Negligible expression of arsenic in some commercially available brands of Portland cement and mineral trioxide aggregate.

INTRODUCTION: This study was designed aiming to determine and compare the amount of arsenic in some brands of mineral trioxide aggregate (MTA) and Portland cement. METHODS: In the present study, arsenic species (As[III], As[V], and dimethylarsinic acid) were separated by high-performance liquid chromatography (HPLC) using a strong anion exchange column and converted into arsines by online HG. The instrumental coupling, HPLC-HG-AFS, was applied to 0.2 g of each cement that was prior digested in a solution of HCl, HNO(3), and HBF(4). Data were expressed as a part per million, and the preliminary analysis of the raw pooled data revealed a bell-shaped distribution. Statistical analysis was performed using one-way analysis of variance for multiple comparisons. RESULTS: In all chromatograms obtained, only type III arsenic could be detected. The minimum amount of arsenic was detected in samples of white MTA ProRoot (3.3 x 10-4) and the maximum in the samples MTA Bio Angelus (Angelus, Londrina, PR, Brazil) (8.6 x 10-4). In the Gray MTA (Angelus), gray ProRoot MTA (Tulsa/Dentsply, Tulsa, OK) and CP Juntalider (Brasilatex Ltda, Diadema, SP, Brazil) did not detect any trace of arsenic. The values of arsenic found in CP Irajazinho (Votorantim Cimentos, Rio Branco, SP, Brazil) and white MTA Angelus were intermediaries to minimum and maximum values. The nonparametric test Kruskal-Wallis showed statistically similar results among all cements tested (p > 0.5). CONCLUSIONS: Overall, the present study showed that all cements showed insignificant amounts of type III arsenic as well as no trace of arsenic DMA and type V could be detected.

Endodontia mecanizada Parte I - Flexão rotativa / Mechanized Endodonty. Part I - rotating flexure

Este trabalho tem como objetivo avaliar a influência da conicidadede instrumentos de níquel-titânio acionados a motor na resistência à fraturapor flexão rotativa, analisando ainda, por meio de microscopia eletrônica devarredura, a superfície de fratura dos instrumentos, bem como a configuraçãodas hélices das hastes de corte helicoidais dos instrumentos no ponto de fratura.Foram utilizados 30 instrumentos fabricados em níquel-titânio acionados a motorda marca K3? (Sybron Dental Specialties-Kerr, México), valores nominaisde 25mm de comprimento e 0,25mm de diâmetro em D01, nas conicidades de0,02 ? 0,04 e 0,06mm/mm. Dez instrumentos endodônticos de cada conicidadeforam avaliados por meio do ensaio destrutivo de flexão rotativa. Diante dasmetodologias empregadas, dos resultados obtidos e após a execução dos testesestatísticos: análise de variância no nível de significância de 5%, e do teste decomparações múltiplas de Student-Newman-Keuls a 5%, conclui que o númerode ciclos para a fratura em flexão rotativa diminui com o aumento da conicidadedos instrumentos endodônticos ensaiados. Quanto à análise por meiodo microscópio eletrônico de varredura, independentemente da conicidade doinstrumento endodôntico, as amostras fraturadas apresentaram superfície defratura com característica dúctil, não ocorrendo deformação plástica visível dosinstrumentos fraturados.