Push-out strength of root fillings with or without thermomechanical compaction.

AIM: To evaluate the influence of thermomechanical compaction (Tagger's hybrid technique - THT) on the push-out strength of several root filling materials to root dentine. METHODOLOGY: Root canals of eighty roots in human canines were prepared with the ProTaper system and filled with one of the following materials, using either lateral compaction (LC) (n = 40) or THT (n = 40): AH Plus/gutta-percha (GP) (n = 10), Sealer 26/GP (n = 10), Epiphany SE/Resilon (n = 10) and Epiphany SE/GP (n = 10). Three 2-mm-thick dentine slices were obtained from each third of each root. The root filling in the first slice was subjected to a push-out test to evaluate the bond strength of the materials to intraradicular dentine. Data (in MPa) were analysed using anova and post hoc Tukey's test (P < 0.05). Failure mode was determined at × 25 magnification. The other two slices were prepared for scanning electron microscopy (SEM) to examine the surface of the filling materials. RESULTS: Lateral compaction (1.34 ± 1.14 MPa) was associated with a significantly higher bond strength (P < 0.05) than the THT (0.97 ± 0.88 MPa). AH Plus/GP (2.23 ± 0.83 MPa) and Sealer 26/GP (1.86 ± 0.50 MPa) had significantly higher bond strengths than the other materials and differed significantly from each other (P < 0.05). There was a significant difference (P < 0.05) between the coronal (1.36 ± 1.15 MPa), middle (1.14 ± 1.05 MPa) and apical thirds (0.95 ± 0.83 MPa). Considering the technique and root filling material interaction, AH Plus/GP-LC was associated with the highest mean values (2.65 ± 0.66 MPa) (P < 0.05). Sealer 26/GP-LC (2.10 ± 0.46 MPa), AH Plus/GP-THT (1.81 ± 0.78 MPa) and Sealer 26/GP-TH (1.63 ± 0.44 MPa) had intermediate values that were not significantly different from each other (P > 0.05). Epiphany SE was associated with the lowest mean values (3.70 ± 0.86 MPa) (P < 0.05), regardless of the root filling technique and type of solid material (cone). Adhesive failures predominated in the specimens filled with Epiphany SE, whilst mixed and cohesive failures were more frequent in those filled with AH Plus and Sealer 26, regardless of the root filling technique. SEM analysis revealed that LC produced a dense and well-compacted filling whilst the use of a hybrid thermomechanical technique resulted in the solid material (GP or Resilon) intermingled within sealer to form a nonhomogenous mass. CONCLUSION: Lateral compaction was associated with higher bond strengths of the materials to intraradicular dentine than a hybrid technique using thermomechanical compaction. The greatest push-out strengths were obtained when the canals were filled with LC of AH Plus and GP cones.

Correlation between oral health perception and clinical factors in a Brazilian community.

OBJECTIVE: The aim of this study was to analyse associations between self-perception of oral health and relevant clinical, personal and socio-demographic factors in a Brazilian community. MATERIAL AND METHODS: Urban adults living in a city in southern Brazil were interviewerd and examined. Individuals with acute pain and who needed multiple extractions of teeth were excluded. Self-perception and the Oral Health Impact Profile (OHIP-14) were applied to measure the impact of oral conditions on the quality of life. Socio-demographic and clinical indicators were also analysed. RESULTS: The clinical examination revealed a high dental caries experience (DMFT = 18.9) and a high prevalence of periodontal disease. Oral condition was considered "normal" by 42% of respondents. The variables associated with the OHIP-14 were: education, age, self-assessment, dental caries and the DMFT index. CONCLUSIONS: Self-perception of oral health was associated with OHIP-14 and the clinical indicators had low influence in the self-perception. Therefore, the development of educational initiatives and preventive strategies for the adult population is recommended.

Quantitative 3D profilometry and SEM analysis of the adaptation of root-end filling materials placed under an optical microscope.

AIM: To evaluate by 3D profilometry and scanning electron microscopy (SEM), the marginal adaptation of mineral trioxide aggregate (MTA) and Sealer 26 placed in root-end cavities with direct vision or under an optical microscope. METHODOLOGY: The root ends of 52 root filled canine teeth were filled with MTA or Sealer 26 under direct vision or optical microscope (n=13). In each group, eight specimens were analysed by profilometry for measurement of the area and depth of gaps. In the other five specimens, gap area was measured using SEM to verify marginal adaptation and surface characteristic. Data were analysed by parametric (anova and Tukey) and non-parametric (Kruskal-Wallis and Dunn) tests. RESULTS: The assessment of the adaptation of both materials to dentine was not influenced by the mode of visualization, which was confirmed by both profilometry and SEM observations. The voids measured with profilometry for Sealer 26 under direct vision were significantly wider and deeper than those for MTA under direct vision (P<0.05). In SEM, significantly larger gap areas were observed with Sealer 26 (P<0.05). CONCLUSION: Root-end cavities filled with MTA had smaller gaps and better marginal adaptation than Sealer 26.

Bond strength of AH Plus and Epiphany sealers on root dentine irradiated with 980 nm diode laser.

AIM: To evaluate the bond strength of AH Plus and Epiphany sealers to human root canal dentine irradiated with a 980 nm diode laser at different power and frequency parameters, using the push-out test. METHODOLOGY: Sixty canine roots were sectioned below the cementoenamel junction to provide 4-mm-thick dentine discs that had their root canals prepared with a tapered bur and irrigated with sodium hypochlorite, ethylenediaminetetraacetic acid and distilled water. The specimens were assigned to five groups (n = 12): one control (no laser) and four experimental groups that were submitted to 980 nm diode laser irradiation at different power (1.5 and 3.0 W) and frequency (continuous wave and 100 Hz) parameters. Half of specimens in each group had their canals filled with AH Plus sealer and half with Epiphany. The push-out test was performed and data (MPa) were analysed statistically by anova and Tukey's test (P < 0.05). The specimens were split longitudinally and examined under SEM to assess the failure modes after sealer displacement. RESULTS: The specimens irradiated with the diode laser and filled with AH Plus had significantly higher bond strength values (8.69 +/- 2.44) than those irradiated and filled with Epiphany (3.28 +/- 1.58) and the nonirradiated controls (3.86 +/- 0.60). The specimens filled with Epiphany did not differ significantly to each other or to the control (1.75 +/- 0.69). There was a predominance of adhesive failures at Epiphany-dentine interface (77%) and mixed failures at AH Plus-dentine interface (67%). CONCLUSIONS: The 980 nm diode laser irradiation of root canal dentine increased the bond strength of AH Plus sealer, but did not affect the adhesion of Epiphany sealer.