Hydrothermal synthesis of high crystallinity ZSM-5 zeolite from coal gasification coarse slag and mother liquor circulation for efficient coal chemical wastewater purification.

A hydrothermal synthesis method was developed to produce high crystallinity ZSM-5 zeolite using coal gasification coarse slag (CGCS) as the raw material. Instead of the expensive NaOH(s.), Na2SiO3(s.) was utilized to activate, depolymerize, and recombine Si and Al elements in the CGCS. The mother liquor circulation technology was employed to recover and reuse raw materials and residual reagents (Na2SiO3(aq.) and TPABr), reducing waste emissions and enhancing resource utilization efficiency. The synthesized ZSM-5 had a specific surface area of 455.675 m2 g-1, pore volume of 0.284 cm3 g-1, and pore diameter of 2.496 nm. The influence of various factors on the morphology and crystallinity of ZSM-5 was investigated, resulting in the production of ZSM-5 with higher specific surface area and pore volume. Adsorption experiments showed that WU-ZSM-5 exhibited a removal efficiency of 85% for ammonia nitrogen (NH4+-N(aq.)), validating its effectiveness in coal chemical wastewater purification. The mother liquor recycling technology enabled zero-emission utilization of solid waste resources and improved the utilization rate of alkali and template to 90%. These results demonstrate the potential application of the developed method in the efficient treatment of coal chemical wastewater.

Immobilization of two dendritic organic phases onto silica and their molecular shape recognition for polycyclic aromatic hydrocarbons, tocopherols and carotenoid isomers.

BACKGROUND: Molecular shape selectivity, based on the size and shape parameters of the molecule, such as length and planarity, is a separation process that can be used for compounds with restricted shapes, such as isomers. The separation of geometric isomers is challenging because these compounds have similar physicochemical properties but differ slightly in molecular shape. The ability to separate and quantify these isomers is important in high performance liquid chromatography (HPLC), which is one of the most widely used techniques in separation science today, because the shape of the molecule has a strong influence on biological processes. RESULTS: We prepared symmetrical discoidal dendrimeric organomolecule gelators (GSDM) and o-phenylenediamine-derived low-molecular-weight dendrimeric organomolecule gelators (G1) and bonded them to silica surfaces. The dendritic organic compound-grafted silica (SiO2@GSDM and SiO2@G1) was used as HPLC stationary phases for the separation of shape-restricted isomers of polycyclic aromatic hydrocarbons (PAHs), carotenoids and tocopherols. The two phases exhibit a very high molecular shape selectivity compared to the commercially available alkyl phases. There are differences in molecular shape selectivity between the two stationary phases. Changes in the chemical structure of dendritic organic compounds can alter the orientation of the molecules, as well as changes in the molecular recognition ability. It was found that SiO2@GSDM has high molecular linear selectivity for PAHs at different temperatures, even at 50 °C. The planar selectivity of SiO2@GSDM was better for triphenylene and o-terphenyl benzenes compared to SiO2@G1. SIGNIFICANCE: This separation behavior may be attributed to the combined effect of weak interaction centers, which allowed the effective separation of bioactive and shape-restricted isomers through multiple interactions. Furthermore, SiO2@GSDM showed better separation of tocopherols and carotenoids, suggesting that the backbone and ordered structure of organic molecular gelators is an effective way to improve the shape selectivity of the molecules, whereas the molecular orientation of the functional groups influences the separation mechanism of the shape-restricted isomers.

A comparative metabolomics analysis of domestic yak (Bos grunniens) milk with human breast milk.

Yaks are tough animals living in Tibet's hypoxic stress environment. However, the metabolite composition of yak milk and its role in hypoxic stress tolerance remains largely unexplored. The similarities and differences between yak and human milk in hypoxic stress tolerance are also unclear. This study explored yak colostrum (YC) and yak mature milk (YMM) using GC-MS, and 354 metabolites were identified in yak milk. A comparative metabolomic analysis of yak and human milk metabolites showed that over 70% of metabolites were species-specific. Yak milk relies mainly on essential amino acids- arginine and essential branched-chain amino acids (BCAAs): L-isoleucine, L-leucine, and L-valine tolerate hypoxic stress. To slow hypoxic stress, human breast milk relies primarily on the neuroprotective effects of non-essential amino acids or derivates, such as citrulline, sarcosine, and creatine. In addition, metabolites related to hypoxic stress were significantly enriched in YC than in YMM. These results reveal the unique metabolite composition of yak and human milk and provide practical information for applying yak and human milk to hypoxic stress tolerance.

