Uniform nucleation and epitaxy of bilayer molybdenum disulfide on sapphire.

Two-dimensional transition-metal dichalcogenides (TMDs) are of interest for beyond-silicon electronics1,2. It has been suggested that bilayer TMDs, which combine good electrostatic control, smaller bandgap and higher mobility than monolayers, could potentially provide improvements in the energy-delay product of transistors3-5. However, despite advances in the growth of monolayer TMDs6-14, the controlled epitaxial growth of multilayers remains a challenge15. Here we report the uniform nucleation (>99%) of bilayer molybdenum disulfide (MoS2) on c-plane sapphire. In particular, we engineer the atomic terrace height on c-plane sapphire to enable an edge-nucleation mechanism and the coalescence of MoS2 domains into continuous, centimetre-scale films. Fabricated field-effect transistor (FET) devices based on bilayer MoS2 channels show substantial improvements in mobility (up to 122.6 cm2 V-1 s-1) and variation compared with FETs based on monolayer films. Furthermore, short-channel FETs exhibit an on-state current of 1.27 mA µm-1, which exceeds the 2028 roadmap target for high-performance FETs16.

Three-dimensional monolithic micro-LED display driven by atomically thin transistor matrix.

Two-dimensional materials are promising candidates for future electronics due to unmatched device performance at atomic limit and low-temperature heterogeneous integration. To adopt these emerging materials in computing and optoelectronic systems, back end of line (BEOL) integration with mainstream technologies is needed. Here, we show the integration of large-area MoS2 thin-film transistors (TFTs) with nitride micro light-emitting diodes (LEDs) through a BEOL process and demonstrate high-resolution displays. The MoS2 transistors exhibit median mobility of 54 cm2 V-1s -1, 210 µA µm-1 drive current and excellent uniformity. The TFTs can drive micrometre-sized LEDs to 7.1 × 107 cd m-2 luminance under low voltage. Comprehensive analysis on driving capability, response time, power consumption and modulation scheme indicates that MoS2 TFTs are suitable for a range of display applications up to the high resolution and brightness limit. We further demonstrate prototypical 32 × 32 active-matrix displays at 1,270 pixels-per-inch resolution. Moreover, our process is fully monolithic, low-temperature, scalable and compatible with microelectronic processing.