Selective elimination of lead(II) ions by alginate/polyurethane composite foams.

A new type of adsorbent which is capable of selectively adsorbing lead(II) ions (Pb(2+)) was developed. The adsorbent was generated by reaction of sodium alginate with NB-9000B, a polyisocyanate type of prepolymer of polyurethane. The adsorbent was a hydrophilic and flexible alginate/polyurethane composite foam (ALG/PUCF) with the alginate chemically immobilized in the cell walls of the foam. Acid-base titration was used to quantify the concentration of carboxyl groups, which are present on the alginate molecules of the ALG/PUCF, functioning as the essential sites for binding Pb(2+). For the optimized ALG/PUCF, the carboxyl was found to be 38.2+/-1.2mumol/g of dry weight. The capacity for adsorbing Pb(2+) ions in 1.0g of dry weight of the optimized ALG/PUCF was found to be 16.0+/-2.1mumol, indicating that ion exchange was the essential mechanism for adsorbing Pb(2+) ions. The adsorption capacity was found to be highly sensitive to the pH of the sample solution; lower pH (<3) significantly decreased the adsorption. Competing ions such as Mg(2+), Ca(2+), and Cd(2+) also caused a decrease in selectivity and capacity for Pb(2+) adsorption, although the effect was less pronounced than the effect of pH. The ALG/PUCF is highly stable, flexible and easy to use. ALG/PUCF is also reusable after regeneration with ethylenediamine-N,N,N',N'-tetraacetic acid, disodium salt (EDTA-2Na). Due to these features, this adsorbent may be highly useful for elimination of Pb(2+) ions from contaminated water.

Affinity-based elimination of aromatic VOCs by highly crystalline multi-walled carbon nanotubes.

Carbon nanotubes (CNTs) are capable of adsorbing pollutant chemicals. Their adsorptive capacities and adsorbing mechanisms, however, are not fully understood. As-grown CNTs often contain both crystalline and amorphous carbon, and the ratio of carbon types can affect adsorption. In this study, highly crystalline multi-walled carbon nanotubes (HC-MWCNTs) were used as the adsorbent for volatile organic compounds (VOCs) in contaminated air samples. Air containing 23 added VOCs (1,1-dichloroethylene, dichloromethane, trans-1,2-dichloroethylene, cis-1,2-dichloroethylene, chloroform, 1,1,1-trichloroethane, carbon tetrachloride, 1,2-dichloroethane, benzene, trichloroethylene, 1,2-dichloropropane, bromodichloromethane, cis-1,3-dichloropropene, toluene, trans-1,3-dichloropropene, 1,1,2-trichloroethane, tetrachloroethylene, dibromochloromethane, m-xylene, p-xylene, o-xylene, bromoform, and p-dichlorobenzene) was used for model samples. Adsorptive experiments were carried out by passing the air samples through a cartridge packed with HC-MWCNTs. Initial results showing high selectivity and high affinity for adsorbing aromatic VOCs (benzene, toluene, m-xylene, p-xylene, o-xylene, and p-dichlorobenzene) have provided new insight into the adsorption mechanisms. Data suggest that the HC-MWCNTs, unlike conventional carbon materials, adsorb aromatic compounds according to Fukui's frontier theory, which is based on the interactions between the HOMO and LUMO of the aromatic VOCs and those of the HC-MWCNTs.