Preparation of Ru/N-doped carbon catalysts by induction of different nitrogen source precursors for the hydroprocessing of lignin oil.

The lignin oil produced by rapid pyrolysis of lignin is considered a promising liquid fuel source. Hydrodeoxygenation (HDO) is a kind of efficient method to upgrade the lignin oil, and a high-performance catalyst is key to the hydrodeoxygenation of lignin oil. In this study, a high dispersion and small size Ru nanoparticle loaded N-doped carbon catalyst was derived by the direct pyrolysis of a mixture of ruthenium trichloride and melamine, and it could efficiently convert lignin oil. The lignin oil was completely transformed at 240 °C and 1 MPa H2, and 36.58% cyclohexane was obtained. The formation, surface area, and nitrogen species of the catalyst could be controlled by changing the precursor of the nitrogen-doped carbon support. The percentage of pyridine nitrogen possessed with melamine as a nitrogen-carbon precursor (31.35%) was much higher than that with urea (16.47%) and dicyandiamide (8.20%) as nitrogen-carbon precursors. The presence of pyridine nitrogen could not only serve as the coordination site for even dispersity and stability of Ru nanoparticles but also regulated the electron density of Ru nanoparticles (NPs) and increased the active site Ru0 through electron transfer.

Strategy for oxygen vacancy enriched CoMn spinel oxide catalyst activated peroxodisulfate for tetracycline degradation: process, mechanism, and toxicity analysis.

Antibiotic-like organic pollutants are harmful to aquatic ecosystems and seriously disrupt the ecological balance. Herein, we propose a simple and versatile method to prepare cobalt-manganese oxides with high specific surface area and abundant oxygen vacancies using low-temperature reduction crystallization, which greatly facilitates the adsorption and electron transfer between the catalyst, PDS, and TC, thus accelerating the degradation of tetracycline (TC). Among them, the degradation efficiency of TC in the CoMn2O4(C)/PDS system was 99.8% in 60 min and the degradation rate remained above 90% after four cycles. The possible degradation mechanism is also discussed, where Co is the main metal active center of the catalyst and Mn plays an auxiliary catalytic role to promote the generation of reactive radicals in PDS through redox interactions between Co and Mn, where SO4 -˙ is the main active species for TC degradation. Finally, the possible degradation pathways of TC are proposed and the toxicity of the intermediates is evaluated. Findings from this work will shed light on the rational design of bimetallic oxide catalysts.

Dendritic organic molecular gel coating with molecular shape selectivity and its application in selective separation by liquid chromatography.

Dendritic organic molecular gels are a promising class of three-dimensional network compounds. Here, we have synthesized a new type of dendritic organic molecular gel stationary phase (SiO2-G3) by using benzyl alcohol as raw material and dimethyl 5-hydroxyisophthalate as growth unit to synthesize a third-generation organic molecular gel G3, which grafted onto the silica surface by cyanogen chloride (CC). The developed stationary phase not only exhibits high molecular shape selectivity but also has a RPLC/HILIC/IEC mixed-mode characteristic for HPLC due to the ordered structure, the multiple strong π-π stacking interactions and the introduction of a hydrophilic triazine fraction during the grafting process. Compared with a commercial C18 column, the developed column exhibited flexible selectivity, enhanced separation performance and excellent separation of monosubstituted benzene, polycyclic aromatic hydrocarbons (PAHs), positional isomers, nucleosides and nucleobases, benzoic acid and aniline compounds. In addition, the new column provided baseline separation of polycyclic aromatic hydrocarbon contaminants in Yellow River water, verifying its potential for application in the analysis of real samples.

Enhancing deep mineralization of refractory benzotriazole via carbon nanotubes-intercalated cobalt copper bimetallic oxide nanosheets activated peroxymonosulfate process: Mechanism, degradation pathway and toxicity.

