Fabrication of Bi2Te3 and Sb2Te3 Thermoelectric Thin Films using Radio Frequency Magnetron Sputtering Technique.

Through various studies on thermoelectric (TE) materials, thin film configuration gives superior advantages over conventional bulk TEs, including adaptability to curved and flexible substrates. Several different thin film deposition methods have been explored, yet magnetron sputtering is still favorable due to its high deposition efficiency and scalability. Therefore, this study aims to fabricate a bismuth telluride (Bi2Te3) and antimony telluride (Sb2Te3) thin film via the radio frequency (RF) magnetron sputtering method. The thin films were deposited on soda lime glass substrates at ambient temperature. The substrates were first washed using water and soap, ultrasonically cleaned with methanol, acetone, ethanol, and deionized water for 10 min, dried with nitrogen gas and hot plate, and finally treated under UV ozone for 10 min to remove residues before the coating process. A sputter target of Bi2Te3 and Sb2Te3 with Argon gas was used, and pre-sputtering was done to clean the target's surface. Then, a few clean substrates were loaded into the sputtering chamber, and the chamber was vacuumed until the pressure reached 2 x 10-5 Torr. The thin films were deposited for 60 min with Argon flow of 4 sccm and RF power at 75 W and 30 W for Bi2Te3 and Sb2Te3, respectively. This method resulted in highly uniform n-type Bi2Te3 and p-type Sb2Te3 thin films.

An Overview of the Strategies for Tin Selenide Advancement in Thermoelectric Application.

Chalcogenide, tin selenide-based thermoelectric (TE) materials are Earth-abundant, non-toxic, and are proven to be highly stable intrinsically with ultralow thermal conductivity. This work presented an updated review regarding the extraordinary performance of tin selenide in TE applications, focusing on the crystal structures and their commonly used fabrication methods. Besides, various optimization strategies were recorded to improve the performance of tin selenide as a mid-temperature TE material. The analyses and reviews over the methodologies showed a noticeable improvement in the electrical conductivity and Seebeck coefficient, with a noticeable decrement in the thermal conductivity, thereby enhancing the tin selenide figure of merit value. The applications of SnSe in the TE fields such as microgenerators, and flexible and wearable devices are also discussed. In the future, research in low-dimensional TE materials focusing on nanostructures and nanocomposites can be conducted with the advancements in material science technology as well as microtechnology and nanotechnology.

Solution-Based Synthesis and Characterization of Cu2ZnSnS4 (CZTS) Thin Films.

Cu2ZnSnS4 (CZTS) ink was synthesized from metal chloride precursors, sulfur, and oleylamine (OLA), as a ligand by a simple and low-cost hot-injection method. Thin films of CZTS were then prepared by spin coating, followed by thermal annealing. The effects of the fabrication parameters, such as ink concentration, spinning rate, and thermal treatment temperatures on the morphology and structural, optical, and electrical properties of the films were investigated. As expected, very thin films, for which the level of transmittance and band-gap values increase, can be obtained either by reducing the concentration of the inks or by increasing the rate of spinning. Moreover, the thermal treatment affects the phase formation and crystallinity of the film, as well as the electrical conductivity, which decreases at a higher temperature.