Reducing Porosity and Refining Grains for Arc Additive Manufacturing Aluminum Alloy by Adjusting Arc Pulse Frequency and Current.

Coarse grains and gas pores are two main problems that limit the application of additive manufacturing aluminum alloys. To reduce porosity and refine grains, this paper presents a quantitative investigation into the effect of pulse frequency and arc current on the porosity and grains of arc additive manufacturing Al⁻5Si alloy. The experiment results show that pulse frequency and arc current have a significant impact on the macrostructure, microstructure, porosity, and tensile properties of the samples. Fine grains and a uniform microstructure can be obtained with low pulse frequency and low arc current as a result of the rapid cooling of the molten pool. With the increase of pulse frequency, density shows a trend that firstly escalates and attains the maximum value at 50 Hz, but later declines as a result of the relation between pores formation and gas escape. Moreover, better tensile properties can be obtained at low pulse frequency and low arc current because of the finer grains.

Research on Mechanisms and Controlling Methods of Macro Defects in TC4 Alloy Fabricated by Wire Additive Manufacturing.

Wire feeding additive manufacturing (WFAM) has broad application prospects because of its advantages of low cost and high efficiency. However, with the mode of lateral wire feeding, including wire and laser additive manufacturing, gas tungsten arc additive manufacturing etc., it is easy to generate macro defects on the surface of the components because of the anisotropy of melted wire, which limits the promotion and application of WFAM. In this work, gas tungsten arc additive manufacturing with lateral wire feeding is proposed to investigate the mechanisms of macro defects. The results illustrate that the defect forms mainly include side spatters, collapse, poor flatness, and unmelted wire. It was found that the heat input, layer thickness, tool path, and wire curvature can have an impact on the macro defects. Side spatters are the most serious defects, mainly because the droplets cannot be transferred to the center of the molten pool in the lateral wire feeding mode. This research indicates that the macro defects can be controlled by optimizing the process parameters. Finally, block parts without macro defects were fabricated, which is meaningful for the further application of WFAM.