Study of impacts of brickkiln emanations on soil quality of agriculture lands in selected areas of District Bhimber, Azad Jammu and Kashmir, Pakistan.

The pollution is hot issue of current era in world and the current study was carried to explore impacts of brickkilns' emanations on physiochemical properties of agricultural lands from District Bhimber of Azad Jammu and Kashmir (AJK) Pakistan. In this research, various edaphic characteristics: pH, soil organic matter, organic carbon, water holding capacity, cation exchange capacity and heavy metal contamination in soils nearby of brickkilns were determined. The pH of soil ranged from 5.55 to 7.50, soil organic matter was 0.35-0.90% and organic carbon content was 0.65-1.40%. The water holding capacity ranged from 2.10 to 3.20 mgL-1 and carbon exchange capacity was 1250 to 4202 meq/100g. The contamination profile of heavy metal depicted that Pb showed highest conc. 0.065 mg/g followed by Co (0.053 mg/g) and Ni with 0.52 mg/g in the soil. Pb and Cr had high conc. in soil samples around brickkilns due to burning of coal and rubber tyres as fuel. The conc. of sulphate and nitrate ranged from 0.90±0.50 mol L-1 to 4.25±0.65 mol L-1 and 2.30±0.50 mol L-1 to 6.55±0.25 mol L-1, respectively. The fertility of agriculture lands was depicted that edaphic properties were directly related while nutritive features were inversely commensurate to distance from brickkilns. The research proved that emanations of brickkilns causes severe impact on quality of agriculture land, plant growth and its yield. Hence, reclamation measures should be taken to mitigate and/or eradicate nuisance of brickkilns emanations by using environmental friendly strategies.

Dielectric Barrier Discharge (DBD) Plasma Coating of Sulfur for Mitigation of Capacity Fade in Lithium-Sulfur Batteries.

Sulfur particles with a conductive polymer coating of poly(3,4-ethylene dioxythiophene) "PEDOT" were prepared by dielectric barrier discharge (DBD) plasma technology under atmospheric conditions (low temperature, ambient pressure). We report a solvent-free, low-cost, low-energy-consumption, safe, and low-risk process to make the material development and production compatible for sustainable technologies. Different coating protocols were developed to produce PEDOT-coated sulfur powders with electrical conductivity in the range of 10-8-10-5 S/cm. The raw sulfur powder (used as the reference) and (low-, optimum-, high-) PEDOT-coated sulfur powders were used to assemble lithium-sulfur (Li-S) cells with a high sulfur loading of ∼4.5 mg/cm2. Long-term galvanostatic cycling at C/10 for 100 cycles showed that the capacity fade was mitigated by ∼30% for the cells containing the optimum-PEDOT-coated sulfur in comparison to the reference Li-S cells with raw sulfur. Rate capability, cyclic voltammetry, and electrochemical impedance analyzes confirmed the improved behavior of the PEDOT-coated sulfur as an active material for lithium-sulfur batteries. The Li-S cells containing optimum-PEDOT-coated sulfur showed the highest reproducibility of their electrochemical properties. A wide variety of bulk and surface characterization methods including conductivity analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and NMR spectroscopy were used to explain the chemical features and the superior behavior of Li-S cells using the optimum-PEDOT-coated sulfur material. Moreover, postmortem [SEM and Brunauer-Emmett-Teller (BET)] analyzes of uncoated and coated samples allowed us to exclude any significant effect at the electrode scale even after 70 cycles.