Ultrahigh proton conductivity of four ionic hydrogen-bonded organic frameworks based on functionalized terephthalates.

Recently, the utilization of hydrogen-bonded organic frameworks (HOFs) with high crystallinity and inherent well-defined H-bonding networks in the field of proton conduction has received increasing attention, but obtaining HOFs with excellent water stability and prominent proton conductivity (σ) remains challenging. Herein, by employing functionalized terephthalic acids, 2,5-dihydroxyterephthalic acid, 2-hydroxyterephthalic acid, 2-nitro terephthalic acid, and terephthalic acid, respectively, four highly water-stable ionic HOFs (iHOFs), [(C8H5O6)(Me2NH2)]∙2H2O (iHOF 1), [(C8H5O5)(Me2NH2)] (iHOF 2), [(C8H4NO6)(Me2NH2)] (iHOF 3) and [(C8H5O4)(Me2NH2)] (iHOF 4) were efficiently prepared by a straightforward synthesis approach in DMF and H2O solutions. The alternating-current (AC) impedance testing in humid conditions revealed that all four iHOFs were temperature- and humidity-dependent σ, with the greatest value reaching 10-2 S·cm-1. As expected, the high density of free carboxylic acid groups, crystallization water, and protonated [Me2NH2]+ units offer adequate protons and hydrophilic environments for effective proton transport. Furthermore, the σ values of these iHOFs with different functional groups were compared. It was discovered that it dropped in the following order under 100 °C and 98 % relative humidity (RH): σ iHOF 1 (1.72 × 10-2 S·cm-1) > σ iHOF 2 (4.03 × 10-3 S·cm-1) > σ iHOF 3 (1.46 × 10-3 S·cm-1) > σ iHOF 4 (4.86 × 10-4 S·cm-1). Finally, we investigated the causes of the above differences and the proton transport mechanism inside the framework using crystal structure data, water contact angle tests, and activation energy values. This study provides new motivation to develop highly proton-conductive materials.

Tailored Porous Ferrocene-Based Metal-Organic Frameworks as High-Performance Proton Conductors.

Although crystalline metal-organic frameworks (MOFs) have gained a great deal of interest in the field of proton conduction in recent years, the low stability and poor proton conductivity (σ) of some MOFs have hindered their future applications. As a result, resolving the issues listed above must be prioritized. Due to their exceptional structural stability, MOFs with ferrocene groups that exhibit particular physical and chemical properties have drawn a lot of attention. This study describes the effective preparation of a set of three-dimensional ferrocene-based MOFs, MIL-53-FcDC-Al/Ga and CAU-43, containing both main group metals and 1,1'-ferrocene dicarboxylic acid (H2FcDC). Multiple measurements, including powder X-ray diffraction (PXRD), infrared (IR), and scanning electron microscopy (SEM), confirmed that the addition of ferrocene groups enhanced the thermal, water, and acid-base stabilities of the three MOFs. Consequently, their proton-conductive behaviors were meticulously measured utilizing the AC impedance approach, and their best proton conductivities are 5.20 × 10-3, 2.31 × 10-3, and 1.72 × 10-4 S/cm at 100 °C/98% relative humidity (RH), respectively. Excitingly, MIL-53-FcDC-Al/Ga demonstrated an extraordinarily ultrahigh σ of above 10-4 S·cm-1 under 30 °C/98% RH. Using data from structural analysis, PXRD, SEM, thermogravimetry (TG), and activation energy, their proton transport mechanisms were thoroughly examined. The fact that these MOFs are notably easy to assemble, inexpensive, toxin-free, and stable will increase the range of practical uses for them.

Ligand-Functionalized MIL-68-type Indium(III) Metal-Organic Frameworks with Prominent Intrinsic Proton Conductivity.

Indium-based metal-organic frameworks (In-MOFs) have now become an attractive class of porous solids in materials science and electrochemistry due to their diverse structures and promising applications. In the field of proton conduction, to find more crystalline MOFs with splendid proton-conductive properties, herein, five three-dimensional isostructural In-MOFs, MIL-68-In or MIL-68-In-X (X = NH2, OH, Br, or NO2) using terephthalic acid (H2BDC) or functionalized terephthalic acids (H2BDC-X) as multifunctional linkages were efficiently fabricated. First, the outstanding structural stability of the five MOFs, including thermal and water stability, was verified by thermal analysis and powder X-ray diffraction. Subsequently, the H2O-mediated proton conductivities (σ) were fully assessed and compared. Notably, their σ evinced a significant positive correlation between the temperature or relative humidity (RH) and varied with the functional groups on the organic ligands. Impressively, their highest σ values are up to 10-3-10-4 S/cm (100 °C/98% RH) and change in this order: MIL-68-In-OH (1.72 × 10-3 S/cm) > MIL-68-In-NH2 (1.70 × 10-3 S/cm) > MIL-68-In-NO2 (4.47 × 10-4 S/cm) > MIL-68-In-Br (4.11 × 10-4 S/cm) > MIL-68-In (2.37 × 10-4 S/cm). Finally, the computed activation energy values under 98 or 68% RHs are assessed, and the related proton conduction mechanisms are speculated. Moreover, after electrochemical testing, these MOFs illustrate remarkable structural rigidity, laying a meritorious material foundation for future applications.