RESUMO
A selective catalytic reduction (SCR)-coated particulate filter was evaluated by means of dynamic tests performed using NH3, NO2, O2 and H2O. The reactions were examined both prior to and after soot removal in order to study the effect of soot on ammonium nitrate formation and decomposition, ammonia storage and NO2 SCR. A slightly larger ammonia storage capacity was observed when soot was present in the sample, which indicated that small amounts of ammonia can adsorb on the soot. Feeding of NO2 and NH3 in the presence of O2 and H2O at low temperature (150, 175 and 200°C) leads to a large formation of ammonium nitrate species and during the subsequent temperature ramp using H2O and argon, a production of nitrous oxides was observed. The N2O formation is often related to ammonium nitrate decomposition, and our results showed that the N2O formation was clearly decreased by the presence of soot. We therefore propose that in the presence of soot, there are fewer ammonium nitrate species on the surface due to the interactions with the soot. Indeed, we do observe CO2 production during the reaction conditions also at 150°C, which shows that there is a reaction with these species and soot. In addition, the conversion of NOx due to NO2 SCR was significantly enhanced in the presence of soot; we attribute this to the smaller amount of ammonium nitrate species present in the experiments where soot is available since it is well known that ammonium nitrate formation is a major problem at low temperature due to the blocking of the catalytic sites. Further, a scanning electron microscopy analysis of the soot particles shows that they are about 30-40 nm and are therefore too large to enter the pores of the zeolites. There are likely CuxOy or other copper species available on the outside of the zeolite crystallites, which could have been enhanced due to the hydrothermal treatment at 850°C of the SCR-coated filter prior to the soot loading. We therefore propose that soot is interacting with the ammonium nitrate species on the CuxOy or other copper species on the surface of the zeolite particles, which reduces the ammonium nitrate blocking of the catalyst and thereby results in higher NO2 SCR activity.
RESUMO
The electrocatalytic oxidation of formaldehyde, which results in CO(2) and HCOOH formation, was investigated under galvanostatic conditions on nanostructured Pt/glassy carbon (GC) electrodes fabricated by employing colloidal lithography (CL). The measurements were performed on structurally well-defined model electrodes of different Pt surface coverages under different applied currents (current densities) and at constant electrolyte transport in a thin-layer flow cell connected to a differential electrochemical mass spectrometry (DEMS) setup to monitor the dynamic response of the reaction selectivity under these conditions. Periodic oscillations of the electrode potential and the CO(2) formation rate appear not only for a continuous Pt film, but also for the nanostructured Pt/GC electrodes when a critical current density is exceeded. The critical current density for achieving regular oscillation patterns increased with decreasing Pt nanodisk density. Lower oscillation frequencies of the electrode potential and lower CO(2) formation rate for nanostructured Pt/GC electrodes compared to continuous Pt film at similar applied current densities suggest that transport processes play an essential role. Moreover, from the simple periodic response of the nanostructured electrodes it follows that all individual Pt disks in the array oscillate in synchrony. This result is discussed in terms of the different modes of spatial coupling present in the system: global coupling, migration coupling and mass transport of the essential chemical species, and the coverage of corresponding adsorbates.
