RESUMO
In this paper, the possibility of applying different welding strategies to overlay an FeCrAl layer against corrosion from heavy liquid metal on a plain plate made of 316L austenitic stainless steel was investigated. This technology could be used in manufacturing the main vessel of CiADS, which may be considered as a more economic and feasible solution than production with the corrosion-resistant FeCrAl alloy directly. The main operational parameters of the laser welding process, including laser power, weld wire feeding speed, diameter of the welding wire, etc., were adjusted correspondingly to the optimized mechanical properties of the welded plate. After performing the standard nuclear-grade bending tests, it can be preliminarily confirmed that the low-power pulse laser with specific operational parameters and an enhanced cooling strategy will be suitable to surface an Fe-10Cr-4Al-RE layer with a thickness of approximately 1 mm on a 40 mm-thick 316L stainless steel plate, thanks to the upgraded mechanical properties incurred by refined grains with a maximum size of around 300 µm in the welded layer.
RESUMO
Today the technical limit for solar towers is represented by the temperature that can be reached with current accumulation and exchange fluids (molten salts are generally adopted and the max temperatures are generally below 600 °C), even if other solutions have been suggested that reach 800 °C. An innovative solution based on liquid lead has been proposed in an ongoing experimental project named Nextower. The Nextower project aims to improve current technologies of the solar sector by transferring experience, originally consolidated in the field of nuclear plants, to accumulate heat at higher temperatures (T = 850-900 °C) through the use of liquid lead heat exchangers. The adoption of molten lead as a heat exchange fluid poses important criticalities of both corrosion and creep resistance, due to the temperatures and structural stresses reached during service. Liquid lead corrosion issues and solutions in addition to creep-resistant material selection are discussed. The experimental activities focused on technical solutions adopted to overcome these problems in terms of the selected materials and technologies. Corrosion laboratory tests have been designed in order to verify if structural 800H steel coated with 6 mm of FeCrAl alloy layers are able to resist the liquid lead attack up to 900 °C and for 1000 h or more. The metallographic results were obtained by mean of scanning electron microscopy with an energy dispersive microprobe confirm that the 800H steel shows no sign of corrosion after the completion of the tests.
RESUMO
An Fe10Cr4Al alloy containing reactive elements developed for application in high-temperature liquid lead environments was analyzed after exposure in 600 and 750°C lead with dissolved oxygen for 1,0002,000 h. Atom probe tomography, transmission electron microscopy, and X-ray scattering were all used to study the protective oxide formed on the surface. Exposure at 750°C resulted in a 2-µm thick oxide, whereas the 600°C exposure resulted in a 100-nm thick oxide. Both oxides were layered, with an FeAl spinel on top, and an alumina layer toward the metal. In the 600°C exposed material, there was a Cr-rich oxide layer between the spinel and the alumina. Metallic lead particles were found in the inner and middle parts of the oxide, related to pores. The combination of the experimental techniques, focusing on atom probe tomography, and the interpretations that can be done, are discussed in detail.