The effects of autohydrolysis pretreatment on the structural characteristics, adsorptive and catalytic properties of the activated carbon prepared from Eucommia ulmoides Oliver based on a biorefinery process.

Eucommia ulmoides Oliver (EU) wood was consecutively treated by autohydrolysis pretreatment and chemical carbonization post-treatment based on a biorefinery process. Results showed that the optimal condition of the autohydrolysis pretreatment and carbonization process yielded 10.37kg xylooligosaccharides (XOS), 1.39kg degraded hemicellulosic products, 17.29kg other degraded products from hemicelluloses and 40.72kg activated carbon (SBET of 1534.06m2/g) from the 100kg raw materials. Simultaneously, 29.14kg gas products generated from the optimum integrated process was significantly lower than that from the direct carbonization process (68.84kg). Besides, the optimal activated carbon (AC170-1.0) also showed a moderate catalytic activity and high stability for hydrogen production by catalytic methane decomposition. Overall, the data presented indicated that the integrated process is an eco-friendly and efficient process to produce XOS and activated carbon, which is beneficial for value-added and industrial application of EU wood.

Effect of structural changes of lignin during the autohydrolysis and organosolv pretreatment on Eucommia ulmoides Oliver for an effective enzymatic hydrolysis.

Eucommia ulmoides Oliver (EU) wood was successively treated by autohydrolysis and organosolv pretreatment integrated process. Autohydrolysis pretreatment facilitated xylooligosaccharides production, subsequent organosolv pretreatment to obtain high-purity lignin and digestible cellulose-rich residue. Results showed that the lignin fractions obtained exhibited smaller molecular weights, narrow polydispersity, more phenolic OH groups and higher syringyl/guaiacyl ratios (S/G) than the milled wood lignin. NMR characterization of the lignin revealed that the ß-O-4 linkages significantly cleaved and the structure of stilbene formed, but its resinol (ß-ß) was resistant to be degraded by organosolv delignification. Moreover, the glucose yield of the integrated residue achieved a maximum value of 89.3% after enzyme hydrolysis, separately about 1.0, 1.3, 3.8 times as compared to that of the ethanol organosolv residue, the hydrothermally treated residue and the EU wood, respectively, which indicated that the integrated process was a promising approach to value-added utilization of the EU wood.

[Carbon sequestration of young Robinia pseudoacacia plantation in Loess Plateau].

In order to understand the carbon sequestration of ecological forests in Loess Plateau, a comparative study was made on the organic carbon density (OCD) of soil, litter, and plant organs in an 8-year-old Robinia pseudoacacia plantation and nearby barren land. Comparing with the barren land, the young R. pseudoacacia plantation had a decrease (0.26 kg x m(-2)) of soil OCD, but the OCD in its litter, root system, and aboveground organs increased by 121.1%, 202.0%, and 656. 7%, respectively, with a total carbon sequestration increased by 3.3% annually, which illustrated that R. pseudoacacia afforestation on Loess Plateau had an obvious positive effect on carbon sequestration.

Studies on the preparation of biodiesel from Zanthoxylum bungeanum Maxim seed oil.

To reduce the cost of biodiesel production, the feasibility of Zanthoxylum bungeanum Maxim seed oil (ZBMSO) was studied to produce biodiesel. A methyl ester biodiesel was produced from ZBMSO using methanol, sulfuric acid, and potassium hydroxide in a two-stage process. The main variables that affect the process were investigated. The high level of free fatty acids in ZBMSO was reduced to < 1% by an acid-catalyzed (2% H2SO4) esterification with methanol to oil molar ratios of 20-25:1 for 1 h. A maximum yield of 96% of methyl esters in ZBMSO biodiesel was achieved using a 6.5:1 molar ratio of methanol to oil, 0.9% KOH (percent oil), and reaction time of 0.5 h at 55 degrees C. Further investigation has also been devoted to the assessment of some important fuel properties of ZBMSO biodiesel produced under the optimized conditions according to specifications for biodiesel as fuel in diesel engines. The fuel properties of the ZBMSO biodiesel obtained are similar to those of no. 0 petroleum diesel fuel, and most of the parameters comply with the limits established by specifications for biodiesel.