RESUMO
Adsorption is a commonly used method for industrial wastewater treatment because of its low-cost, easy operation and high efficiency. In this work, chitosan was crosslinked and functionalized with a low-cost phosphonium salt, tetrakis(hydroxymethyl)phosphonium sulfate (THPS), to enhance its adsorption capacity for Cr(VI). The novel phosphonium-crosslinked chitosan (PCC) was characterized using elemental analysis, XRF, FTIR, NMR and SEM-EDX. At pH 6, PCC had a higher Langmuir equilibrium constant than the unmodified chitosan (0.19 ± 0.02 L mg-1 versus 0.0044 ± 0.0005 L mg-1) and PCC demonstrated higher adsorption capacity than chitosan at equilibrium Cr(VI) concentrations below 120 mg L-1. Additionally, magnesium sulfate or magnesium chloride was shown to desorb Cr(VI) and recycle PCC. When treated with THPS, chitosan is activated for Cr(VI) adsorption at pH 6; therefore, PCC can be used in wastewater treatment over a wider pH range than chitosan.
RESUMO
The impact of biochar properties on acid-extractable organics (AEO) adsorption from oil sands process-affected water (OSPW) was studied. Biochar from wheat straw with the highest ash content (14%) had the highest adsorption capacity (0.59 mg/g) followed by biochar from pulp mill sludge, switchgrass, mountain pine, hemp shives, and aspen wood. The adsorption capacity had no obvious trend with surface area, total pore volume, bulk polarity and aromaticity. The large impact of metal content was consistent with the carboxylates (i.e., naphthenate species) in the OSPW binding to the metals (mainly Al and Fe) on the carbon substrate. Although the capacity of biochar is still approximately two orders of magnitude lower than that of a commercial activated carbon, confirming the property (i.e., metal content) that most influenced AEO adsorption, may allow biochar to become competitive with activated carbon after normalizing for cost, especially if this cost includes environmental impacts.