Peroxymonosulfate-based advanced oxidation processes (PMS-AOPs) are effective methods for the degradation of highly toxic and refractory nitrogen-containing heteroatomic pollutants such as benzotriazole (BTA). The construction of catalytic materials with multiple active centers is the key to generating abundant reactive oxygen species (ROS) and achieving high mineralization efficiency in PMS-AOPs. Herein, carbon nanotubes-intercalated cobalt copper bimetallic oxide nanosheets catalyst (CoCuNS@CNTs) was obtained by pyrolysis of two-dimensional (2D) MOF precursor. The degradation rate constant of BTA in CoCuNS@CNTs/PMS system was 4 times higher than that of metal oxide nanosheets catalyst without CNTs, while exhibiting high cycling stability and mineralization efficiency. Serial characterizations demonstrated that CoCu nanosheets was formed by CNTs-induced the directional assembly of metal oxide nanoparticles, which had high graphitization and abundant oxygen vacancies and could greatly facilitated the adsorption and electron transfer between the catalyst, PMS and BTA. Moreover, the doping of Cu species significantly improved PMS utilization and accelerated the Co(III)/Co(II) redox cycle. Both radicals (SO4-• and •OH) and non-radicals (1O2) played a role in CuCoNS@CNTs/PMS system and the contributions of ROS were 72.2%, 11.1% and 16.7%, respectively. Meanwhile, the concentration of key ROS (SO4-•) production increased from 4.76 µM to 8.56 µM compared with cobalt oxide nanosheets (CoNS). Three degradation pathways of BTA were proposed: benzene ring opening, benzene ring hydroxylation and triazole ring dimerization. Finally, the toxicity changes during the degradation process were measured and the toxicity of eleven intermediates was evaluated. This study may provide new insights into the degradation of persistent organic pollutants.

Synergistic effect of Mn doping and hollow structure boosting Mn-CoP/Co2P nanotubes as efficient bifunctional electrocatalyst for overall water splitting.

The sluggish kinetic of hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) severely hampers the commercial application of electrochemical water splitting, promoting the urgent exploration of high-efficient bifunctional electrocatalysts. Heteroatom doping and structure engineering have been identified as the most effective strategies to boost the catalytic activity of electrocatalysts. Herein, Mn doping and hollow structure were integrated in the design of Co-based transition metal phosphide catalyst to prepare Mn-CoP/Co2P nanotubes (denoted as Mn-CP NTs) by a facile template-free method. Confirmed by characterization analysis, the introduced Mn species were in high dispersion in the regular CoP/Co2P hollow tubular framework. Such a favorable design in composition and structure effectively boosted the catalytic activity of Mn-CP NTs toward electrochemical water splitting. The Mn-CP NTs showed superior HER and OER activity demonstrated by the low overpotentials of 82 mV (vs HER) and 309 mV (vs OER) at the current density of 10 mA cm-2, as well as the satisfactory durability. When used as both cathode and anode in electrolyzer for overall water splitting, only a low cell voltage of 1.67 V was required for the Mn-CP NTs to drive 10 mA cm-2, accompanied with excellent stability confirmed by over 50 h test.

Spiderweb-inspired all-weather CoS quantum dots confined in N-doped carbon for boosted sulfate radical evolution.

Inspired by the working principle of natural spiderweb and long-persistence phosphors, we have synthesized a spiderweb-like nanocomposite in which CoS quantum dots are confined in N-doped carbon frameworks/carbon nanotubes (CNTs). The intimate combination of three-dimensional conductive networks of CoS/CNTs with abundant active sites allows effective capture of sulfate radicals via both physical confinement and chemical bonding and accelerates the redox kinetics significantly. Furthermore, in virtue of the light storing and luminescence behaviors of long-persistence phosphors, the all-weather CoS/CNTs produced can realize an optimum degradation efficiency of 64% under dark conditions. Overall, this work reveals a significant step forward for building a desirable all-weather catalyst with abundant active sites for potential use in degradation under dark conditions.

Nano-Sized PtRu/C Electrocatalyst With Separated Phases and High Dispersion Improves Electrochemical Performance of Hydrogen Oxidation Reaction.

