The Comparison of Efficacy and Safety between Radiofrequency Ablation Alone and Ethanol Ablation Followed by Radiofrequency Ablation in the Treatment of Mixed Cystic and Solid Thyroid Nodule.

Purpose: To compare the efficacy and safety of radiofrequency ablation (RFA) and ethanol ablation (EA) followed by RFA in treating mixed cystic and solid thyroid nodules. Materials and Methods: We included 243 nodules from 243 patients who underwent RFA for mixed cystic and solid benign nodules. The nodules were divided into two groups (RFA alone and EA + RFA). We evaluated volume reduction rate (VRR), therapeutic success rate, improvement in symptomatic and cosmetic issues, complications, and adverse effects. Results: The RFA group included 204 patients, and the EA + RFA group included 39 patients. The long-term success rates in the RFA only and EA + RFA groups were 90.2% and 97.4%, respectively. The mean VRR at the last follow-up in the RFA and EA + RFA groups were 81.6% and 87.2%, respectively. Therapeutic results were similar in both groups at the last follow-up. Cosmetic and symptomatic problems markedly improved in both groups. No major complications were observed. Conclusion: Both RFA alone and EA + RA are safe and effective methods for treating mixed cystic and solid thyroid nodules, although EA + RFA is slightly more effective.

Effective Interaction between Homo- and Heteropolymer Block of Poly(n-butyl acrylate)-b-poly(methyl methacrylate-r-styrene) Diblock Copolymers.

We investigated the segregation behavior of a molten diblock copolymer, poly(n-butyl acrylate)-b-poly(methyl methacrylate-r-styrene) (PBA-b-P(MMA-r-S)), wherein styrene (S) is incorporated as a comonomer in the second block to modulate the effective interaction between homopolymer and a random copolymer block. The temperature dependence of the effective interaction parameter χeff between n-butyl acrylate (BA) and the average monomer of the MMA-r-S random block was evaluated from small-angle X-ray scattering (SAXS) analysis using the random phase approximation (RPA) approach. The calculated χeff, as a function of the styrene fraction in the random copolymer block, shows a good agreement with the mean-field binary interaction model. This consistency indicates that the effective interaction between component BA and the average monomer of the random copolymer block is smaller than the interactions between pure components (χBA,MMA,χBA,S). The present study suggests that the introduction of a random copolymer block to a block copolymer can effectively reduce the degree of incompatibility of the block copolymer system without altering the constituent species, which may serve as a viable methodology in designing novel thermoplastic elastomers based on triblock or multiblock copolymers.

Small-Angle X-ray Scattering Analysis on the Estimation of Interaction Parameter of Poly(n-butyl acrylate)-b-poly(methyl methacrylate).

The temperature dependence of the Flory-Huggins interaction parameter χ for poly(n-butyl acrylate)-b-poly(methyl methacrylate) (PBA-b-PMMA) was quantified from small-angle X-ray scattering (SAXS) analysis using random phase approximation (RPA) theory. It was found from the χ estimation (χ=0.0103+14.76/T) that the enthalpic contribution, χH, a measure for temperature susceptibility of χ, is 1.7-4.5 folds smaller for PBA-b-PMMA than for the conventional styrene-diene-based block copolymers, which have been widely used for thermoplastic elastomers. This finding suggests that these fully acrylic components can be a desirable chemical pair for constituting terpolymers applied for thermally stable and mechanically resilient elastomers.