Long-term in vitro degradation behaviour of Fe and Fe/Mg2Si composites for biodegradable implant applications.

The major drawback of Fe-based materials for biodegradable implant applications is their slow degradation rate. Addition of second phase particles into the Fe matrix can increase the degradation rate at the beginning of the corrosion process. However, so far, there is neither quantitative data on in vitro degradation nor direct experimental evidence for long-term dissolution of Fe-based biodegradable composites. Here, a series of immersion tests at different exposure intervals (20, 50 and 100 days) to modified Hanks' solution were performed to study the degradation behavior of Fe and Fe/Mg2Si composites prepared by different powder metallurgy techniques. The results revealed the role of Mg2Si in the composition and stability of the protective films formed during the static corrosion experiments. Fe/Mg2Si composites showed higher degradation rates than those of pure Fe at all stages of immersion. Degradation rates at distinct exposure intervals strongly depended on the composition and stability of formed oxide, hydroxide, carbonate and phosphate protective films on the degraded surfaces. The release of Fe ions into the solution at later stages of the experiment was limited due to the barrier effect of the insoluble deposit. This fundamental study provided a basis for the processes of protective film formation in modified Hanks' solution, which enables a detailed identification of its characteristic features.

Synthesis, mechanical properties and corrosion behavior of powder metallurgy processed Fe/Mg2Si composites for biodegradable implant applications.

Recently, Fe and Fe-based alloys have shown their potential as degradable materials for biomedical applications. Nevertheless, the slow corrosion rate limits their performance in certain situations. The shift to iron matrix composites represents a possible approach, not only to improve the mechanical properties, but also to accelerate and tune the corrosion rate in a physiological environment. In this work, Fe-based composites reinforced by Mg2Si particles were proposed. The initial powders were prepared by different combinations of mixing and milling processes, and finally consolidated by hot rolling. The influence of the microstructure on mechanical properties and corrosion behavior of Fe/Mg2Si was investigated. Scanning electron microscopy and X-ray diffraction were used for the assessment of the composite structure. Tensile and hardness tests were performed to characterize the mechanical properties. Potentiodynamic and static corrosion tests were carried out to investigate the corrosion behavior in a pseudo-physiological environment. Samples with smaller Mg2Si particles showed a more homogenous distribution of the reinforcement. Yield and ultimate tensile strength increased when compared to those of pure Fe (from 400MPa and 416MPa to 523MPa and 630MPa, respectively). Electrochemical measurements and immersion tests indicated that the addition of Mg2Si could increase the corrosion rate of Fe even twice (from 0.14 to 0.28mm·year-1). It was found that the preparation method of the initial composite powders played a major role in the corrosion process as well as in the corrosion mechanism of the final composite.

Fabrication, mechanical properties and in vitro degradation behavior of newly developed ZnAg alloys for degradable implant applications.

Zn and Zn-based alloys have been recognized as highly promising biodegradable materials for orthopedic implants and cardiovascular stents, due to their proved biocompatibility and, more importantly, lower corrosion rates compared to Mg alloys. However, pure Zn has poor mechanical properties. In this study, Ag is used as a promising alloying element to improve the mechanical properties of the Zn matrix as well as its biocompatibility and antibacterial properties. Accordingly, we design three ZnAg alloys with Ag content ranging from 2.5 to 7.0wt% and investigate the influence of the Ag content on mechanical and corrosion behavior of the alloys. The alloys are developed by casting process and homogenized at 410°C for 6h and 12h, followed by hot extrusion at 250°C with extrusion ratio of 14:1. Degradation behavior is assessed by electrochemical and static immersion tests in Hank's modified solution. Microstructural analysis reveals that hot extrusion significantly reduces the grain size of the alloys. Zn-7.0%Ag alloy shows a reasonably equiaxed and considerably refined microstructure with mean grain size of 1.5µm. Tensile tests at room temperature suggest that increasing the Ag content steadily enhances the tensile strength, while it does not affect the tensile ductility significantly. Zn-7.0%Ag shows high yield strength and ultimate tensile strength of 236MPa and 287MPa, respectively, which is due to the grain refinement and high volume fraction of fine AgZn3 particles precipitating along the grain boundaries during the extrusion process. Among all these alloys, Zn-7.0%Ag displayed superplasticity over a wide range of strain rates (from 5×10-4s-1 to 1.0×10-2s-1) providing the possibility of exploiting forming processes at rapid rates and/or even at lower temperatures. In addition, extruded alloys exhibit slightly faster degradation rate than pure Zn. X-ray diffraction results show the presence of ZnO and Zn(OH)2 on the degraded surfaces. Moreover, scanning electron microscopy imaging reveals that micro-galvanic corrosion is more pronounced on the alloys with higher Ag content due to the higher volume fraction of AgZn3 particles.

Novel Zn-based alloys for biodegradable stent applications: Design, development and in vitro degradation.

The search for a degradable metal simultaneously showing mechanical properties equal or higher to that of stainless steel and uniform degradation is still an open challenge. Several magnesium-based alloys have been studied, but their degradation rate has proved to be too fast and rarely homogeneous. Fe-based alloys show appropriate mechanical properties but very low degradation rate. In the present work, four novel Zn-Mg and two Zn-Al binary alloys were investigated as potential biodegradable materials for stent applications. The alloys were developed by casting process and homogenized at 350°C for 48h followed by hot extrusion at 250°C. Tube extrusion was performed at 300°C to produce tubes with outer/inner diameter of 4/1.5mm as precursors for biodegradable stents. Corrosion tests were performed using Hanks׳ modified solution. Extruded alloys exhibited slightly superior corrosion resistance and slower degradation rate than those of their cast counterparts, but all had corrosion rates roughly half that of a standard purity Mg control. Hot extrusion of Zn-Mg alloys shifted the corrosion regime from localized pitting to more uniform erosion, mainly due to the refinement of second phase particles. Zn-0.5Mg is the most promising material for stent applications with a good combination of strength, ductility, strain hardening exponent and an appropriate rate of loss of mechanical integrity during degradation. An EBSD analysis in the vicinity of the laser cut Zn-0.5Mg tube found no grain coarsening or texture modification confirming that, after laser cutting, the grain size and texture orientation of the final stent remains unchanged. This work shows the potential for Zn alloys to be considered for stent applications.