Alloys and core-shell nanoparticles have recently received enormous attention which opened up new avenues for highly active catalysts. Despite considerable advances in this field, the majority of proposed approaches suffer from either complicated procedures or unstable structures, severely hindering their practical applications. Here, we successfully synthesized alloy electrocatalyst with separated phases, PtRu alloy nanoparticles robustly supported by carbon matrix (PtRu/C), using a convenient two-step solvothermal method. The constructed PtRu/C at different NaOH contents (0-1.25 mmol) were compared and electrochemical activity were evaluated by the hydrogen oxidation reaction (HOR). In contrast, the homogeneous distribution and minimum average size of Ru and Pt nanoparticles on carbon, appeared at approximately 4 nm, proving that PtRu/C-0.75 possessed abundant accessible active sites. The catalytic activities and the reaction mechanism were studied via electrochemical techniques. PtRu/C-0.75 has excellent activity due to its unique electronic structure and efficient charge transfer, with the largest j0 value of 3.68 mA cm-2 in the HOR.

Revealing the mechanism of high water resistant and excellent active of CuMn oxide catalyst derived from Bimetal-Organic framework for acetone catalytic oxidation.

Environmental H2O is an influential factor in the low-temperature catalytic oxidation of volatile organic compounds (VOCs), and it significantly impacts the reaction process and mechanism. Here, a series of rod-like Cu-Mn oxides were synthesised by pyrolysing Cu/Mn-BTC for acetone oxidation. The results confirm that the formation of multiphase interfaces have more excellent catalytic performance compared to single-phase catalysis. This phenomenon can be attributed to the formation of multiphase interfaces, which resulted in the synthesized catalysts with more active oxygen species and defective sites. The CuMn2Ox catalyst exhibited superior catalytic performance (T90 = 150 °C), high water resistance and long-term stability. Furthermore, in situ diffuse reflectance infrared Fourier transform spectroscopy and thermal desorption-gas chromatography-mass spectrometry results indicated that the degradation pathway of acetone was as follows: acetone ((CH3)2CO*) â†’ enolate complexes ((CH2) = C(CH3) O*) â†’ acetaldehyde ((CH3CHO*) â†’ acetate (CH3COO*) â†’ formate (HCOO*) â†’ CO2 and H2O. At a low-temperature, water vapour dissociated a large number of activated hydroxyl groups on the multiphase interface, which promoted the dissociation of enolate complexes and acetaldehyde species. This composite oxide is a promising catalyst for removing oxygenated VOCs at high humidity.

Advancing to 4.6 V Review and Prospect in Developing High-Energy-Density LiCoO2 Cathode for Lithium-Ion Batteries.

Layered LiCoO2 (LCO) is one of the most important cathodes for portable electronic products at present and in the foreseeable future. It becomes a continuous push to increase the cutoff voltage of LCO so that a higher capacity can be achieved, for example, a capacity of 220 mAh g-1 at 4.6 V compared to 175 mAh g-1 at 4.45 V, which is unfortunately accompanied by severe capacity degradation due to the much-aggravated side reactions and irreversible phase transitions. Accordingly, strict control on the LCO becomes essential to combat the inherent instability related to the high voltage challenge for their future applications. This review begins with a discussion on the relationship between the crystal structures and electrochemical properties of LCO as well as the failure mechanisms at 4.6 V. Then, recent advances in control strategies for 4.6 V LCO are summarized with focus on both bulk structure and surface properties. One closes this review by presenting the outlook for future efforts on LCO-based lithium ion batteries (LIBs). It is hoped that this work can draw a clear map on the research status of 4.6 V LCO, and also shed light on the future directions of materials design for high energy LIBs.

Anion Doping for Layered Oxides with a Solid-Solution Reaction for Potassium-Ion Battery Cathodes.

The development of potassium-ion batteries (PIBs) is challenged by the shortage of stable cathode materials capable of reversibly hosting the large-sized K+ (1.38 Å), which is prone to cause severe structural degradation and complex phase evolution during the potassiation/depotassiation process. Here, we identified that anionic doping of the layered oxides for PIBs is effective to combat their capacity fading at high voltage (>4.0 V). Taking P2-type K2/3Mn7/9Ni1/9Ti1/9O17/9F1/9 (KMNTOF) as an example, we showed that the partial substitution of O2- by F- enlarged the interlayer distance of the K2/3Mn7/9Ni1/9Ti1/9O2 (KMNTO), which becomes more favorable for fast K+ transition without violent structural destruction. Meanwhile, based on the experimental data and theoretical results, we identified that the introduction of F- anions effectively increased the redox-active Mn cationic concentration by lowering the average valence of the Mn element, accordingly providing more reversible capacity derived from the Mn3+/4+ redox couple, rather than oxygen redox. This anionic doping strategy enables the KMNTOF cathode to deliver a high reversible capacity of 132.5 mAh g-1 with 0.53 K+ reversible (de)intercalation in the structure. We expect that the discovery provides new insights into structural engineering for pursuing stable cathodes to facilitate the future applications of high-performance PIBs.

