Evaluation and comparison of surface characteristics of commercially available TMA wires using scanning electron microscopy and optical profilometer.

AIM: The aim of this study was to evaluate and compare the surface characteristics of colored titanium molybdenum alloy archwires (purple-coated TMA and honey dew-coated TMA) and the regular titanium molybdenum alloy archwires. MATERIALS AND METHODS: The experiment comprised three groups, Group I - regular TMA archwires, Group II - purple-coated TMA archwires, Group III - honey dew-coated TMA wires involving 21 samples each. The surface characteristics were assessed using scanning electron microscopy and optical profilometer. RESULTS: The results were statistically analyzed using analysis of variance wherein Group I regular TMA wires exhibited a root mean square value of 148.071 nm and a standard deviation of 9.0027 nm followed by group II (purple-coated TMA wires) which showed a root mean square value of 84.095 nm with a standard deviation of 2.6005 nm, while group III (honey dew-coated TMA wires) was found to have a root mean square value of 71.681 nm with a standard deviation of 1.4645 nm on subjecting to optical profilometry. CONCLUSION: The surface roughness is higher for regular TMA wire exhibiting superior characteristic of color-coated TMA wires, especially honey dew-coated TMA wires over the regular and purple-coated TMA wires. This property of the archwires details regarding its application in both sliding and frictionless mechanics in retraction phase of fixed orthodontic treatment.

Evaluation of nickel ion release from various orthodontic arch wires: An in vitro study.

AIM: The high incidence of nickel (Ni) allergy and the increasing use of Ni-containing dental biomaterials have been of growing concern. The purpose of this investigation was to analyze and evaluate the rate of Ni ion release from different types arch wires used in orthodontics. MATERIALS AND METHODS: Four groups of arch wires (nickel titanium [NiTi], SS, Cu NiTi and ion implanted NiTi) with twelve samples were stored in artificial saliva with a pH 5.6-7.0 thermostated at (36.5°C) and tested at different intervals i.e., 7(th) day, 14(th) day, and 21(st) day. The amount of Ni and Ti ions released from the sample were evaluated using an atomic adsorption spectrophotometer. The solution was replaced with a fresh bottle to avoid sediments. RESULTS: Statistical analysis was performed by nonparametric tests (Student's paired t-test, one-way analysis of variance and multiple comparison test by Tukey "Honestly significant difference"). The statistical package SPSS PC plus (version 4.0.1) was used for data processing and statistical analysis. Results showed significantly statistical influence on the release amount of Ni and Ti ions. Large variation in concentration of Ni released from brackets and bands combined. However, the amount of Ni ions released in all test solutions diminished with time and was below the critical value necessary to induce allergy and below daily dietary intake level. CONCLUSIONS: The daily release of NiTi, SS, Cu NiTi and ion implanted NiTi by an orthodontic appliance in acid pH, particularly favorable to corrosion, was well below that ingested with a normal daily diet. It is therefore concluded that the quantities of metal ions released in our experimental conditions should not be cause for concern in utilizing the appliance.