Scale inhibition study by turbidity measurement.

The concept of a critical supersaturation ratio (CSSR) has been used to characterize the effectiveness of different types of scale inhibitors, inhibitor concentration, and precipitating solution pH in order to prevent the formation of barium sulfate scale. The scale inhibitors used in this work were aminotrimethylene phosphonic acid (ATMP), diethylenetriaminepentamethylene phosphonic acid (DTPMP), and phosphinopolycarboxylic acid polymer (PPCA). The CSSR at which barium sulfate precipitates was obtained as a function of time for different precipitation conditions and was used as an index to evaluate the effect of the precipitation conditions. The results showed that the CSSRs decrease with increasing elapsed time after mixing the precipitating solutions, but increases with increasing scale inhibitor concentration and solution pH. The CSSR varies linearly with the log of the scale inhibitor concentration and with the precipitating solution pH. A SEM analysis showed that the higher the scale inhibitor concentration and solution pH, the smaller and more spherical the BaSO4 precipitates. Analysis of the particle size distribution revealed that increasing the elapsed time, the scale inhibitor concentration, and precipitating solution pH, all produce a broader particle size distribution and a smaller mean diameter of the BaSO4 precipitates. DTPMP and PPCA were the most effective BaSO4 scale inhibitors per ionizable proton and the most effective on a concentration basis, respectively.

Study of Ca-ATMP precipitation in the presence of magnesium ion.

ATMP (aminotri(methylenephosphonic acid)), a phosphonate scale inhibitor used in the petroleum industry, was used as a model scale inhibitor in this study. One of the goals of this work was to determine the range of conditions under which Mg ions, which are formed in reservoir formations containing dolomite, modulate the formation of Ca-ATMP precipitate as a scale inhibitor. The results revealed that the amount of ATMP precipitated decreased with addition of Mg ions in solution at all values of the solution pH. Furthermore, an increase in both the solution pH and the concentration of the divalent cations in solution resulted in a change of the molar ratio of (Ca + Mg) to ATMP in the precipitates. At a low solution pH (pH 1.5), Mg ions had little effect on the composition of the Ca-ATMP precipitate. However, at higher values of the solution pH (pH 4 and 7), the Ca to ATMP molar ratio in the precipitates decreased with increasing concentration of the Mg. Here it was found that Mg ions replaced Ca ions on available reactive sites of ATMP molecules. These results determined the limits of the Mg ion concentration, which affects the precipitation of Ca-ATMP, Mg-ATMP, and (Ca + Mg)-ATMP. The dissolution of the scale inhibitors was studied using a rotating disk reactor. These experiments showed that the total divalent cation molar ratio (Ca + Mg) to ATMP in the precipitates is the primary factor that controls the rate of dissolution (release) of the phosphonate precipitates. The phosphonate precipitate dissolution rates decreased as the molar ratio of divalent cations to ATMP in the precipitates increased.