Investigation of Thermal Properties of Zr-Based Metallic Glass-Polymer Composite with the Addition of Silane.

Composites based on Zr65Cu17.5Ni10Al7.5/PTFE (polytetrafluoroethylene) with silane were prepared by ball milling with subsequent thermal pressing. Silanization was performed in the alcoholic solution with metallic glass powder. Different composites, 30/70 and 50/50 with silane, were prepared. During ball milling, Zr2Cu and Zr2Ni intermetallic phases were formed. The Zr-based metallic glass had a large supercooled region, and the melting point of the 30/70 and 50/50 composites with silane was near to the melting point of PTFE. The 50/50 composite (silane) had the highest thermal conductivity compared to the 30/70 composite samples. The incorporation of silane in metallic glass/polymer was investigated by Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscope (SEM) analysis. Thermogravimetric analysis (TGA) showed the thermal stability of the composite samples up to 450-460 °C. It was also concluded that the 50/50 composite with silane has better thermal stability than the 30/70 composite with silane. The addition of silane in 30/70 and 50/50 composites increased the thermal conductivity compared to the composites without silane.

Non-electrolytic synthesis of copper oxide/carbon nanocomposite by surface plasma in super-dehydrated ethanol.

Electrolytic processes are widely used to synthesize different nanomaterials and it does not depend on what kind of the method has been applied (wet-chemistry, sonochemistry, plasma chemistry, electrolysis and so on). Generally, the reactions in the electrolyte are considered to be reduction/oxidation (REDOX) reactions between chemical reagents or the deposition of matter on the electrodes, in line with Faraday's law. Due to the presence of electroconductive additives in any electrolyte, the polarization effect of polar molecules conducting an electrical current disappears, when external high-strength electric field is induced. Because initially of the charge transfer always belongs of electroconductive additive and it does not depend on applied voltage. The polarization of ethanol molecules has been applied to conduct an electric current by surface plasma interaction for the synthesis of a copper oxide/carbon nanocomposite material.

X-ray emission spectra of graphene nanosheets.

Investigations of the electronic structure of graphene nanosheets synthesized by the reduction of oxidized graphene nanosheets were carried out using ultra-soft X-ray emission spectroscopy (USXES). Oxidized graphene nanosheets were produced from carbon nanofiber starting material using a modified Hummers method. X-ray diffraction, and scanning and transmission electron microscopy investigations were used in addition to USXES to study the electronic structure evolution from carbon nanofibers to graphene nanosheets. The effect of the degree of corrugation of the graphene nanosheets on the fine structure of the CK(alpha)-emission bands was revealed by USXES. It was found that corrugation of the graphene nanosheets is caused by overlapping of the pi-orbitals and formation of mixed (sigma + pi)-states.

Synthesis of amorphous carbon nanoparticles and carbon encapsulated metal nanoparticles in liquid benzene by an electric plasma discharge in ultrasonic cavitation field.

A newly-developed method permits an electric plasma discharge to occur with relatively low electric power in insulating organic solutions due to the presence of an ultrasonic cavitation. A stable electric plasma could be generated in an ultrasonic cavitation field containing a thousand tiny activated bubbles, in which the electric conductivity could be improved due to formed radicals and free electrons, using copper electrodes and a titanium ultrasonic horn. This method allowed us to synthesize pyrolytic amorphous carbon nanoparticles smaller than about 30 nm in diameter from benzene liquid. In addition, we synthesized TiC nanoparticles about 50-150 nm in size, and copper nanoparticles smaller than 10 nm, which were encapsulated in multilayered graphite cages. Finally, we used GC-MS and MALDI-TOF-MS to observe and analyze the polymerized compounds and the degree of polymerization of the benzene liquid after the plasma treatment.