surfaces after finishing and polishing and statistically significant differences between the surface parameters and the mechanical properties of the samples. The low values of the roughness and the acceptable values of the mechanical resistance for the conventional samples indicate these materials for the long-term temporary bridge's realization, allowing the correct restoration of the functions and the rehabilitation at the oral level.