Impact of post printing cleaning methods on geometry, transmission, roughness parameters, and flexural strength of 3D-printed zirconia.

OBJECTIVE: To analyze the impact of different post printing cleaning methods on geometry, transmission, roughness parameters, and flexural strength of additively manufactured zirconia. METHODS: Disc-shaped specimens (N = 100) were 3D-printed from 3 mol%-yttria-stabilized zirconia (material: LithaCon 3Y 210; printer: CeraFab 7500, Lithoz) and were cleaned with five different methods (n = 20): (A) 25 s of airbrushing with the dedicated cleaning solution (LithaSol 30®, Lithoz) and 1-week storage in a drying oven (40 °C); (B) 25 s airbrushing (LithaSol 30®) without drying oven; (C) 30 s ultrasonic bath (US) filled with Lithasol30®; (D) 300 s US filled with LithaSol 30®; (E) 30 s US filled with LithaSol 30® followed by 40 s of airbrushing (LithaSol 30®). After cleaning, the samples were sintered. Geometry, transmission, roughness (Ra, Rz), characteristic strengths (σ0), and Weibull moduli (m) were analyzed. Statistical analyses were performed using Kolmogorov-Smirnov-, t-, Kruskal-Wallis-, and Mann-Whitney-U-tests (α < 0.05). RESULTS: Short US (C) resulted in the thickest and widest samples. Highest transmission was found for US combined with airbrushing (E, p ≤ 0.004), followed by D and B (same range, p = 0.070). Roughness was lowest for US combined with airbrushing (E, p ≤ 0.039), followed by A and B (same range, p = 0.172). A (σ0 = 1030 MPa, m = 8.2), B (σ0 = 1165 MPa, m = 9.8), and E (σ0 = 1146 MPa, m = 8.3) were significantly stronger (p < 0.001) and substantially more reliable than C (σ0 = 480 MPa, m = 1.9) and D (σ0 = 486 MPa, m = 2.1). SIGNIFICANCE: For 3D-printed zirconia, cleaning strategy selection is important. Airbrushing (B) and short US combined with airbrushing (E) were most favorable regarding transmission, roughness, and strength. Ultrasonic cleaning alone was ineffective (short duration) or detrimental (long duration). Strategy E could be particularly promising for hollow or porous structures.

MSVAT-SPACE-STIR and SEMAC-STIR for Reduction of Metallic Artifacts in 3T Head and Neck MRI.

BACKGROUND AND PURPOSE: The incidence of metallic dental restorations and implants is increasing, and head and neck MR imaging is becoming challenging regarding artifacts. Our aim was to evaluate whether multiple-slab acquisition with view angle tilting gradient based on a sampling perfection with application-optimized contrasts by using different flip angle evolution (MSVAT-SPACE)-STIR and slice-encoding for metal artifact correction (SEMAC)-STIR are beneficial regarding artifact suppression compared with the SPACE-STIR and TSE-STIR in vitro and in vivo. MATERIALS AND METHODS: At 3T, 3D artifacts of 2 dental implants, supporting different single crowns, were evaluated. Image quality was evaluated quantitatively (normalized signal-to-noise ratio) and qualitatively (2 reads by 2 blinded radiologists). Feasibility was tested in vivo in 5 volunteers and 5 patients, respectively. RESULTS: Maximum achievable resolution and the normalized signal-to-noise ratio of MSVAT-SPACE-STIR were higher compared with SEMAC-STIR. Performance in terms of artifact correction was dependent on the material composition. For highly paramagnetic materials, SEMAC-STIR was superior to MSVAT-SPACE-STIR (27.8% smaller artifact volume) and TSE-STIR (93.2% less slice distortion). However, MSVAT-SPACE-STIR reduced the artifact size compared with SPACE-STIR by 71.5%. For low-paramagnetic materials, MSVAT-SPACE-STIR performed as well as SEMAC-STIR. Furthermore, MSVAT-SPACE-STIR decreased artifact volume by 69.5% compared with SPACE-STIR. The image quality of all sequences did not differ systematically. In vivo results were comparable with in vitro results. CONCLUSIONS: Regarding susceptibility artifacts and acquisition time, MSVAT-SPACE-STIR might be advantageous over SPACE-STIR for high-resolution and isotropic head and neck imaging. Only for materials with high-susceptibility differences to soft tissue, the use of SEMAC-STIR might be beneficial. Within limited acquisition times, SEMAC-STIR cannot exploit its full advantage over TSE-STIR regarding artifact suppression.

