Physicochemical properties and in vivo evaluation of Pt/TiO2-SiO2 nanopowders.

AIM: Sol-gel is a suitable and advantageous method to synthesize mixed oxide nanomaterials with unique physicochemical and biological properties. MATERIALS & METHODS: In this work, TiO2-SiO2 nanopowders cogeled with platinum acetylacetonate were developed and studied in the perspective of nanomedicine. The physicochemical properties of the Pt/TiO2-SiO2 nanopowders, named NanoRa2-Pt, were evaluated in detail by means of complementary spectroscopic and microscopic tools. The nanopowder's biocatalytic efficiency in wound healing was evaluated in a Type I diabetes animal model. RESULTS: These are TiO2-SiO2 submicron mesoporous particles with variable size and shape containing ultra-small platinum nanoparticles with catalytic properties. CONCLUSION: The use of NanoRa2-Pt catalyzes the natural healing processes with a faster remodeling stage. These sols, which we call nanobiocatalysts, belong to an emerging and very promising research field known as catalytic nanomedicine.

Immersion Calorimetry: Molecular Packing Effects in Micropores.

Repeated and controlled immersion calorimetry experiments were performed to determine the specific surface area and pore-size distribution (PSD) of a well-characterized, microporous poly(furfuryl alcohol)-based activated carbon. The PSD derived from nitrogen gas adsorption indicated a narrow distribution centered at 0.57±0.05 nm. Immersion into liquids of increasing molecular sizes ranging from 0.33 nm (dichloromethane) to 0.70 nm (α-pinene) showed a decreasing enthalpy of immersion at a critical probe size (0.43-0.48 nm), followed by an increase at 0.48-0.56 nm, and a second decrease at 0.56-0.60 nm. This maximum has not been reported previously. After consideration of possible reasons for this new observation, it is concluded that the effect arises from molecular packing inside the micropores, interpreted in terms of 2D packing. The immersion enthalpy PSD was consistent with that from quenched solid density functional theory (QSDFT) analysis of the nitrogen adsorption isotherm.

Carbon-supported ionic liquids as innovative adsorbents for CO2 separation from synthetic flue-gas.

Fixed-bed thermodynamic CO2 adsorption tests were performed in model flue-gas onto Filtrasorb 400 and Nuchar RGC30 activated carbons (AC) functionalized with [Hmim][BF4] and [Emim][Gly] ionic liquids (IL). A comparative analysis of the CO2 capture results and N2 porosity characterization data evidenced that the use of [Hmim][BF4], a physical solvent for carbon dioxide, ended up into a worsening of the parent AC capture performance, due to a dominating pore blocking effect at all the operating temperatures. Conversely, the less sterically-hindered and amino acid-based [Emim][Gly] IL was effective in increasing the AC capture capacity at 353 K under milder impregnation conditions, the beneficial effect being attributed to both its chemical affinity towards CO2 and low pore volume reduction. The findings derived in this work outline interesting perspectives for the application of amino acid-based IL supported onto activated carbons for CO2 separation under post-combustion conditions, and future research efforts should be focused on the search for AC characterized by optimal pore size distribution and surface properties for IL functionalization.

Assessment of CO2 adsorption capacity on activated carbons by a combination of batch and dynamic tests.