Construction of Li3PO4 nanoshells for the improved electrochemical performance of a Ni-rich cathode material.

A Li3PO4 nanocoating around a nickel-rich cathode material was successfully constructed via controlling the reaction between the electrode material and a preformed phosphorus-containing polymeric nanoshell; this not only effectively tackles the alkali residue challenge, but it also contributes to much-improved electrochemical performance being shown by a high-energy cathode.

Coordination-Assisted Precise Construction of Metal Oxide Nanofilms for High-Performance Solid-State Batteries.

The application of solid-state batteries (SSBs) is challenged by the inherently poor interfacial contact between the solid-state electrolyte (SSE) and the electrodes, typically a metallic lithium anode. Building artificial intermediate nanofilms is effective in tackling this roadblock, but their implementation largely relies on vapor-based techniques such as atomic layer deposition, which are expensive, energy-intensive, and time-consuming due to the monolayer deposited per cycle. Herein, an easy and low-cost wet-chemistry fabrication process is used to engineer the anode/solid electrolyte interface in SSBs with nanoscale precision. This coordination-assisted deposition is initiated with polyacrylate acid as a functional polymer to control the surface reaction, which modulates the distribution and decomposition of metal precursors to reliably form a uniform crack-free and flexible nanofilm of a large variety of metal oxides. For demonstration, artificial Al2O3 interfacial nanofilms were deposited on a ceramic SSE, typically garnet-structured Li6.5La3Zr1.5Ta0.5O12 (LLZT), that led to a significant decrease in the Li/LLZT interfacial resistance (from 2079.5 to 8.4 Ω cm2) as well as extraordinarily long cycle life of the assembled SSBs. This strategy enables the use of a nickel-rich LiNi0.83Co0.07Mn0.1O2 cathode to deliver a reversible capacity of 201.5 mAh g-1 at a considerable loading of 4.8 mg cm-2, featuring performance metrics for an SSB that is competitive with those of traditional Li-ion systems. Our study demonstrates the potential of solution-based routes as an affordable and scalable manufacturing alternative to vapor-based deposition techniques that can accelerate the development of SSBs for practical applications.

Altered milk yield and rumen microbial abundance in response to concentrate supplementation during the cold season in Tibetan sheep

BACKGROUND Weight loss and decline of milk yield in Tibetan sheep was a challenge for the dairy industry in Qinghai-Tibet Plateau, which were considered to be caused by underfeeding of the sheep during the harsh winter. The objective of this study was to assess the role of feed supplementation in the milk performance and rumen microbiome of ewes under forage-based diets. Based on parity, milking period, milk yield, and body weight, ten 1.5-yr-old ewes were allocated randomly into two groups. One group of ewes was fed no supplement Control group (CON) and the other group was fed with concentrate feed supplement (Treatment group, T). Individual milk yield was determined daily; both the milk composition and rumen bacterial characteristics were analyzed after the end of feeding trials. RESULTS Results showed that lactose in the milk of the CON group was significantly lower (P < 0.05) than that of the T group at days 30 and 60. Milk yield in the T group was greater than in the CON group at day 30 (P < 0.05). Additionally, the dominant ruminal bacteria (phyla Bacteroidetes, Firmicutes, and Verrucomicrobia) were shared by both groups through 16S rRNA gene pyrosequencing. Greater relative abundance of Bacteroidales RF16 group in family level, Victivallales in order level, Lentisphaeria in class level, and Lachnospiraceae bacterium in species level were observed in the T group than in the CON group (P < 0.05). CONCLUSIONS These results demonstrated that supplementation of concentrate in the cold season improved milk lactose yield and milk production, and the rumen microbial abundance of Tibetan sheep.

A General Synthesis Strategy for Hollow Metal Oxide Microspheres Enabled by Gel-Assisted Precipitation.

