Impact of degeneration and material pairings on cartilage friction: Cartilage versus glass.

The association of knee joint osteoarthritis and altered frictional properties of the degenerated cartilage remains ambiguous, because previous in vitro studies did not consider the characteristic loads and velocities during gait. Therefore, the aim of this study was to quantify the friction behavior of degenerated human cartilage under characteristic stance and swing phase conditions. A dynamic pin-on-plate tribometer was used to test the tribological systems of cartilage against cartilage and cartilage against glass, both with synthetic synovial fluid as lubricant. Using the International Cartilage Repair Society classification, the cartilage samples were assigned to a mildly or a severely degenerated group before testing. Friction coefficients were calculated under stance and swing phase conditions at the beginning of the test and after 600 s of testing. The most important finding of this study is that cartilage against glass couplings displayed significantly higher friction for the severely degenerated samples compared to the mildly degenerated ones, whereas cartilage against cartilage couplings only indicated slight tendencies under the observed test conditions. Consequently, care should be taken when transferring in vitro findings from cartilage against cartilage couplings to predict the friction behavior in vivo. Therefore, we recommend in vitro tribological testing methods which account for gait-like loading conditions and to replicate physiological material pairings, particularly in preclinical medical device validation studies.

Impact of hyaluronic acid injection on the knee joint friction.

PURPOSE: The purpose of this in vitro study was to investigate whether or not hyaluronic acid supplementation improves knee joint friction during osteoarthritis progression under gait-like loading conditions. METHODS: Twelve human cadaveric knee joints were equally divided into mild and moderate osteoarthritic groups. After initial conservative preparation, a passive pendulum setup was used to test the whole joints under gait-like conditions before and after hyaluronic acid supplementation. The friction-related damping properties given by the coefficient of friction µ and the damping coefficient c (in kg m2/s) were calculated from the decaying flexion-extension motion of the knee. Subsequently, tibial and femoral cartilage and meniscus samples were extracted from the joints and tested in an established dynamic pin-on-plate tribometer using synthetic synovial fluid followed by synthetic synovial fluid supplemented with hyaluronic acid as lubricant. Friction was quantified by calculating the coefficient of friction. RESULTS: In the pendulum tests, the moderate OA group indicated significantly lower c0 values (p < 0.05) under stance phase conditions and significantly lower µ0 (p = 0.01) values under swing phase conditions. No degeneration-related statistical differences were found for µend or cend. Friction was not significantly different (p > 0.05) with regard to mild and moderate osteoarthritis in the pin-on-plate tests. Additionally, hyaluronic acid did not affect friction in both, the pendulum (p > 0.05) and pin-on-plate friction tests (p > 0.05). CONCLUSION: The results of this in vitro study suggested that the friction of cadaveric knee joint tissues does not increase with progressing degeneration. Moreover, hyaluronic acid viscosupplementation does not lead to an initial decrease in knee joint friction.