RESUMO
Perfluorosulfonated ionomers are the most successful ion-exchange membranes at an industrial scale. One recent, cutting-edge application of perfluorosulfonated ionomers is in polymer electrolyte fuel cells (PEFCs). In PEFCs, the ionomers are used as a component of the catalyst layer (CL) in addition to functioning as a proton-exchange membrane. In this study, the microstructures in the CLs of PEFCs were characterized by combined synchrotron X-ray scattering and transmission electron microscopy (TEM) analyses. The CL comprised a catalyst, a support, and an ionomer. Fractal dimensional analysis of the combined ultrasmall- and small-angle X-ray scattering profiles indicated that the carbon-black-supported Pt catalyst (Pt/CB) surface was covered with the ionomer in the CL. Anomalous X-ray scattering revealed that the Pt catalyst nanoparticles on the carbon surfaces were aggregated in the CLs. These findings are consistent with the ionomer/catalyst microstructures and ionomer coverage on the Pt/CB surface obtained from TEM observations.
RESUMO
Block copolymer nanopaticles were prepared from the mixture solutions containing good/poor solvents by a simple evaporation process. The block copolymers formed disorder, unidirectionally stacked lamellar, and onion-like structures in nanoparticles depending on preparation temperatures. Thermal annealing induced the disorder-order phase transition and order-order phase transformation in the block copolymer nanoparticles, even though the annealing temperature is lower than the of one polymer segment. The unusual thermal behaviors suggest that the glass transition temperature of the block copolymer is decreased by the effect of nanoparticle, whose surface areas are larger than their volumes.