Influence of different curing modes on the bonding effectiveness of self-adhesive resin luting cements in combination with universal adhesives.

OBJECTIVES: This study aimed to investigate the immediate dentin bond performance and bond durability of self-adhesive resin luting cements (RLCs) in combination with universal adhesives in different curing modes. METHODS: Two self-adhesive RLCs were used with universal adhesives as primers. They were also used alone as self-adhesive RLCs. Two multiple-step RLC systems were used as comparison materials. To measure the shear bond strength (SBS) in different curing modes, 12 specimens were prepared for each group. Stainless-steel rods were bonded to bovine dentin, and the bonded specimens were assigned to the baseline group (stored for 24 h) and artificially aged group (thermal cycling [TC], 10,000 cycles). After each storage period, the SBS of the bonded specimens was measured. The Knoop hardness number (KHN) of the cured RLCs was measured with or without primer application in different curing modes at 24 h and after 10,000 TC. The representative RLC/dentin interfaces were observed using scanning electron microscopy (SEM). RESULTS: Dentin SBS was significantly influenced by the RLC system but not by the curing mode. Self-adhesive RLCs alone showed significantly lower SBS values than self-adhesive RLCs with primer regardless of the curing mode or storage period. The storage period, curing mode, and RLC system significantly influenced the KHN. SIGNIFICANCE: The use of universal adhesives as a primer may help enhance the immediate dentin bond performance and bond durability of self-adhesive RLCs.

Scanning electron microscopy observation of dentin bond interfaces in different types of resin luting cements.

This study aimed to observe and compare the resin luting cement (RLC)/dentin interfaces of different types of RLC systems with scanning electron microscopy (SEM). This study evaluated six self-adhesive resin luting cement systems (SARLCs), four systems combining a SARLC with a tooth primer (SARLCPs), and six conventional resin luting cement systems (CVRLCs). Cured resin composite rods were bonded to bovine dentin using RLCs in different etching modes. The morphological features at the interfaces were observed using SEM. Although all RLCs in etch-&-rinse (ER) mode showed a clear hybrid layer, most SARLCs had a thinner and more porous hybrid layer than the SARLCPs and CVRLCs. All SARLCPs with primer and CVRLCs showed a thin high-density layer below the primer layer in both etching modes. CVRLCs and SARLCPs with primer treatment systems may be more versatile and reliable when compared to simplified RLC systems.

Whitening efficacy and tooth sensitivity in a combined in-office and at-home whitening protocol: A randomized controlled clinical trial.

OBJECTIVE: This controlled randomized clinical trial determined the whitening efficacy and the intensity and absolute risk of tooth sensitivity in dual whitening when prefilled at-home whitening trays were used between in-office whitening intervals. MATERIALS AND METHODS: An in-office whitening agent containing 35% hydrogen peroxide was used. A prefilled tray with a whitening agent containing 6% hydrogen peroxide was used for at-home whitening. Sixty-six subjects were randomly assigned to three groups. Group I: at-home whitening was performed 10 times between the in-office whitening treatments. Group II: at-home whitening was performed five times between the in-office whitening treatments. Group III: only in-office whitening was performed. The tooth color changes were evaluated using a spectrophotometer. A visual analog scale was used to express the pain intensity. RESULTS: All the groups showed increased ΔE*ab, ΔE00 , and ΔWID with increased whitening sessions. Group I at the 3rd whitening session showed significantly higher ΔE*ab, ΔE00 , and ΔWID than group III. Tooth sensitivity showed higher values up to 24 h after whitening. CONCLUSIONS: Although dual whitening with the prefilled tray and in-office whitening had higher whitening ability than in-office whitening alone, the intensity and absolute risk of tooth sensitivity was similar. CLINICAL RELEVANCE: The dual whitening might produce faster and stronger whitening effects than in-office whitening alone.

Evaluation of the effect of a glass ionomer cement containing fluoro-zinc-silicate glass on dentin remineralization using the ultrasonic pulse-echo method.

The purpose of this study was to investigate the protective effect of a glass ionomer cement (GIC) consisting of fluoro-zinc-silicate glass on the demineralization of bovine dentin using the ultrasonic pulse-echo method. The findings were compared with those obtained using a conventional GIC. Slabs of dentin from bovine teeth were sliced, shaped into a rectangular form, and immersed in 0.5 M ethylenediaminetetraacetic acid solution at 25ºC for 6 days, followed by storage in distilled water for 3 days. After demineralization, they were immersed in artificial saliva with and without the GIC specimens. The propagation times of the longitudinal ultrasonic waves in the samples were measured. The ultrasonic velocities of the fluoro-zinc-silicate glass-containing GICs were significantly increased 2-3 days after the start of the experiment and showed an upward trend thereafter. These findings indicate that the GICs containing fluoro-zinc-silicate glass might exhibit the potential to promote remineralization in the dentin.

Immediate bond performance of resin composite luting systems to saliva-contaminated enamel and dentin in different curing modes.

The purpose of this study was to evaluate the immediate shear bond strength of resin composite luting systems to tooth with or without saliva contamination in different curing modes. The Knoop hardness number of the resin composite luting agents was measured. Four combinations of resin composite luting systems were used. The shear bond strength to bovine teeth was measured with and without saliva contamination in different curing modes at different storage periods. The Knoop hardness number of the resin composite luting agents was also evaluated. Significantly lower enamel and dentin shear bond strengths and Knoop hardness number values were observed in all resin composite luting systems at 5 min versus 24 h, regardless of the curing mode or saliva contamination. The influence of the curing mode of the resin composite luting systems on shear bond strengths and Knoop hardness number was dependent on material. For the saliva contamination conditions, only G-CEM ONE EM did not show any significant difference in shear bond strength among the groups with and without saliva contamination, regardless of curing mode, storage period, or tooth substrate. All the resin composite luting systems showed lower shear bond strengths and Knoop hardness number values immediately after setting.