Regulating "Tip Effect" and Zn2+-Deposition Kinetics by In Situ Constructing Interphase for Low Voltage Hysteresis and Dendrite-Free Zn Anode.

Metal zinc (Zn) is being explored as a possible anode for aqueous zinc ion batteries (AZIBs). However, unrestrained Zn dendrite caused by "tip effect" and chemical corrosion continue to plague the Zn deposition process, limiting the functionality of AZIBs and prohibiting their use at high current densities. This work presents an in situ approach for introducing homogeneous ZnO nanoarrays onto the surface of Zn foil (Zn@ZnO NAs) as a functional protective interphase. On the one hand, well-distributed ZnO NAs protection layer can regulate the "tip effect" and confine the growth of Zn dendrite. On the other hand, the ZnO NAs layer can enhance the desolvation and diffusion process of Zn2+ on the surface of anode, attributing to low voltage hysteresis and exceptional electrochemical performance at high current densities. As a result, the Zn@ZnO NAs exhibits a low voltage hysteresis of 50.8 mV with a superb lifespan of 1200 h at a current density of 5 mA cm-2. Moreover, Zn@ZnO NAs||α-MnO2 full-cell shows a superior cycling performance after 500 cycles at 0.5 A g-1 with a capacity of 216.69 mAh g-1. This work is expected to provide ideas for designing other reversible zinc anode chemical systems, especially under a high current density.

Constructing a Size-Controllable Spherical P2-Type Layered Oxides Cathode That Achieves Practicable Sodium-Ion Batteries.

P2-type layered metal oxides are regarded as promising cathode materials for sodium-ion batteries due to their high voltage platform and rapid Na+ diffusion kinetics. However, limited capacity and unfavorable cycling stability resulting from inevitable phase transformation and detrimental structure collapse hinder their future application. Herein, based on P2-type Na0.67Ni0.18Mn0.67Cu0.1Zn0.05O2, we synthesized a series of secondary spherical morphology cathodes with different radii derived from controlling precursors prepared by a coprecipitation method, which can be promoted to large-scale production. Consequently, the synthesized materials possessed a high tap density of 1.52 g cm-3 and a compacted density of 3.2 g cm-3. The half cells exhibited a specific capacity of 111.8 mAh g-1 at a current density of 0.1 C as well as an 82.64% capacity retention with a high initial capacity of 85.80 mAh g-1 after 1000 cycles under a rate of 5 C. Notably, in situ X-ray diffraction revealed a reversible P2-OP4 phase transition and displayed a tiny volume change of 6.96% during the charge/discharge process, indicating an outstanding cycling stability of the modified cathode. Commendably, the cylindrical cell achieved a capacity of 4.7 Ah with almost no change during 1000 cycles at 2 C, suggesting excellent potential for future applications.