Characterization of the Static, Creep, and Fatigue Tensile Behavior of Basalt Fiber/Polypropylene Composite Rods for Passive Concrete Reinforcement.

Fiber-reinforced polymer (FRP) composites are becoming more frequently adopted as so-called "corrosion-resistant" concrete reinforcement materials due to their excellent mechanical properties and formability. However, their long-term reliability must be thoroughly investigated in order to understand failure mechanisms and to develop service life models. This study is on the mechanical properties of a prototype basalt fiber-reinforced polypropylene (BFPP) rod under quasi-static and sustained loading. Static strength and modulus at elevated temperatures do not decrease significantly, but the variability in strength increases with temperature, as shown by a Weibull analysis. Creep behavior is typical of unidirectional FRP, where the creep rupture strength follows a power law. Fatigue at various stress ratios R reveals the sensitivity of composite strength to the matrix damage, which increases at lower values of R (i.e., higher stress amplitudes). These results are discussed in the context of service life and concrete structure design guidelines.

Mass production of low-boiling point solvent- and water-soluble graphene by simple salt-assisted ball milling.

Developing a mass production method for graphene is essential for practical usage of this remarkable material. Direct exfoliation of graphite in a liquid is a promising approach for production of high quality graphene. However, this technique has three huge obstacles to be solved; limitation of solvent, low yield and low quality (i.e., multilayer graphene with a small size). Here, we found that soluble graphite produced by mechanochemical reaction with salts overcomes the above three drawbacks. Soluble graphite was exfoliated into monolayer graphene with more than 10% yield in five minutes of sonication. The modified graphite was easily exfoliated in a low-boiling point solvent such as acetone, alcohol and water without the aid of a surfactant. Molecular simulation revealed that the salt is adsorbed to the active carbon at the graphite edge. In the case of weak acid salts, the original bonding nature between the alkali ion and the base molecule is retained after the reaction. Thus, alkali metals are easily dissociated in a polar solvent, leading to negative charge of graphene, enabling the exfoliation of graphite in low boiling point solvents. The approach proposed here opens up a new door to practical usage of the attractive 2D material.