Polyetherimide-Reinforced Smart Inlays for Bondline Surveillance in Composites.

An integrable sensor inlay for monitoring crack initiation and growth inside bondlines of structural carbon fiber-reinforced plastic (CFRP) components is presented. The sensing structures are sandwiched between crack-stopping poly(vinyliden fluoride) (PVDF) and a thin reinforcing polyetherimide (PEI) layer. Good adhesion at all interfaces of the sensor system and to the CFRP material is crucial, as weak bonds can counteract the desired crack-stopping functionality. At the same time, the chosen reinforcing layer must withstand high strains, safely support the metallic measuring grids, and possess outstanding fatigue strength. We show that this robust sensor system, which measures the strain at two successive fronts inside the bondline, allows to recognize cracks in the proximity of the inlay regardless of the mechanical loads. Feasibility is demonstrated by static load tests as well as cyclic long-term fatigue testing for up to 1,000,000 cycles. In addition to pure crack detection, crack distance estimation based on sensor signals is illustrated. The inlay integration process is developed with respect to industrial applicability. Thus, implementation of the proposed system will allow the potential of lightweight CFRP constructions to be better exploited by expanding the possibilities of structural adhesive bonding.

Phase Transitions of Polarised PVDF Films in a Standard Curing Process for Composites.

The article reports on the influence of annealing PVDF in an autoclave process on the PVDF phase composition. DSC, FTIR and XRD measurements serve to observe the phase changes in an already stretched, polarised and ß-phase rich film. Annealing was conducted between 90 and 185 ∘C to cover a broad range of curing processes in an autoclave. The ß-phase is found to be stable up to near the melting range at 170 ∘C. At 175 ∘C, the non-piezoelectric α-phase dominates and the piezoelectric γ- and γ'-phases appear. The γ-phase grows at elevated temperatures and replaces the ß-phase. This observation stresses the importance of developing new methods to reactivate the polarisation after annealing, in particular for the integration of PVDF as a sensor in laminated structures, such as CFRP.

Smart Inlays for Simultaneous Crack Sensing and Arrest in Multifunctional Bondlines of Composites.

Disbond arrest features combined with a structural health monitoring system for permanent bondline surveillance have the potential to significantly increase the safety of adhesive bonds in composite structures. A core requirement is that the integration of such features is achieved without causing weakening of the bondline. We present the design of a smart inlay equipped with a micro strain sensor-system fabricated on a polyvinyliden fluorid (PVDF) foil material. This material has proven disbond arrest functionality, but has not before been used as a substrate in lithographic micro sensor fabrication. Only with special pretreatment can it meet the requirements of thin film sensor elements regarding surface roughness and adhesion. Moreover, the sensor integration into composite material using a standard manufacturing procedure reveals that the smart inlays endure this process even though subjected to high temperatures, curing reactions and plasma treatment. Most critical is the substrate melting during curing when sensory function is preserved with a covering caul plate that stabilizes the fragile measuring grids. The smart inlays are tested by static mechanical loading, showing that they can be stretched far beyond critical elongations of composites before failure. The health monitoring function is verified by testing the specimens with integrated sensors in a cantilever bending setup. The results prove the feasibility of micro sensors detecting strain gradients on a disbond arresting substrate to form a so-called multifunctional bondline.