Hydrophobized MFC as Reinforcing Additive in Industrial Silica/SBR Tire Tread Compound.

Silica is used as reinforcing filler in the tire industry. Owing to the intensive process of silica production and its high density, substitution with lightweight bio-based micro fibrillated cellulose (MFC) is expected to provide lightweight, sustainable, and highly reinforced tire composite. MFC was modified with oleoyl chloride, and the degree of substitution (DS) was maintained between 0.2 and 0.9. Subsequently, the morphology and crystallinity of the modified MFC were studied and found to be significantly dependent on the DS. The advantages associated with the use of the modified MFC in synergy with silica for the reinforcement of styrene butadiene rubber (SBR) nanocomposite was investigated in comparison with silica/SBR compound. The structural changes occasioned by the DS values influenced the processability, curing kinetics, modulus-rolling resistance tradeoff, and tensile properties of the resultant rubber compounds. We found that the compound made with modified MFC at a DS of 0.67 (MFC16) resulted to the highest reinforcement, with a 350% increase in storage modulus, 180% increase in Young`s modulus, and 15% increase in tensile strength compared to the referenced silica-filled compounds. Our studies show that MFC in combination with silica can be used to reinforce SBR compound for tire tread applications.

Controlling mesopore size and processability of transparent enzyme-loaded silica films for biosensing applications.

Silica-based nanoporous thin films including large mesopores are relevant as enzyme supports for applications in biosensing. The diffusion and immobilization of large biomolecules such as enzymes in such porous films require the presence of large mesopores. Creating such morphologies based on a bottom-up synthesis using colloidal templates is a challenge in view of the combination of desired material properties and the robustness of the casting process for the fabrication of thin films. Here a strategy to reproducibly synthesize transparent porous silica thin films with submicrometer thickness and homogeneously distributed porosity is presented. For this purpose, polystyrene-poly-2-vinylpyridine (PS-P2VP) amphiphilic block copolymers are used as porogenic templates. Low-chain alcohols are employed as both selective solvents for the P2VP blocks and reaction media for silica synthesis. Rheology measurements reveal a strong influence of the block copolymer length on the behavior of PS-P2VP micelles in suspension. The pore distribution and accessibility into the film are controlled by adjusting the silica to block copolymer weight ratio. The solvent choice is shown to control not only the micelle size and the generated pore morphology but also the structural homogeneity of the films. Finally, the suitability of the synthesized films as supports for enzymes is tested using a model enzyme, horseradish peroxidase EC 1.11.1.7. Our approach is innovative, robust, and reproducible and provides a convenient alternative to synthesize large mesopores up to small macropores (20-100 nm) in nanostructured thin films with applications in biosensing and functional coatings.

Self-patterned nanoparticle layers for vertical interconnects: application in tandem solar cells.

We demonstrate self-patterned insulating nanoparticle layers to define local electrical interconnects in thin-film electronic devices. We show this with thin-film silicon tandem solar cells, where we introduce between the two component cells a solution-processed SiO2 nanoparticle layer with local openings to allow for charge transport. Because of its low refractive index, high transparency, and smooth surface, the SiO2 nanoparticle layer acts as an excellent intermediate reflector allowing for efficient light management.