Single mandibular implant study - denture satisfaction in the elderly.

To investigate whether there are differences in patients' denture satisfaction when an implant placed in the midline of the edentulous mandible is loaded either immediately or three months later, after second-stage surgery. One hundred and fifty-eight edentulous patients received a single implant in the midline of the mandible. After randomisation, it was loaded either immediately after implant placement (N = 81, group A) or three months later, after a submerged healing phase and a second-stage surgery (N = 77, group B). Patients' denture satisfaction aspects were assessed, using visual analogue scales (VAS), before treatment, one month after implant placement during the submerged healing phase (only group B) and one and four months after implant loading. The statistical analysis was performed using the Wilcoxon signed-rank and rank-sum tests. One month after loading, a significant improvement in comfort, function and stability of the mandibular denture could be observed in both groups (P ≤ 0·05). A slight but not significant improvement was found between one and four months after loading. Patients with second-stage surgery and delayed loading rated the stability and fit of the mandibular denture as significantly better than patients who had immediate loading. A single implant in the edentulous mandible significantly increased patients' denture satisfaction. After four months, stability and fit of the mandibular denture were considered better when a delayed loading protocol had been followed. A single mandibular implant in the edentulous mandible significantly increases patients' denture satisfaction, regardless of the loading protocol.

Clinical assessment of enamel wear caused by monolithic zirconia crowns.

The purpose of this study was to measure enamel wear caused by antagonistic monolithic zirconia crowns and to compare this with enamel wear caused by contralateral natural antagonists. Twenty monolithic zirconia full molar crowns were placed in 20 patients. Patients with high activity of the masseter muscle at night (bruxism) were excluded. For analysis of wear, vinylpolysiloxane impressions were prepared after crown incorporation and at 6-, 12-, and 24-month follow-up. Wear of the occlusal contact areas of the crowns, of their natural antagonists, and of two contralateral natural antagonists (control teeth) was measured by use of plaster replicas and a 3D laser-scanning device. Differences of wear between the zirconia crown antagonists and the control teeth were investigated by means of two-sided paired Student's t-tests and linear regression analysis. After 2 years, mean vertical loss was 46 µm for enamel opposed to zirconia, 19-26 µm for contralateral control teeth and 14 µm for zirconia crowns. Maximum vertical loss was 151 µm for enamel opposed to zirconia, 75-115 µm for control teeth and 60 µm for zirconia crowns. Statistical analysis revealed significant differences between wear of enamel by zirconia-opposed teeth and by control teeth. Gender, which significantly affected wear, was identified as a possible confounder. Monolithic zirconia crowns generated more wear of opposed enamel than did natural teeth. Because of the greater wear caused by other dental ceramics, the use of monolithic zirconia crowns may be justified.

In vitro investigation on extensively destroyed vital teeth: is fracture force a limiting factor for direct restoration?

To evaluate the in vitro fracture load of extensively damaged vital teeth after either direct or indirect restauration, severe tooth substance loss was simulated for 96 molars. Subsequently, two cavities were prepared with little (design 1) or more substantial (design 2) residual tooth support. All molars were provided with a 2-mm ferrule design and then divided into 12 test groups based on their occlusal surface size. They were restored with composite or with either of two types of single crown (cast metal or milled zirconia). After thermal ageing (10,000 cycles at 6.5 and 60 °C), 1.2 million cycles of chewing simulation were applied (64 N). Maximum fracture load was determined with a loading angle of 45°. Statistical analysis was performed by use of Kaplan-Meier modelling, Student's t-tests, one-way anova, post hoc Tukey's HSD tests and linear regression analysis. Regarding mean fracture load without ageing, the indirect restorations outperformed composite (design 1: direct: 508 ± 123 N, indirect: 741 ± 248 N; design 2: direct: 554 ± 167 N, indirect: 903 ± 221 N). After artificial ageing, however, these differences were no longer significant (design 1: direct: 328 ± 189 N, indirect: 506 ± 352 N; design 2: direct 399 ± 208 N, indirect 577 ± 292 N). Instead, the fracture load of the aged composite restorations was comparable with that for zirconia (design 1) and cast metal (design 2) crowns. Fracture loads of direct composite restorations after artificial ageing might fulfil clinical requirements.