RESUMO
Electroless Ni-P films were investigated with the aim of application as barrier and seed layers in 3D interconnect technology. Different shapes of blind-via holes were fabricated with a deep reactive ion etcher and SiO2 formed on these holes as an insulating layer. The surface of the substrate has been made hydrophilic by O2 plasma treatment with 100 W of power for 20 min. Electroless Ni-P films were deposited as both a diffusion barrier and a seed layer for Cu filling process. Prior to plating, substrates were activated in a palladium chloride solution after sensitization in a tin chloride solution with various conditions in order to deposit uniform films in TSV. After the formation of the electroless barrier layer, electro Cu was plated directly on the barrier layer. Ni-P films fabricated in blind-via holes were observed by scanning electron microscope. Energy dispersive spectroscopy line scanning was carried out for evaluating the diffusion barrier properties of the Ni-P films. The electroless Ni-P layer worked well as a Cu diffusion barrier until 300 degrees C. However, Cu ions diffused into barrier layer when the annealing temperature increases over 400 degrees C.