RESUMO
Field emission cathodes, comprised of commercially available carbon fiber fabrics directly brazed to metal substrates, were fabricated and tested. Cathodes fabricated in this manner eliminate the need for an epoxy bond between the carbon fibers and the substrates and can be baked, in a vacuum, at high temperatures, limited by the re-melt temperature of the braze. Preliminary testing at mildly relativistic voltages (200 kV-300 kV) yielded average current emission densities of 100's of A/cm2, which are in line with previously published results on epoxy-bonded carbon fiber field emission cathodes.
RESUMO
With its low work function and high mechanical strength, the LaB6/VB2 eutectic system is an interesting candidate for high performance thermionic emitters. For the development of device applications, it is important to understand the origin, value, and spatial distribution of the work function in this system. Here we combine thermal emission electron microscopy and low energy electron microscopy with Auger electron spectroscopy and physical vapor deposition of the constituent elements to explore physical and chemical conditions governing the work function of these surfaces. Our results include the observation that work function is lower (and emission intensity is higher) on VB2 inclusions than on the LaB6 matrix. We also observe that the deposition of atomic monolayer doses of vanadium results in surprisingly significant lowering of the work function with values as low as 1.1eV.