RESUMO
Carbon fiber-reinforced plastic (CFRP) has been widely investigated as a reinforcement material to address the corrosion and durability issues of reinforced concrete (RC). To improve the strain of FRP grids, we investigated the effect of single-fiber types, hybrid ratios, and stacking patterns on the strain of the composite materials. Blended fabrics in which different fibers are woven were used to further improve the strain of carbon fibers (CFs). In the blended fabrics, CFs with high tensile strength were mixed with high-strain glass fibers (GFs) or aramid fibers (AFs). Fibers with different mechanical properties were mixed to improve the strain without reducing the tensile strength of the composite materials. The fiber arrangement direction was controlled by CF/GF blended fabric. CFs are arranged in the direction parallel to the tensile load direction with no strength degradation, and GFs are arranged in the direction perpendicular to the increase in strain. Compared to the mechanical properties of the single CF composites, the fabrics obtained via an FRP mixing method proposed in this study showed an increase in the tensile strength by 7% from 568.17 to 608.34 MPa with no strength degradation and an increase in strain by 34% from 0.97% to 1.30%.
RESUMO
As the use of carbon-fiber-reinforced plastic (CFRP) and glass-fiber-reinforced plastic is frequent in the field of construction, a method for measuring FRP resin content is needed. Herein, thermal gravimetric analysis (TGA) was employed to optimize the heat treatment conditions (temperature and time) for determining the resin content in which only the resin was removed without fiber heat loss. Accordingly, the measurement was performed in 100 °C increments at a resin pyrolysis temperature up to 800 °C with a heat treatment time of 4 h to continuously observe the degree of thermal decomposition of the resin. The thermal decomposition of unsaturated polyester was confirmed at the melting point (350 â) regardless of the type of fibers used as reinforcement. In the case of CFRP, most of the resin decomposition occurred at 300 °C. Notably, the resin was removed at a pyrolysis temperature of 400 â and almost no change in weight was observed. However, at a pyrolysis temperature of 500 °C or higher, the thermal decomposition of the fibers occurred partially. The results show that the composite resin was removed within 10 min at a pyrolysis temperature of 400 °C in an air atmosphere when using TGA.
RESUMO
In the present study, fiber-reinforced plastics (FRP) grid-reinforced concrete with very rapid hardening polymer (VRHP) mortar composites were fabricated using three types of design methods for the FRP grid (hand lay-up method, resin infusion method, and prepreg oven vacuum bagging method), along with two types of fibers (carbon fiber and glass fiber) and two types of sheets (fabric and prepreg). The FRP grid was prepared by cutting the FRP laminates into a 10 mm thick, 50 mm × 50 mm grid. The tensile behavior of the FRP grid embedded in composites was systematically analyzed in terms of the load extension, fracture mode, partial tensile strain, and load-bearing rate. The CFRP grid manufactured by the prepreg OVB method showed the best tensile behavior compared to the CFRP grid manufactured by the hand lay-up and resin infusion methods. The load-bearing of each grid point was proportional to the height from the load-bearing part when reaching the maximum tensile load. In addition, finite element analysis was conducted to compare the experimental and analysis results.