In this work, batch and dynamic adsorption tests are coupled for an accurate evaluation of CO2 adsorption performance of three different activated carbons (AC) obtained from olive stones by chemical activation followed by physical activation with CO2 at varying times (i.e., 20, 40, and 60 h). Kinetic and thermodynamic CO2 adsorption tests from simulated flue gas at different temperatures and CO2 pressures are carried out under both batch (a manometric equipment operating with pure CO2) and dynamic (a lab-scale fixed-bed column operating with a CO2/N2 mixture) conditions. The textural characterization of the AC samples shows a direct dependence of both micropore and ultramicropore volume on the activation time; hence, AC60 has the higher contribution. The adsorption tests conducted at 273 and 293 K showed that when CO2 pressure is lower than 0.3 bar, the lower the activation time, the higher CO2 adsorption capacity; a ranking of ω(eq)(AC20) > ω(eq)(AC40) > ω(eq)(AC60) can be exactly defined when T = 293 K. This result is likely ascribed to the narrower pore size distribution of the AC20 sample, whose smaller pores are more effective for CO2 capture at higher temperature and lower CO2 pressure, the latter representing operating conditions of major interest for decarbonation of flue gas effluent. Moreover, the experimental results obtained from dynamic tests confirm the results derived from the batch tests in terms of CO2 adsorption capacity. It is important to highlight the fact that the adsorption of N2 on the synthesized AC samples can be considered to be negligible. Finally, the importance of proper analysis for data characterization and adsorption experimental results is highlighted for the correct assessment of the CO2 removal performance of activated carbons at different CO2 pressures and operating temperatures.

Mesoporous materials for clean energy technologies.

Alternative energy technologies are greatly hindered by significant limitations in materials science. From low activity to poor stability, and from mineral scarcity to high cost, the current materials are not able to cope with the significant challenges of clean energy technologies. However, recent advances in the preparation of nanomaterials, porous solids, and nanostructured solids are providing hope in the race for a better, cleaner energy production. The present contribution critically reviews the development and role of mesoporosity in a wide range of technologies, as this provides for critical improvements in accessibility, the dispersion of the active phase and a higher surface area. Relevant examples of the development of mesoporosity by a wide range of techniques are provided, including the preparation of hierarchical structures with pore systems in different scale ranges. Mesoporosity plays a significant role in catalysis, especially in the most challenging processes where bulky molecules, like those obtained from biomass or highly unreactive species, such as CO2 should be transformed into most valuable products. Furthermore, mesoporous materials also play a significant role as electrodes in fuel and solar cells and in thermoelectric devices, technologies which are benefiting from improved accessibility and a better dispersion of materials with controlled porosity.

Investigation on the low-temperature transformations of poly(furfuryl alcohol) deposited on MCM-41.

MCM-41-type mesoporous silica was used as a support for poly(furfuryl alcohol) deposition. This material was produced by precipitation-polycondensation of furfuryl alcohol (FA) in aqueous slurry of the SiO2 support followed by controlled partial carbonization. By tuning the FA/MCM-41 mass ratio in the reaction mixture, various amounts of polymer particles were introduced on the inner and outer surface of the MCM support. The thermal decomposition of the PFA/MCM-41 composites was studied by thermogravimetry (TG) and spectroscopic techniques (DRIFT, XPS), whereas the evolution of textural parameters with increasing polymer content was investigated using low-temperature adsorption of nitrogen. The mechanism of thermal transformations of PFA deposited on the MCM-41 surface was discussed in detail. It was found that heating at a temperature of about 523 K resulted in opening of the furan rings and the formation of γ-diketone moieties, which were found to be the highest effective surface species for the adsorption of polar volatile organic compounds. A further increase in calcination temperature caused a drop in the amounts of surface carbonyls and the appearance of condensed aromatic domains.

Formation of CO(x)-free H2 and cup-stacked carbon nanotubes over nano-Ni dispersed single wall carbon nanohorns.

Transitional metals (M) were dispersed on single-wall carbon nanohorns (M/SWCNHs, M = Fe, Co, Ni, Cu) by simple thermal treatment of the deposited metal nitrate without H(2) reduction. Nanometallic Ni particles on SWCNH were evidenced by high-resolution transmission electron microscopic observation and X-ray photoelectron spectroscopy. The nano-Ni dispersed on SWCNH showed the highest CH(4) decomposition activity; the activity of used transitional metals decreases in the order Ni ≫ Co > Fe ≫ Cu. On the other hand, the reaction rate over Ni/SWCNH was much larger than that over Ni/Al(2)O(3), and the former provided CO(x)-free H(2) and cup-stacked carbon nanotubes, while Ni/Al(2)O(3) produced CO(x) in addition to H(2). SWCNH was superior to Al(2)O(3) as the catalyst support of Ni for the CH(4) decomposition reaction.