Ionomers Based on Addition and Ring Opening Metathesis Polymerized 5-phenyl-2-norbornene as a Membrane Material for Ionic Actuators.

Two types of poly(5-phenyl-2-norbornene) were synthesized via ring opening metathesis and addition polymerization. The polymers sulfonation reaction under homogeneous conditions resulted in ionomer with high sulfonation degree up to 79% (IEC 3.36 meq/g). The prepared ionomer was characterized by DSC, GPC, 1H NMR and FT-IR. Polymers for electromechanical applications soluble in common polar organic solvents were obtained by replacing proton of sulfonic group with imidazolium and 1-methylimidazlium. Membranes were prepared using the above-mentioned polymers and 1-ethyl-3-methylimidazolium tetrafluoroborate (EMImBF4), as well as mixtures with polyvinylidene fluoride (PVDF). Mechanical, morphological, and conductive properties of the membranes were examined by tensile testing, SEM, and impedance spectroscopy, respectively. Dry and air-stable actuators with electrodes based on SWCNT were fabricated via hot-pressing. Actuators with membranes based on methylimidazolium containing ionomers outperformed classical bucky gel actuator and demonstrated high strain (up to 1.14%) and generated stress (up to 1.21 MPa) under low voltage of 2 V.

Data on synthesis and characterization of sulfonated poly(phenylnorbornene) and polymer electrolyte membranes based on it.

This article describes data on preparation of sulfonated hydrogenated poly(phenylnorbornene) with different cations synthesized via sequential ring-opening metathesis polymerization, reduction, homogeneous sulfonation and cation exchange reactions. The data of the characterization of new polymers by nuclear magnetic resonance (1H NMR) spectroscopy, Fourier-transform infrared (FT-IR) spectroscopy and differential scanning calorimetry (DSC) are presented. The effect of imidazolium and 1-methylimidazolium cations, ionic liquid and Zwitter-type ion liquid on ionic conductivities evaluated by impedance spectroscopy. Preparation procedure of polymer electrolyte membrane based on new polymers and Nafion as a blend with polyvinylidene fluoride (PVDF) is given. Scanning electron microscopy images and ionic conductivities of these membrane are presented.