Hollow metal oxide microspheres (HMMs) have drawn enormous attention in different research fields. Reliable and scalable synthetic protocols applicable for a large variety of metal oxides are in emergent demand. Here we demonstrated that polymer hydrogel, such as the resorcinol formaldehyde (RF) one, existed as an efficient synthetic platform to build HMMs. Specifically, the RF gel forms stacked RF microspheres enlaced with its aqueous phase, where the following evaporation of the highly dispersed water leads to a gel-assisted precipitation (GAP) of the dissolved metal precursor onto the embedded polymeric solids suited for the creation of HMMs. By taking advantage of the structural features of hydrogel, this synthesis design avoids the delicate control on the usually necessitated coating process and provides a simple and effective synthetic process versatile for functional HMMs, particularly Nb2 O5 as a high-performance electrode material in Li-ion intercalation pseudocapacitor.

High-Performance Cathode Materials for Potassium-Ion Batteries: Structural Design and Electrochemical Properties.

Due to the obvious advantage in potassium reserves, potassium-ion batteries (PIBs) are now receiving increasing research attention as an alternative energy storage system for lithium-ion batteries (LIBs). Unfortunately, the large size of K+ makes it a challenging task to identify suitable electrode materials, particularly cathode ones that determine the energy density of PIBs, capable of tolerating the serious structural deformation during the continuous intercalation/deintercalation of K+ . It is therefore of paramount importance that proper design principles of cathode materials be followed to ensure stable electrochemical performance if a practical application of PIBs is expected. Herein, the current knowledge on the structural engineering of cathode materials acquired during the battle against its performance degradation is summarized. The K+ storage behavior of different types of cathodes is discussed in detail and the structure-performance relationship of materials sensitive to their different lattice frameworks is highlighted. The key issues facing the future development of different categories of cathode materials are also highlighted and perspectives for potential approaches and strategies to promote the further development of PIBs are provided.

Effects of acid ionization on the formation mechanism of bimodal mesoporous Al-MCM-41s from coal gasification fine residue and evaluation of adsorption capabilities.

The development of synthetic methods to obtain high value-added mesoporous Al-MCM-41 from a low-cost silicon-aluminum source with low toxicity is an active research topic in solid waste resource utilization. In particular, the controlled synthesis of MCM-41 with a two-level pore distribution is a challenging task. In this work, the synthesis of unimodal and bimodal mesoporous Al-MCM-41s was achieved using acids with different degrees of ionization from coal gasification fine residue (CGFR) as bulk solid waste generated by the coal gasification process. We determined that the degree of acid ionization affected the self-assembly of inorganic/organic species as well as condensation processes, resulting in some changes of the hexagonal mesoscopic structure. The unimodal mesoporous Al-MCM-41 with acetic acid HAc and bimodal mesoporous Al-MCM-41s with an inorganic acid environment (HCl, HNO3 or H2SO4) could be effectively prepared in a controllable manner by the silicon and aluminum source obtained at alkali dissolution time 6 h and crystallization conditions at pH 10.5 and 383 K in 72 h. Moreover, the synthesis of Al-MCM-41-HAc with different SiO2/Al2O3 molar ratios (18-89) could also be realized by different alkali dissolution times. And alkali dissolution time (2-24 h) and the crystallization conditions (pH 4.5-11.5, temperatures 373-393 K, and time 48-96 h) also affected the formation of unimodal and bimodal mesoporous Al-MCM-41-HAc. In addition, the maximum adsorption amount onto bimodal mesoporous Al-MCM-41-H2SO4 (476.19 mg g-1 at 308 K) was larger than that onto unimodal mesoporous Al-MCM-41-HAc (243.90 mg g-1 at 303 K). The mesoporous Al-MCM-41s showed good stability.

Molecular characterization and analysis of the association of growth hormone 1 gene with growth traits in Chinese indigenous yak (Bos grunniens).

This study aimed to investigate the effects of polymorphisms in growth hormone 1 (GH1) gene on the growth traits in Chinese indigenous yak. Using the polymerase chain reaction-restriction fragment length polymorphism (PCR-PFLP) approach, one novel single-nucleotide polymorphism (SNP), termed as g.1721G>A, was identified in the exon 4 of GH1 gene in 423 individuals of yak population. Based on the chi-square (χ2) test, the frequencies of g.1721G>A alleles agreed with Hardy-Weinberg equilibrium (HWE) (P < 0.05). A significant association was observed between this SNP and several growth traits (P < 0.01 or P < 0.05), in which the genotype GG exhibited the best values. The present study suggested that the identified SNP was a useful genetic marker for the improvement of growth traits in Chinese indigenous yak.