RESUMO
Recently, there has been increased use of calcium-nitrite and calcium-nitrate as the main components of chloride- and alkali-free anti-freezing agents to promote concrete hydration in cold weather concreting. As the amount of nitrite/nitrate-based accelerators increases, the hydration of tricalcium aluminate (C3A phase) and tricalcium silicate (C3S phase) in cement is accelerated, thereby improving the early strength of cement and effectively preventing initial frost damage. Nitrite/nitrate-based accelerators are used in larger amounts than usual in low temperature areas below -10 °C. However, the correlation between the hydration process and strength development in concrete containing considerable nitrite/nitrate-based accelerators remains to be clearly identified. In this study, the hydrate composition (via X-ray diffraction and nuclear magnetic resonance), pore structures (via mercury intrusion porosimetry), and crystal form (via scanning electron microscopy) were determined, and investigations were performed to elucidate the effect of nitrite/nitrate-based accelerators on the initial strength development and hydrate formation of cement. Nitrite/nitrate-AFm (aluminate-ferret-monosulfate; AFm) was produced in addition to ettringite at the initial stage of hydration of cement by adding a nitrite/nitrate-based accelerator. The amount of the hydrates was attributed to an increase in the absolute amounts of NO2- and NO3- ions reacting with Al2O3 in the tricalcium aluminate (C3A phase). Further, by effectively filling the pores, it greatly contributed to the enhancement of the strength of the hardened cement product, and the degree of the contribution tended to increase with the amount of addition. On the other hand, in addition to the occurrence of cracks due to the release of a large amount of heat of hydration, the amount of expansion and contraction may increase, and it is considered necessary to adjust the amount used for each concrete work.
RESUMO
Recently, calcium nitrite (Ca(NO2)2) and calcium nitrate (Ca(NO3)2) have been increasingly used as the main components of salt- and alkali-free anti-freezing agents, for promoting concrete hydration in cold-weather concreting. With an increase in the amount of nitrite-based accelerator, the hydration of C3A, C3S, and ßC2S in the cement is accelerated, thereby improving its early strength and effectively preventing the initial frost damage. Meanwhile, with an increase in the amount of nitrite-based accelerator, the expansion and shrinkage of the concrete-and, therefore, the crack occurrence-are expected to increase. In this study, various experiments were conducted on shrinkage, crack initiation, and the development of mortar containing a considerable amount of a nitrite-based accelerator. The result confirmed that, as the amount of nitrite-based accelerator was increased, the shrinkage was increased, and cracking in early age was more likely to occur, compared to the cases without the addition of this accelerator.
RESUMO
There has recently been an increased use of anti-freezing agents that are primarily composed of salt- and alkali-free calcium nitrite (Ca(NO2)2) and calcium nitrate (Ca(NO3)2) to promote the hydration reaction of concrete in cold weather concreting. Nitrite-nitrate based accelerators accelerate the hydration of C3A and C3S in cement more quickly when their quantities are increased, thereby boosting the concrete's early strength and effectively preventing early frost damage. However, the connection between the hydrate formation behavior and the strength development characteristic over time has yet to be clearly identified. Therefore, in this study, a wide range of physicochemical reviews were carried out to clarify the relationship between the hydrate formation behavior and the strength development characteristics, both at an early age and at later ages, which results from the addition of nitrite-nitrate based accelerators to concrete in varying amounts. These accelerators also act as anti-freezing agents. The results show that an increased quantity of nitrite-nitrate based accelerators caused an increase in the early strength of the concrete. This was due to the formation of nitrite and nitrate hydrates in large amounts, in addition to ettringite containing SO42, which is generated during the hydration reaction of normal Portland cement at an early age. On the other hand, at later ages, there was a rise in nitrite and nitrate hydrates with needle crystal structures exhibiting brittle fracture behavior. A decrease in C-S-H gel and Ca(OH)2 hydrates, deemed to have caused a decline in strength on Day 3 and thereafter, was also observed.