Angle-resolved XPS analysis and characterization of monolayer and multilayer silane films for DNA coupling to silica.

We measure silane density and Sulfo-EMCS cross-linker coupling efficiency on aminosilane films by high-resolution X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) measurements. We then characterize DNA immobilization and hybridization on these films by (32)P-radiometry. We find that the silane film structure controls the efficiency of the subsequent steps toward DNA hybridization. A self-limited silane monolayer produced from 3-aminopropyldimethylethoxysilane (APDMES) provides a silane surface density of ~3 nm(-2). Thin (1 h deposition) and thick (19 h deposition) multilayer films are generated from 3-aminopropyltriethoxysilane (APTES), resulting in surfaces with increased roughness compared to the APDMES monolayer. Increased silane surface density is estimated for the 19 h APTES film, due to a ∼32% increase in surface area compared to the APDMES monolayer. High cross-linker coupling efficiencies are measured for all three silane films. DNA immobilization densities are similar for the APDMES monolayer and 1 h APTES. However, the DNA immobilization density is double for the 19 h APTES, suggesting that increased surface area allows for a higher probe attachment. The APDMES monolayer has the lowest DNA target density and hybridization efficiency. This is attributed to the steric hindrance as the random packing limit is approached for DNA double helices (dsDNA, diameter ≥ 2 nm) on a plane. The heterogeneity and roughness of the APTES films reduce this steric hindrance and allow for tighter packing of DNA double helices, resulting in higher hybridization densities and efficiencies. The low steric hindrance of the thin, one to two layer APTES film provides the highest hybridization efficiency of nearly 88%, with 0.21 dsDNA/nm(2). The XPS data also reveal water on the cross-linker-treated surface that is implicated in device aging.

High-resolution X-ray photoelectron spectroscopy of mixed silane monolayers for DNA attachment.

The amine density of 3-aminopropyldimethylethoxysilane (APDMES) films on silica is controlled to determine its effect on DNA probe density and subsequent DNA hybridization. The amine density is tailored by controlling the surface reaction time of (1) APDMES, or (2) n-propyldimethylchlorosilane (PDMCS, which is not amine terminated) and then reacting it with APDMES to form a mixed monolayer. High-resolution X-ray photoelectron spectroscopy (XPS) is used to quantify silane surface coverage of both pure and mixed monolayers on silica; the XPS data demonstrate control of amine density in both pure APDMES and PDMCS/APDMES mixed monolayers. A linear correlation between the atomic concentration of N atoms from the amine and Si atoms from the APDMES in pure APDMES films allows us to calculate the PDMCS/APDMES ratio in the mixed monolayers. Fluorescence from attached DNA probes and from hybridized DNA decreases as the percentage of APDMES in the mixed monolayer is decreased by dilution with PDMCS.