Permeability improvement of polyethersulfone-polietylene glycol (PEG-PES) flat sheet type membranes by tripolyphosphate-crosslinked chitosan (TPP-CS) coating.

In this study, improvement of urea and creatinine permeability of polyethersulfone (PES) membrane by coating with synthesized tripolyphosphate-crosslinked chitosan (TPP-CS) has been conducted. Original and modified membranes, e.g. pristine PES, polyethersulfone-polyethylene glycol (PES-PEG) and PES-PEG/TPP-CS membranes were characterized using FTIR, DTG, SEM, AFM, water uptake, contact angles, porosity measurement, tensile strength test and permeation tests against urea and creatinine. The results show that the PES modification by TPP-CS coating has been successfully carried out. The water uptake ability, hydrophilicity and porosity of the modified membranes increase significantly to a greater degree. All modified membranes have good thermal stability and tensile strength and their permeation ability towards urea and creatinine increase with the increasing concentration of TPP-CS. PES membrane has urea clearance ability of 7.36 mg/dL and creatinine of 0.014 mg/dL; membrane PES-PEG shows urea clearance of 11.87 mg/dL and creatinine of 0.32 mg/dL; while PES-PEG/TPP-CS membrane gives urea clearance of 20.87-36.40 mg/dL and creatinine in the range of 0.52-0.78 mg/dL. These results suggest that the PES-PEG membrane coated with TPP-CS is superior and can be used as potential material for hemodialysis membrane.

In vitro hemocompatibility of PVA-alginate ester as a candidate for hemodialysis membrane.

Alginate based biopolymer with improved physical and chemical properties after esterification using polyvinyl alcohol (PVA) has been studied for possible application as a hemodialysis membrane. The alginic acid to vinyl alcohol molar ratio was predetermined at 0, 0.1, 0.5 and 1. Mechanical strength, hydrophilicity and Ca(2+) adsorption of the membrane before and after modification were evaluated. The obtained PVA-alginate (PVA-Alg) ester membrane was also confirmed using FTIR and SEM. It shows that the PVA-Alg membrane tensile strength is higher than that of native alginate. The water contact angle of the membrane was found to be around 33-50°. The Ca(2+) adsorption capacity tends to decrease with the increase in molar ratio. Furthermore, the modified PVA-Alg ester membrane achieves better protein adsorption and platelet adhesion than the unmodified one. It also exhibits a dialysis performance of 47.1-50.0% for clearance of urea and 42.2-44.6% for clearance of creatinine, respectively. It is expected that this PVA-Alg ester may challenge cellulose acetate for potential application as hemodialysis membranes.